A technology of bricks and tiles, which is applied in the field of colored bricks and tiles and its production technology, can solve the problems of easy cracking and poor waterproof performance, achieve the effects of good crack resistance and waterproof performance, avoid firing process, and improve waterproof effect

Inactive Publication Date: 2017-11-17
安徽维东建材股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the disadvantages of easy cracking and poor waterproof performance of the colored tiles in the prior art, and to provide a colored tile with the advantages of crack resistance and waterproof. Another purpose of the present invention is to provide a colored tile The production process of bricks and tiles is simple and efficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Color brick tile and production technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The preparation of colored bricks and tiles, the weight ratio of raw materials: 30 parts of cement, 10 parts of quartz sand, 30 parts of river sand, 2 parts of iron red, 3 parts of glass fiber, 2 parts of sodium carbonate, 1 part of brightener, 4 parts of additives, 1 part of additive and 20 parts of water;

[0025] The preparation of auxiliary agent, raw material weight ratio: 1 part of maleic anhydride, 1 part of gum arabic, 2 parts of Tween-80, 1 part of acetone, 2 parts of sodium sodium stearate and 6 parts of water, the The preparation method of the auxiliary agent is as follows:

[0026] Step S1: Add gum arabic and Tween-80 into water and put into the reaction kettle, set the temperature at 50-60°C, and stir at 200-300r / min for 20-30min;

[0027] Step S2: Weigh maleic anhydride, acrylic acid and benzylidene acetone according to the ratio, mix them evenly, and put them into the reactor. Stir at 800-100r / min for 50-60min to obtain;

[0028] The production process...

Embodiment 2

[0036] The preparation of colored bricks and tiles, the weight ratio of raw materials: 32 parts of cement, 12 parts of quartz sand, 32 parts of river sand, 3 parts of iron red, 5 parts of glass fiber, 4 parts of sodium carbonate, 1.5 parts of brightener, 5 parts of additives, 2 parts of additives and 22 parts of water;

[0037] The preparation of auxiliary agent, raw material weight ratio: 1.5 parts of maleic anhydride, 1.5 parts of gum arabic, 3 parts of Tween-80, 1.5 parts of Bianzacetone, 3 parts of sodium sodium stearate and 8 parts of water, described The preparation method of the auxiliary agent is as follows:

[0038] Step S1: Add gum arabic and Tween-80 into water and put into the reaction kettle, set the temperature at 50-60°C, and stir at 200-300r / min for 20-30min;

[0039] Step S2: Weigh maleic anhydride, acrylic acid and benzylidene acetone according to the ratio, mix them evenly, and put them into the reactor. Stirring at 800-100r / min for 50-60min, that is.

Embodiment 3

[0041] The preparation of colored bricks and tiles, the weight ratio of raw materials: 35 parts of cement, 15 parts of quartz sand, 35 parts of river sand, 3 parts of iron red, 4 parts of glass fiber, 4 parts of sodium carbonate, 2 parts of brightener, 5 parts of additives, 2 parts of additives and 25 parts of water;

[0042] The preparation of auxiliary agent, raw material weight ratio: 1 part of maleic anhydride, 1.5 parts of gum arabic, tween-804 parts, 2 parts of acetone, 2 parts of sodium sodium stearate and 8 parts of water, described The preparation method of auxiliary agent is as follows:

[0043] Step S1: Add gum arabic and Tween-80 into water and put into the reaction kettle, set the temperature at 50-60°C, and stir at 200-300r / min for 20-30min;

[0044] Step S2: Weigh maleic anhydride, acrylic acid and benzylidene acetone according to the ratio, mix them evenly, and put them into the reactor. Stirring at 800-100r / min for 50-60min, that is.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a color brick tile. The color brick tile is prepared from the following raw materials in parts by weight: 35 parts of cement, 12 parts of quartz sand, 35 parts of river sand, 3 parts of iron oxide red, 4 parts of glass fiber, 3 parts of sodium carbonate, 1.5 parts of brightener, 5 parts of accessory ingredient and 25 parts of water. According to a ratio, the cement, the quartz sand, the river sand, the iron oxide red and the sodium carbonate are weighed; the quartz sand and the river sand of which the grain size is 4.5mm are grinded and smashed to 100 meshes and are evenly mixed; the glass fiber is added, and acrylic ester coating and pigment can be sprayed to finally obtain a finished tile by vibration. Compared with the prior art, the color brick tile has the following advantages that the brightener is added into the color brick tile, so that the prepared color brick tile has the advantages of smooth surface and good brightness, and meanwhile, the water-proof effect of the color brick tile is further improved through the application of the acrylic ester coating. In conclusion, the technical scheme of the invention is adopted, production efficiency is high, and the produced color brick tile has the advantages of high strength, safety, reliability, long service life, even material distribution and good pigment adhesion and is capable of preventing cracking.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a colored brick tile and a production process thereof. Background technique [0002] The scientific name of colored brick tiles is colored concrete tiles, also known as colored cement tiles, cement colored tiles, etc. The colored tiles on the market generally refer to colored cement tiles. It is a new type of roof decoration building material in recent years. Colored tiles are made of cement, sand, etc. after a reasonable ratio, passed through a mold, and pressed under high pressure. It has the advantages of strong pressure resistance and high bearing capacity. Relevant national standards include JC / T746-2007 standard. [0003] Compared with ordinary kiln-fired tiles, colored concrete tiles have the advantages of strong impermeability, strong bearing capacity, and low water absorption. Cement tiles have the advantages of high density, high strength, light weight, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B41/62
Inventor 梁维东
Owner 安徽维东建材股份有限公司