Preparation method of alkyd resin coating capable of forming flat surface

An alkyd resin, surface smoothing technology, applied in polyester coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of unsightly surface and poor dispersion, and achieve bright gloss, enhanced adhesion performance, and film smooth surface effect

Inactive Publication Date: 2018-04-03
合肥林邦门业有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Water-based coatings with alkyd resins as film-formers have become the most commonly used water-based coating systems due to their excellent weather resistance, oil resistance and high hardness. However, water-based alkyd resins have the disadvantage of poor dispersion, and there are uneven surfaces on the painted surface. , the surface is not beautiful, and it needs to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A method for preparing an alkyd resin paint with smooth surface, comprising the steps of:

[0020] S1. Stir 50kg of polyvinyl alcohol and 16kg of bamboo charcoal powder for 40min at a stirring temperature of 90°C, add 2kg of silane coupling agent and grind for 40min at a grinding pressure of 4kPa, add 12kg of agarose for ultrasonic treatment for 40min at a power of 550W, and obtain the first materials;

[0021] S2. Mix 12kg of fumed silica, 12kg of wollastonite powder, 4kg of vermiculite powder, 12kg of nano-talc powder, 8kg of ethyl acetate, 8kg of the first material, and 60kg of water, and ultrasonically disperse it for 50 minutes with an ultrasonic power of 700W to obtain the second material ;

[0022] S3, 80kg phenolic modified alkyd resin, 20kg acrylic acid modified alkyd resin, 20kg diethylene glycol methyl ether acetate, 6kg ethylene glycol, 8kg water-based polyurethane resin, 4kg polyamide polyamine epichlorohydrin resin, Stir 12kg of oxidized polyethylene wax...

Embodiment 2

[0024] A method for preparing an alkyd resin paint with smooth surface, comprising the steps of:

[0025] S1. Stir 60kg of polyvinyl alcohol and 8kg of bamboo charcoal powder for 80min at a stirring temperature of 80°C, add 4kg of silane coupling agent and grind for 20min at a grinding pressure of 6kPa, add 6kg of agarose for ultrasonic treatment for 60min at an ultrasonic power of 400W, and obtain the first materials;

[0026] S2. Mix 16kg of fumed silica, 8kg of wollastonite powder, 8kg of vermiculite powder, 6kg of nano talc powder, 16kg of ethyl acetate, 4kg of the first material, and 120kg of water, and disperse it ultrasonically for 30 minutes with an ultrasonic power of 850W to obtain the second material ;

[0027] S3, with 60kg phenolic modified alkyd resin, 26kg acrylic acid modified alkyd resin, 10kg diethylene glycol methyl ether acetate, 10kg ethylene glycol, 4kg waterborne polyurethane resin, 10kg polyamide polyamine epichlorohydrin resin, Stir 6kg of oxidized p...

Embodiment 3

[0029] A method for preparing an alkyd resin paint with smooth surface, comprising the steps of:

[0030] S1. Stir 58kg of polyvinyl alcohol and 10kg of bamboo charcoal powder for 70min at a stirring temperature of 82°C, add 3.5kg of silane coupling agent and grind for 25min at a grinding pressure of 5.5kPa, add 8kg of agarose for ultrasonic treatment for 55min at an ultrasonic power of 450W, and obtain first material;

[0031] S2. Mix 15kg of fumed silica, 9kg of wollastonite powder, 7kg of vermiculite powder, 8kg of nano talc powder, 14kg of ethyl acetate, 5kg of the first material, and 100kg of water, and disperse it ultrasonically for 35 minutes with an ultrasonic power of 800W to obtain the second material ;

[0032] S3, with 65kg phenolic modified alkyd resin, 24kg acrylic acid modified alkyd resin, 12kg diethylene glycol methyl ether acetate, 9kg ethylene glycol, 5kg waterborne polyurethane resin, 8kg polyamide polyamine epichlorohydrin resin, Stir 8kg of oxidized pol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of an alkyd resin coating capable of forming flat surfaces. The method comprises the steps as follows: polyvinyl alcohol and bamboo charcoal powder are stirred, a silane coupling agent is added, grinding is performed, agarose is added, ultrasonic treatment is performed, and a first material is obtained; fumed silica, wollastonite powder, vermiculite powder, nano talcum powder, acetic ether, the first material and water are mixed, ultrasonic treatment is performed, and a second material is obtained; phenolic aldehyde modified alkyd resin, acrylic acid modified alkyd resin, diethylene glycol methyl ether acetate, ethylene glycol, waterborne polyurethane resin, polyamide polyamine epoxy chloropropane resin and oxidized polyethylene wax are uniformly stirred, the second material, polyoxypropylene glycerol ether, hydroxyl silicone oil, sodium lauryl sulfate, a wetting agent and a preservative are added, the mixture is stirred continuously, and the alkyd resin coating capable of forming the flat surfaces is obtained. The method is simple, and the obtained coating has good base material adhesion and film compactness, is not prone to peeling offand has good heat and damp resistance and temperature change resistance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a method for preparing alkyd resin coatings with smooth surfaces. Background technique [0002] In the process of modern home decoration, it is inevitable to come into contact with a large amount of paint, especially in order to make the furniture beautiful, the manufacturer will coat a large amount of paint on the surface of the furniture. With the gradual improvement of living standards, people's awareness of environmental protection and health has become stronger and stronger, and more requirements have been placed on the coatings used on the surface of furniture. In addition to stable quality and beautiful coating, there are also such as no peculiar smell, no poison Volatilization of substances, environmental protection and other requirements. [0003] A large amount of organic volatiles are used in traditional furniture coatings, which has caused great harm to the environm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D175/04C09D123/30C09D129/04C09D183/06C09D7/61C09D7/63
CPCC08L2205/025C08L2205/035C09D167/08C08L67/08C08L75/04C08L23/30C08L29/04C08L83/06C08K13/02C08K3/36C08K3/34C08K5/101C08K5/053C08K3/04
Inventor 袁中领
Owner 合肥林邦门业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap