Wear and corrosion resistant oil paint

A corrosion-resistant and paint technology, applied in the field of anti-corrosion paint, can solve the problems of wear resistance, corrosion resistance, shortened service life, surface fracture and damage, etc., to achieve good physical and mechanical properties, prolong service life, and reduce production costs low effect

Inactive Publication Date: 2017-06-13
黄波
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the wear resistance and corrosion resistance of most aluminum products exposed outdoors are not very satisfactory, especially the aluminum doors and windows used in people's daily life, aluminum railings and handrails in public places, etc. In the environment exposed to wind, sun and rain, the surface is corroded, oxidized, and then broken and damaged, which greatly shortens its service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A wear-resistant and corrosion-resistant paint, comprising the following components in parts by weight:

[0015] 30 parts of thermosetting acrylic resin, 20 parts of epoxy resin, 10 parts of polyurethane, 10 parts of perchlorethylene resin, 10 parts of chlorinated rubber, 5 parts of mica powder, 5 parts of sodium nitrite, 1 part of dimethyl tin, 1 part of graphite powder 1 part, 5 parts of kaolin, 1 part of hydroxyethyl methylcellulose, 1 part of pigment, 1 part of xylene, 5 parts of silicone oil.

Embodiment 2

[0017] A wear-resistant and corrosion-resistant paint, comprising the following components in parts by weight:

[0018] 50 parts of thermosetting acrylic resin, 40 parts of epoxy resin, 20 parts of polyurethane, 20 parts of perchlorethylene resin, 20 parts of chlorinated rubber, 10 parts of mica powder, 10 parts of sodium nitrite, 5 parts of dimethyl tin, 5 parts of graphite powder 15 parts of kaolin, 5 parts of hydroxyethyl methylcellulose, 5 parts of pigment, 5 parts of xylene, and 10 parts of silicone oil.

Embodiment 3

[0020] A wear-resistant and corrosion-resistant paint, comprising the following components in parts by weight:

[0021] 40 parts of thermosetting acrylic resin, 30 parts of epoxy resin, 15 parts of polyurethane, 15 parts of perchlorethylene resin, 15 parts of chlorinated rubber, 8 parts of mica powder, 8 parts of sodium nitrite, 2 parts of dimethyl tin, 3 parts of graphite powder 10 parts of kaolin, 2 parts of hydroxyethyl methylcellulose, 3 parts of pigment, 2 parts of xylene, and 8 parts of silicone oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wear-resistant and corrosion-resistant paint, which comprises the following components in parts by weight: 30-50 parts of thermosetting acrylic resin, 20-40 parts of epoxy resin, 10-20 parts of polyurethane, and 10-20 parts of perchlorethylene resin. 20 parts, 10-20 parts of chlorinated rubber, 5-10 parts of mica powder, 5-10 parts of sodium nitrite, 1-5 parts of dimethyl tin, 1-5 parts of graphite powder, 5-15 parts of kaolin, hydroxyethyl 1-5 parts of methyl cellulose, 1-5 parts of pigment, 1-5 parts of xylene, 5-10 parts of silicone oil. The invention is applied to the aluminum profile to greatly improve the properties of wear resistance, scratch resistance, corrosion resistance and oxidation resistance, and prolong the service life of the aluminum profile.

Description

technical field [0001] The invention belongs to the technical field of anti-corrosion paint, and in particular relates to a wear-resistant and corrosion-resistant paint. Background technique [0002] Aluminum alloy is the most widely used non-ferrous metal structural material in industry, and has been widely used in aviation, aerospace, automobile, machinery manufacturing, shipbuilding and chemical industry. The density of aluminum alloy is low, but its strength is relatively high, which is close to or exceeds that of high-quality steel. It has good plasticity and can be processed into various profiles. It has excellent electrical conductivity, thermal conductivity and corrosion resistance. It is widely used in industry, and its usage is second only to aluminum alloy. Yu steel. However, the wear resistance and corrosion resistance of most aluminum products exposed outdoors are not very satisfactory, especially the aluminum doors and windows used in people's daily life, alum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D163/00C09D175/04C09D127/24C09D115/02C09D7/12C09D5/08
Inventor 黄波
Owner 黄波
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap