Method for preparing ceramic permeable ink

A technology of ink and ceramics, which is applied in the field of preparation of ceramic penetrating inks, can solve the problems of poor control of fragrance, low fragrance wrapping rate, short fragrance retention time, etc., and achieve fine and bright colors, good penetration effect and strong three-dimensional effect Effect

Inactive Publication Date: 2017-05-10
FOSHAN GAOMING HAIDI CERAMIC RAW MATERIAL CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the microcapsules on the market usually have the disadvantages of low essence content, low essence encapsulation rate, short fragrance retention time, and cannot control the release of fragrance well.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] A preparation method of guava essence microcapsules is:

[0030] (1) Based on the total weight of 100%, weigh 0.2-0.5% of dimethyl disulfide, 0.1-0.3% of citronellol, 0.04-0.08% of myrcene, 4-10% of ethanol, ethyl acetate Esters 0.25-0.4%, methyl laurate 0.1-0.2%, butyric lactone 0.8-2.1%, trans-2-hexenal 0.03-0.2%, thiomenthone 0.5-0.8%, methyl butyrate Ester 0.2-0.3%, Ethyl Turkone 0.3-0.5%, Ethyl Pinene 1.2-2%, Phenylethyl Acetate 0.6-0.9%, Ethyl Levulinate 0.3-0.6%, Hexanal 0.5-0.8%, Geraniol 0.01-0.03%, diacetyl 0.2-0.4%, propylene glycol balance, mix them evenly to make guava essence;

[0031] (2) Dissolving a certain amount of chitosan in an acetic acid solution with a mass fraction of 1.0% is made into a chitosan-acetic acid solution with a mass fraction of 0.5-3.0%; a certain amount of gelatin is dissolved in distilled water to make a mass fraction of 1.0-3.0% solution, and adjust its pH to 3.0-4.5 with a mass fraction of 10% acetic acid solution to obtain a ...

Embodiment 1

[0041] A preparation method of ceramic penetrating ink, comprising the steps of:

[0042] (1) Weigh 40 parts of zinc acetate, 30 parts of diethylene glycol dibutyl ether, 1 part of guava flavor microcapsules, 1 part of sodium dodecylbenzenesulfonate, and 1 part of fluorocarbon modified silicone;

[0043] (2) After mixing and stirring the zinc acetate, diethylene glycol dibutyl ether, guava essence microcapsules, sodium dodecylbenzenesulfonate and fluorocarbon-modified silicone for 5 hours, pass the resulting solid insoluble matter through It can be removed by filtering or centrifugal separation to obtain a uniform solution containing metal ions, and the solution can be ball-milled or sand-milled.

Embodiment 2

[0045] A preparation method of ceramic penetrating ink, comprising the steps of:

[0046] (1) Weigh 45 parts of zinc acetate, 35 parts of diethylene glycol dibutyl ether, 2 parts of guava flavor microcapsules, 25 parts of sodium dodecylbenzenesulfonate, and 2 parts of fluorocarbon modified silicone;

[0047] (2) After mixing and stirring the zinc acetate, diethylene glycol dibutyl ether, guava essence microcapsules, sodium dodecylbenzenesulfonate and fluorocarbon-modified silicone for 20 hours, pass the resulting solid insoluble matter through It can be removed by filtering or centrifugal separation to obtain a uniform solution containing metal ions, and the solution can be ball-milled or sand-milled.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing ceramic permeable ink. The ceramic permeable ink comprises the following components: 40-45 parts of zinc acetate, 30-35 parts of di-ethylene glycol di-butyl ether, 1-2 parts of guava essence micro capsules, 15-25 parts of sodium dodecyl benzene sulfonate and 1-2 parts of a leveling agent. The ceramic permeable ink has decoration effects of being high in resolution ratio, fine and bright in color and good in three-dimensional feeling, and further has green fragrance and fruit fragrance of guava, so that the additional value of the ink can be increased, the use effect of the ink can be improved, and the ink does not layer, is stable in system and long-lasting in fragrance retention.

Description

technical field [0001] The invention relates to the technical field of ceramic inkjet printing, in particular to a preparation method of ceramic penetrating ink. Background technique [0002] Nowadays, ceramic inkjet printing technology, as a new non-contact, pressure-free and plate-free printing technology, is recognized by the industry as the third technological revolution in the global ceramic industry. However, the development of ceramic inkjet technology has also led to homogeneous competition among ceramic companies. In recent years, many companies have shifted their research and development focus to ceramic inks with special decorative effects, that is, functional inks. Functional ink is a combination of inkjet printing technology and traditional technology. The functional ink is directly sprayed onto the ceramic surface through an inkjet printer, showing special and more three-dimensional textures such as concave-convex texture, metallic luster, bleeding, matte, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/322C09D11/36C09D11/38B01J13/22B01J13/02C12P19/20C12P19/14C12P19/04C08G12/40C08G12/32
Inventor 徐常山
Owner FOSHAN GAOMING HAIDI CERAMIC RAW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com