Preparation method and application of heteroatom-doped metal carbon-containing material

A heteroatom and metal technology, applied in the field of preparation of metal carbonaceous materials, can solve the problems of limited degree of graphitization, limited catalytic ability, large specific surface area of ​​materials, etc., and achieves the effect of strong stability and improved electrochemical performance.

Inactive Publication Date: 2017-09-26
北京至心安科技股份有限公司
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Patent "CN 106311152 A" (a mesoporous zeolite-like imidazolate framework material and its preparation method and application) describes a method for preparing zeolite-like imidazole by solvothermal method. The material has a large specific surface area but has no high-efficiency Catalytically active sites and therefore unsuitable for electrode materials
[0004] Patent "CN 104817577 A" (an efficient and simple preparation method and catalytic application of zeolite-like imidazole framework ZIF-8 crystals with different shapes) describes a method for preparing zeolite-like imidazole framework ZIF-8 crystals in methan...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of heteroatom-doped metal carbon-containing material
  • Preparation method and application of heteroatom-doped metal carbon-containing material
  • Preparation method and application of heteroatom-doped metal carbon-containing material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0055] Part of the specific embodiments of the present invention provides a method for preparing a heteroatom-doped metal carbonaceous material, the preparation method comprising the following steps:

[0056] (1) Dissolving metal ions, imidazole ligand compounds and water-soluble polymers in solvent A;

[0057] (2) adding the graphene oxide solution to the solution in step (1) after a period of time;

[0058] (3) mixing and stirring the solutions of steps (1) and (2), separating the solid and liquid, and calcining the obtained precipitate under the protection of an inert gas to obtain a nitrogen-doped metal carbonaceous material;

[0059] (4) Put the nitrogen-doped metal carbonaceous material obtained in step (3) into the high-temperature zone of the double-temperature-controlled vacuum tube furnace, and place the material containing heteroatoms in the low-temperature zone, and heat it under high temperature with inert protective gas and low pressure. calcining to obtain a he...

Embodiment 1

[0061] A method for preparing a three-dimensional cobalt-carbon material doped with boron and nitrogen atoms, the preparation method comprising the following steps:

[0062] (1) Dissolve 0.5 M cobalt sulfate, 0.5 M 2-methylimidazole and 0.5 g polyacrylamide in 50 mL acetonitrile solvent, and stir at 200 rpm;

[0063] (2) After 30 s, add 0.1 g / L, 1 mL graphene oxide solution to the solution in step (1);

[0064] (3) Mix the solutions obtained in steps (1) and (2) and stir at a speed of 200 rpm for 1 h, then centrifuge at a speed of 10,000 rpm for 1 min to separate the solid from the liquid. Drying at 80 ℃ for 12 h, followed by calcination under nitrogen protection for 2 h, the calcination temperature was 750 ℃, and the calcination heating rate was 5 ℃ / min to obtain the nitrogen-doped cobalt carbon material N-Co / C-1;

[0065] (4) Put 1 g of the N-Co / C-1 material obtained in step (3) into the high-temperature zone of a double-temperature-controlled vacuum tube furnace for 10 min...

Embodiment 2

[0068] A method for preparing a three-dimensional cobalt-carbon material doped with fluorine, boron and nitrogen atoms, the preparation method comprising the following steps:

[0069] (1) Dissolve 0.5 M cobalt oxide, 1 M 4-nitroimidazole and 4 g polyvinylpyrrolidone in 50 mL N,N-dimethylacetamide solvent;

[0070] (2) After 60 s, add 1 g / L, 4 mL graphene oxide solution to the solution in step (1);

[0071] (3) Mix the solutions of steps (1) and (2) and stir at 200 rpm for 1.5 h, then centrifuge at 11,000 rpm for 2 min to separate the solid from the liquid. Drying at ℃ for 14 h, calcining for 3 h under the protection of nitrogen, the calcination temperature is 700 ℃, and the calcination heating rate is 6 ℃ / min, and the nitrogen-doped three-dimensional cobalt carbon material N-Co / C-2 is obtained;

[0072] (4) Put the N-Fe / C-4 material obtained in step (3) into the high-temperature zone of a double-temperature-controlled vacuum tube furnace for 20 min. The temperature in the hig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method and application of a heteroatom-doped metal carbon-containing material. The preparation method comprises the following steps: dissolving metal ions, an imidazole ligand compound and a water-soluble high molecular polymer into a solvent A respectively; adding a graphene oxide solution after a period of time; mixing and stirring; carrying out solid-liquid separation and calcining obtained sediment under the protection of inert gas to obtain a nitrogen-doped metal carbon-containing material; doping the nitrogen-doped metal carbon-containing material with other heteroatoms under a chemical vapor deposition condition; carrying out high-temperature calcining under inert protection gas and low pressure so as to obtain the heteroatom-doped metal carbon-containing material. The material provided by the invention can be used as an electrode material and is used for heavy metal detection, organic matter detection, active carbon detection or oxygen reduction reaction and the like.

Description

technical field [0001] The invention relates to the field of material preparation, in particular to a preparation method and application of a heteroatom-doped metal carbonaceous material. Background technique [0002] Recently, as a new type of material, zeolitic imidazolate frameworks (ZIFs) cracked at high temperature have been widely used in various electrochemical reactions, because compared with commercial Pt / C, IrO2 and other materials, its It has more stable performance. ZIFs are a series of porous crystals with a three-dimensional topology, which are formed through the coordination between transition metals and imidazole ligands, and belong to Metal-Organic Frameworks (MOFs). The "M-Im-M" bond is formed between the metal and the ligand in ZIFs, and the included angle is consistent with that of zeolite SiO2, so it is named as the zeolite-like imidazole structure. Due to the existence of these rings, the formed molecular sieves form standard channels or cages. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G9/00C01G49/00C01G51/00C25B1/02C25B11/04H01G11/24H01G11/30
CPCY02E60/13C01G51/00C01G9/00C01G49/00C01P2004/03C01P2004/04C01P2004/80C25B1/02C25B11/04H01G11/24H01G11/30
Inventor 李泽晖曹友錋罗扬王温博孙绍铭
Owner 北京至心安科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap