Graphene conductive coating and preparation method thereof

A conductive coating and graphene technology, applied in the direction of conductive coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems that affect the coating construction and performance, and the coating cannot be kept stable for a long time, so as to improve the electron transmission rate and solve the problem of transparency. The effect of poor light and good adhesion

Inactive Publication Date: 2018-03-30
NINGBO SHIHONG QIANXI TRADE CO LTD
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the application of graphene in conductive coatings, graphene is very prone to agglomeration and stratification, which makes the coating unable to maintain stability for a long time, and affects the construction and performance of the coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A graphene conductive paint, comprising each component of the following parts by weight: 15 parts of graphene, 15 parts of carbon nanotubes, 6 parts of conductive carbon black, 10 parts of amino resins, 2 parts of carboxylic acid polymer dispersants, poly 5 parts of styrene-acrylate, 4 parts of adhesion promoter, 3 parts of silicone leveling agent, 0.5 parts of photoinitiator, 50 parts of toluene.

[0023] Wherein, the adhesion promoter includes the following components in parts by weight: 10 parts of butyl acetate, 15 parts of chlorinated acrylic resin, 40 parts of propylene glycol methyl ether acetate, 15 parts of maleic anhydride resin, 20 parts of n-butanol, 25 parts of water, 20 parts of phosphoric acid; the preparation method of the adhesion promoter comprises the following steps: adding propylene glycol methyl ether acetate, maleic anhydride resin, n-butanol and water into the container in proportion; start stirring, and add chlorinated acrylic resin After it is ...

Embodiment 2

[0029] A kind of graphene conductive paint, comprises each component of following parts by weight: 30 parts of graphenes, 5 parts of carbon nanotubes, 2 parts of conductive carbon blacks, 30 parts of alkyd resins, 5 parts of carboxylic acid polymer dispersants, 2 parts of fluoroacrylate, 2 parts of adhesion promoter, 1 part of acrylic leveling agent, 0.7 parts of photoinitiator, 40 parts of acetone.

[0030] Wherein, the adhesion promoter includes the following components in parts by weight: 5 parts of butyl acetate, 20 parts of chlorinated acrylic resin, 30 parts of propylene glycol methyl ether acetate, 4 parts of maleic anhydride resin, 10 parts of n-butanol, 15 parts of water, 5 parts of phosphoric acid;

[0031] The preparation method of the adhesion promoter comprises the following steps: sequentially adding propylene glycol methyl ether acetate, maleic anhydride resin, n-butanol and water into the container in proportion; starting stirring, adding chlorinated acrylic re...

Embodiment 3

[0037] A graphene conductive paint, comprising each component of the following parts by weight: 20 parts of graphene, 20 parts of carbon nanotubes, 10 parts of conductive carbon black, 20 parts of epoxy resin, 3 parts of carboxylic acid polymer dispersants, 3 parts of polyurethane, 5 parts of adhesion promoter, 5 parts of acrylic leveling agent, 1.0 part of photoinitiator, 30 parts of xylene.

[0038] Wherein, the adhesion promoter includes the following components in parts by weight: 15 parts of butyl acetate, 30 parts of chlorinated acrylic resin, 20 parts of propylene glycol methyl ether acetate, 12 parts of maleic anhydride resin, 15 parts of n-butanol, 10 parts of water, 10 parts of phosphoric acid; the preparation method of the adhesion promoter comprises the following steps: adding propylene glycol methyl ether acetate, maleic anhydride resin, n-butanol and water into the container in proportion; Acrylic resin, after it is completely dissolved, add butyl acetate; after st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a graphene conductive coating and a preparation method thereof. The graphene conductive coating is prepared from the following components in parts by weight: 15 to 30 parts ofgraphene, 5 to 20 parts of carbon nano pipes, 2 to 10 parts of conductive carbon black, 10 to 30 parts of matrix resin, 2 to 5 parts of dispersing agents, 2 to 5 parts of binding agents, 2 to 5 partsof adhesion promoters, 1 to 5 parts of flatting agents, 0.5 to 1.0 part of a photoinitiator and 30 to 50 parts of organic solvents. According to the graphene conductive coating and the preparation method thereof, the graphene and the carbon nano pipes firstly form a graphene / carbon nano pipe composite material, the graphene and the carbon nano pipes can be mixed to be evener under the effect of critical fluid, the Van Der Waals' force among layers of the graphene is damaged through pressure released instantaneously, and thus the graphene is not easy to agglomerate.

Description

technical field [0001] The invention belongs to the technical field of conductive paint, in particular to a graphene conductive paint and a preparation method thereof. Background technique [0002] Conductive coatings have been developed for about half a century. It is a functional coating that has developed rapidly with modern science and technology. At present, conductive coatings play an important role in various military and civilian industrial fields such as electronics, electrical appliances, aviation, and printing. [0003] Conductive coatings can be traced back to the patent of conductive adhesive made of silver and epoxy resin in the United States in 1948, and then in the 1950s, my country also began to enter the field of conductive coatings. The most commonly used conductive fillers in coatings are graphite fillers, metal fillers, metal oxide fillers, etc. Since the advent of graphene in 2004, this "miracle material" has attracted great interest from the global s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/20C09D167/08C09D163/00C09D133/00C09D5/24C09D7/65
CPCC09D161/20C08K2201/001C08K2201/011C08K2201/014C08L2205/035C09D5/24C09D133/00C09D163/00C09D167/08C08L33/02C08K13/06C08K9/02C08K3/04C08K7/24
Inventor 贾龙沈宏斌
Owner NINGBO SHIHONG QIANXI TRADE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com