Ageing-resistant environment-friendly lawn particle

An anti-aging and lawn technology, which is applied in the formulation and preparation of anti-aging and environmentally friendly plastic particles, can solve the problems of strong odor, single color, and poor quality of tire raw materials, and achieve high strength, good elasticity, and good aging resistance.

Inactive Publication Date: 2018-04-06
QINGDAO UNIV OF SCI & TECH
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, rubber granules for artificial turf at home and abroad, especially black waste tire granules, are mainly used in China. Although the cost of waste tire granules is low, and can alleviate the problems of rubber resource shortage and waste tire environmental pollution, however, Tire granules also have disadvantages such as inferior tire raw materials, strong smell, single color, and cannot be recycled and reused.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 100 parts by weight of raw rubber, 150 parts by weight of filler, 5 parts by weight of plasticizer, 1 part by weight of antioxidant, 0.7 parts by weight of vulcanizing agent, 0.2 parts by weight of accelerator, 1.2 parts by weight of activator, and 3 parts by weight of colorant. Among them, the raw rubber is CM / EPDM / SBS with a ratio of 60 / 25 / 15; the filler is calcium carbonate; the plasticizer is paraffin oil; the anti-aging agent is anti-aging agent Alba; the vulcanizing agent is dicumyl peroxide DCP; The accelerator is TAIC; the activator is zinc oxide; the colorant is cyanine green G.

[0026] The temperature of the internal mixer is set at 90°C, and the chlorinated polyethylene rubber / EPDM rubber is put into the internal mixer according to the ratio, and fillers, plasticizers, anti-aging agents, vulcanizing agents, accelerators, activators, Colorants, etc., are uniformly discharged after mixing for 8 minutes, and the thin slices are removed and parked for 24 hours t...

Embodiment 2

[0028] 100 parts by weight of raw rubber, 120 parts by weight of filler, 10 parts by weight of plasticizer, 1 part by weight of antioxidant, 1 part by weight of vulcanizing agent, 1 part by weight of accelerator, 1.2 parts by weight of activator, and 6 parts by weight of colorant; wherein, the The raw rubber is chlorinated polyethylene / nitrile rubber / ethylene vinyl acetate, the ratio is 70 / 15 / 15; the filler is kaolin; the plasticizer is paraffin oil; the anti-aging agent is anti-aging agent BBM; the vulcanizing agent is peroxide Cumene DCP; the vulcanization accelerator is TMTD, TAIC; the activator is zinc oxide; the colorant is 5952 pigment green B.

[0029] The temperature of the internal mixer is set at 100°C, and the raw rubber is put into the internal mixer according to the proportion, and fillers, plasticizers, anti-aging agents, vulcanizing agents, accelerators, activators, colorants, etc. are added in sequence, and the mixture is uniform after mixing for 8 minutes. Dis...

Embodiment 3

[0031] 100 parts of raw rubber, 100 parts of filler, 10 parts of plasticizer, 1 part of anti-aging agent, 1.5 parts of dye.

[0032] Among them, the raw rubber is chlorinated polyethylene / ethylene vinyl acetate, the ratio is 80 / 20; the filler is calcium carbonate and kaolin; the plasticizer is environmentally friendly naphthenic oil; the anti-aging agent is anti-aging agent W-300; The agent is 5001 rubber green 2B.

[0033] The temperature of the internal mixer is set at 90°C, and the chlorinated polyethylene / ethylene vinyl acetate elastomer is put into the internal mixer, and fillers, plasticizers, anti-aging agents, etc. Refining for 8 minutes, discharging, and tableting to obtain the mixed rubber. Put the mixed film into the extruder at a temperature of 110°C, extrude the rubber strip, and after the rubber strip is soaked in the release agent, send it into the electron accelerator irradiator or cobalt 60 irradiator for irradiation cross-linking. The dosage is 40KGy, and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of artificial lawn particles. The formula of the lawn particles comprises the following components: 100 parts of raw rubber, 20-150 parts of filler, 0-20 parts of a plasticizer, 0-6 parts of an active agent, 1-5 parts of an anti-ageing agent, 0-5 parts of a vulcanizing agent, 0-6 parts of an accelerant and 1-8 parts of a coloring agent. The preparation method comprises the following production steps: (1) adding rubber compounds into an internal mixer according to a ratio, sequentially adding the filler, plasticizer, anti-ageing agent, vulcanizing agent and the like, mixing and uniformly discharging, and batching-off so as to obtain a rubber master batch; (2) placing the rubber master batch on an open mill, uniformly mixing, and batching-off sheets; and (3) extruding the sheets in an extruder to form strips, granulating after cross-linking, or performing extrusion granulation and cross-linking. The lawn particles provided by the invention arelightweight, high in strength, environmentally friendly and excellent in ageing resistance. Moreover, the particles have the characteristics of being difficult to discolor and long in service life.

Description

technical field [0001] The invention belongs to the field of polymer materials, and more specifically relates to a formula and a preparation method of aging-resistant and environment-friendly plastic particles filled in artificial turf. Background technique [0002] Artificial turf is a artificial lawn made of non-living plastic chemical fiber products. Unlike natural turf, it does not need to consume resources such as fertilizers and water necessary for growth. It can meet the needs of high-intensity sports 24 hours a day, and has simple maintenance, rapid drainage, and excellent site flatness. Artificial turf has the advantages of bright appearance, green seasons, vividness, good drainage, long service life, and low maintenance costs. Artificial turf is widely used in special venues for hockey, baseball, and rugby, public practice fields for sports such as football, tennis, and golf, or as ground pavement to beautify the indoor environment. The rubber particles are locat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L53/02C08L91/06C08L9/02C08L23/08C08L7/00C08K13/02C08K3/26C08K5/14C08K3/22C08K3/34
CPCC08L23/286C08L2205/035C08L2205/02C08L2201/08C08L23/16C08L53/02C08L91/06C08K13/02C08K2003/265C08K5/14C08K2003/2296C08L9/02C08L23/0853C08K3/34C08K3/346C08L7/00C08L23/0815
Inventor 张振秀郎咸华孙琰张昕
Owner QINGDAO UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com