Glass reinforced plastic and glass reinforced plastic swallow tail made of same

A fiberglass and dovetail technology, applied in the field of railway transportation equipment, can solve problems such as low strength and poor corrosion resistance, achieve the effects of prolonging service life, excellent corrosion resistance and high temperature resistance, and improving production efficiency

Active Publication Date: 2017-05-31
BEIJING TIANYISHANGJIA NEW MATERIAL
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to overcome the defects of low strength and poor corrosion resistance of the existing brake dovetail due to the use of carbon structural steel, and to provide a high strength and good corrosion resistance FRP dovetail and its Production Process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass reinforced plastic and glass reinforced plastic swallow tail made of same
  • Glass reinforced plastic and glass reinforced plastic swallow tail made of same
  • Glass reinforced plastic and glass reinforced plastic swallow tail made of same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The production technology of the FRP dovetail provided by the present embodiment comprises the following steps:

[0044] (1) carbon fiber 15Kg is mixed with non-alkali glass fiber 20Kg, basalt fiber 5Kg and placed in the lower mold in the mold with dovetail shape after being mixed, closes mold on described lower mold loam cake;

[0045] (2) Add iron powder 10Kg, dioctyl phthalate 10Kg, T31 epoxy resin curing agent 4Kg, decabromodiphenyl ether 10Kg, RX-80 resin 2Kg, carbon black 16Kg and quartz powder 20Kg to the molten The slurry is formed in 95Kg of epoxy resin, and then the slurry is injected into the mold through the glue injection port of the upper mold, kept at 110 ° C for 2 minutes, and demoulded to obtain a semi-finished product;

[0046] (3) After the semi-finished product is polished and deburred, the FRP dovetail is obtained.

Embodiment 2

[0048] The production technology of the FRP dovetail provided by the present embodiment comprises the following steps:

[0049] (1) carbon fiber 20Kg is mixed with non-alkali glass fiber 10Kg, basalt fiber 10Kg and placed in the lower mold in the mold with dovetail shape after being mixed, closes mold on described lower mold loam cake;

[0050] (2) 12.5Kg of copper powder, 6Kg of diisodecyl phthalate, 8Kg of amine-105 epoxy resin curing agent, 15Kg of tetrabromobisphenol A, 4,4'-bismaleimide di Add 1Kg of benzene methane, 20Kg of carbon black and 20Kg of moissanite powder into 80Kg of molten epoxy resin to form a slurry, and then inject the slurry into the mold through the injection port of the upper mold, and heat it at 150°C Insulation and curing for 4 minutes, demoulding to obtain a semi-finished product;

[0051] (3) After the semi-finished product is polished and deburred, the FRP dovetail is obtained.

Embodiment 3

[0053] The production technology of the FRP dovetail provided by the present embodiment comprises the following steps:

[0054] (1) carbon fiber 17Kg is mixed with non-alkali glass fiber 18Kg, basalt fiber 6.5Kg and placed in the lower mold in the mold with dovetail shape after being mixed, closes mold on described lower mold loam cake;

[0055] (2) Add 8Kg of iron powder, 5Kg of copper powder, 9Kg of dibutyl phthalate, 5.8Kg of methyl ethyl ketone peroxide, 13Kg of microencapsulated red phosphorus, 1.4Kg of 203 resin, 30Kg of carbon black and 8Kg of quartz powder into Form a slurry in 100Kg of molten epoxy resin, then inject the slurry into the mold through the injection port of the upper mold, heat and solidify at 125°C for 3 minutes, and demould to obtain a semi-finished product;

[0056] (3) After the semi-finished product is polished and deburred, the FRP dovetail is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a glass reinforced plastic and a glass reinforced plastic swallow tail made of the glass reinforced plastic. The glass reinforced plastic is prepared from epoxy resin, carbon fiber, glass fiber, basalt fiber, metal powder, a plasticizer, a curing agent, a flame retardant, a tackifier and a filler. Through reasonable proportioning of the specific raw materials, the tensile strength of the glass reinforced plastic can be increased to be 550 to 600 MPa from 370 to 500 MPa at present, so that the bending parts of the swallow tail made of the glass reinforced plastic are effectively prevented from being cracked, and the safety of the swallow tail in the braking process is guaranteed; the glass reinforced plastic swallow tail provided by the invention also has excellent corrosion resistance and high-temperature resistance, so that the surface treatment working procedure of the swallow tail can be cancelled in the actual production of brake linings, the production efficiency can be improved, the application environment of the brake linings can also be broadened, and the service life is prolonged.

Description

technical field [0001] The invention belongs to the technical field of railway transportation equipment, and in particular relates to a glass fiber reinforced plastic and a glass fiber reinforced plastic dovetail made therefrom. Background technique [0002] With the rapid development of the economy and the continuous improvement of people's living standards, rail transit has gradually developed into my country's important infrastructure, the main artery of the national economy and the preferred tool for people to travel. The development of modernization has made my country's railway industry develop by leaps and bounds. [0003] In the actual operation of urban rail vehicles, a good and stable braking system is the guarantee for their safe operation. Due to the continuous improvement of the running speed of urban rail vehicles, the braking load of the train is greatly increased, which also puts forward higher requirements for the braking system of the train. The brake pad ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08K13/04C08K13/06C08K9/10C08K3/02C08K7/06C08K7/14C08K7/10C08K3/08C08K5/12B29C70/36B29C70/40B29C37/02
CPCB29C37/02B29C70/36B29C70/40C08K3/04C08K3/08C08K5/12C08K7/06C08K7/14C08K13/04C08K2003/085C08K2003/0856C08L63/00C08L2201/08C08K13/06C08K9/10C08K2003/026C08K7/10
Inventor 吴佩芳李君君
Owner BEIJING TIANYISHANGJIA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap