Agglomerating agent for concrete road plate and preparation method

A technology of concrete roads and gelling agents, which is applied to roads, roads, pavements paved with prefabricated blocks, etc., can solve the problems that urban groundwater cannot be well replenished, increase the cost of municipal facilities, and easily cause floods, etc. Achieve the effects of strong practical application value, improved microstructure and morphology, and easy operation

Inactive Publication Date: 2017-09-19
合肥慧林建材有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional urban concrete pavement blocks the exchange of water and air due to the condensation of mortar, and most of the surface runoff flows into the river through the drainage channel. This not only increases the cost of municipal facilities, but also easily causes flood disasters, and the urban groundwater cannot be well obtained. resupply, land falls, and cities heat up

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] Provided on the one hand is a preparation method for a gelling agent for concrete road slabs, the preparation method of the gelling agent for concrete road slabs comprises the steps:

[0037] Step (1): Weigh the water reducing agent, retarder and toughening agent according to the parts by weight, and mix them evenly to obtain the mixture A;

[0038] Step (2): Weigh 3.1-3.5 μm ultrafine slag powder, zeolite powder, magnesium carbonate powder, sodium dodecylbenzenesulfonate, polyisocyanate, furfuryl ketone resin, and cement according to parts by weight, and mix them evenly to obtain mix B;

[0039] Step (3): Mix the mixture A and the mixture B evenly to obtain the gelling agent for concrete road slabs.

[0040] Compared with the prior art, the present invention has the following beneficial effects:

[0041](1) Fufuryl ketone resin is added in the present invention, which has superior acid resistance, alkali resistance and heat resistance, and can be stable for a long ti...

Embodiment 1

[0047] A kind of gelling agent for concrete road slab provided by this embodiment on the one hand, described gelling agent for concrete road slab comprises the following components by weight: 3.5 μ m ultrafine slag powder 48 parts, zeolite 14 parts of powder, 3 parts of water reducing agent, 1.2 parts of retarder, 9 parts of magnesium carbonate powder, 0.1 part of sodium dodecylbenzenesulfonate, 18 parts of polyisocyanate, 11 parts of furfurone resin, 13 parts of cement, toughening 0.2 parts of the agent.

[0048] The water reducer is composed of the following raw materials in mass percentage: 25% of sodium ethylene polyamine alkyl phosphonate, 0.5% of phosphobutane tricarboxylic acid, 0.5% of sodium lauryl sulfate, and the rest is water.

[0049] The retarder is composed of potassium stearate and sodium hexametaphosphate with a weight ratio of 3.5:1.

[0050] The preparation method of described furfurone resin is as follows:

[0051] Step (1): take 4 parts by weight of furf...

Embodiment 2

[0058] One aspect of this embodiment provides a gelling agent for concrete road slabs. The gelling agent for concrete road slabs includes the following components in parts by weight: 42 parts of 3.1 μm ultrafine slag powder, zeolite 20 parts of powder, 1 part of water reducing agent, 1.5 parts of retarder, 3 parts of magnesium carbonate powder, 3 parts of sodium dodecylbenzenesulfonate, 12 parts of polyisocyanate, 19 parts of furfurone resin, 10 parts of cement, toughening 1.3 parts.

[0059] The water reducer is composed of the following raw materials in mass percentage: 0.5% of sodium ethylene polyamine alkyl phosphonate, 20% of phosphobutane tricarboxylic acid, 0.1% of sodium lauryl sulfate, and the rest is water.

[0060] The retarder is composed of potassium stearate and sodium hexametaphosphate in a weight ratio of 1:1.

[0061] The preparation method of described furfurone resin is as follows:

[0062] Step (1): Take 2 parts by weight of furfural and 4 parts by weight...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of the processing of concrete road plates, and provides an agglomerating agent for a concrete road plate and a preparation method. The agglomerating agent for the concrete road plate is prepared from the following components: 3.1 to 3.5 microns of superfine slag powder, zeolite powder, a water reducing agent, a retardant, magnesium carbonate powder, sodium dodecyl benzene sulfonate, polyisocyanate, furfural acetone resin, cement and a flexibilizer. The polyisocyanate and the furfural acetone resin are added in to the formula of the agglomerating agent, and meanwhile are bound with other components; the manufactured agglomerating agent is enabled to have quite good compression strength and permeability; the performance of the concrete road plate is improved. The preparation method provided by the invention is scientific, reasonable, and simple and is easy to operate. The agglomerating agent is wide in application range and excellent in effect.

Description

technical field [0001] The invention belongs to the technical field of road slab processing, and in particular relates to a gelling agent for concrete road slabs and a preparation method. Background technique [0002] The traditional urban concrete pavement blocks the exchange of water and air due to the condensation of mortar, and most of the surface runoff flows into the river through the drainage channel. This not only increases the cost of municipal facilities, but also easily causes flood disasters, and the urban groundwater cannot be well obtained. The resupply, the ground drops, and the city heats up. Permeable concrete, also known as porous concrete, is characterized by the use of single-grain extremely coarse aggregate as the skeleton, and a thin layer of cement mortar wrapped on the surface of the coarse aggregate particles, which acts as a cementing layer between the aggregate particles to form a skeleton-pore structure. porous concrete material. The key raw mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00E01C5/06
CPCC04B28/00C04B2111/00267C04B2111/00284C04B2111/0075E01C5/065C04B18/141C04B24/003C04B14/047C04B24/04C04B24/16C04B22/16C04B22/10C04B24/125C04B24/20C04B24/30C04B7/02C04B2103/0068
Inventor 刘伍
Owner 合肥慧林建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com