Plastic blend friction material and preparation method thereof

A friction material and blending technology, applied in the field of friction materials, can solve the problems of affecting the entry of small molecules or macromolecular chains of monomers, blockage of pores of mesoporous materials, etc., so as to improve friction and wear performance, improve high-temperature friction performance, reduce sticky effect

Inactive Publication Date: 2017-01-25
来安县隆华摩擦材料有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The research on polymer-based mesoporous composites is still in its infancy, and there are some common problems in the preparation process: (1) how to effectively modify the surface of mesoporous materials to improve the interfacial compatibility between the two phases, and at the same time, the surface modification can not cause The blockage of the pore openings of mesoporous materials affects the entry of monomeric small molecules or macromolecular chains

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] A plastic blended friction material, which is composed of the following raw materials in parts by weight:

[0023] Melamine 37, 37% formaldehyde solution 50, bentonite 4, 8-hydroxyquinoline copper 0.7, nonylphenol 0.1, liquid EPDM rubber 10, sp800.2, epoxy octyl stearate 3, polyvinyl chloride 140, Ethyl orthosilicate 6, triethanolamine 0.2, alkylphenol polyoxyethylene ether 0.3, dihydrocarbyl pentasulfide RC25402, potassium hexatitanate whisker 1, titanate coupling agent kt1050.3, lithium naphthenate 0.1 , Butyltin Mercaptide 0.6, Ammonium Polyphosphate 1, Citric Acid 1, 1,3,5 Trimethylbenzene 0.01.

[0024] A preparation method of the plastic blend friction material, comprising the following steps:

[0025] (1) Add the above-mentioned ammonium polyphosphate into deionized water 10 times its weight, stir evenly, add tetraethyl orthosilicate, raise the temperature to 50°C, add the above-mentioned citric acid, keep stirring for 20 minutes to obtain an aqueous sol solutio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a plastic blend friction material which is prepared from the following raw materials in parts by weight: 37-40 parts of melamine, 50-60 parts of 37-40% formalin, 4-6 parts of bentonite, 0.7-1 part of copper 8-hydroxyquinoline, 0.1-0.2 part of nonyl phenol, 10-16 parts of liquid ethylene propylene diene monomer rubber, 0.2-0.4 part of sp80, 3-4 parts of epoxy octyl stearate, 140-170 parts of polyvinyl chloride, 6-8 parts of ethyl orthosilicate, 0.2-0.3 part of triethanolamine, 0.3-0.5 part of alkylphenol polyoxyethylene, 2-3 parts of dialkyl pentasulfide RC2540, 1-2 parts of potassium hexatitanate whisker, 0.3-1 part of titanate coupling agent kt105, 0.1-0.2 part of lithium naphthenate, 0.6-1 part of butyl tin mercaptide, 1-2 parts of ammonium polyphosphate, 1-2 parts of citric acid and 0.01-0.02 part of 1,3,5-trimethylbenzene. The plastic blend friction material has the advantages of high temperature friction resistance, favorable comprehensive properties and high stability.

Description

technical field [0001] The invention relates to the technical field of friction materials, in particular to a plastic blend friction material and a preparation method thereof. Background technique [0002] Tribological materials, according to the working conditions and requirements of friction elements, can be divided into anti-friction materials, wear-resistant materials and friction materials. According to the type of material, it is divided into metal tribological materials, inorganic non-metallic tribological materials and polymer tribological materials. The perishable characteristics of metal materials hinder their application in special occasions such as navigation or chemical industry; ceramic materials Brittleness hinders its application more seriously, especially the remaining pores of ceramic materials in the sintering process have a considerable impact on performance; polymers and their composite materials have excellent physical and chemical properties, light wei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/16C08L61/28C08K13/04C08K7/26C08K7/08C08K5/372C08K3/34C08G12/32C08J5/14
CPCC08G12/32C08L27/06C08L2201/08C08L2205/035C08L2205/04C08L23/16C08L61/28C08K13/04C08K7/26C08K7/08C08K5/372C08K3/346
Inventor 薛正宇
Owner 来安县隆华摩擦材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products