Corrosion-resistant and fireproof coating
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A refractory coating and corrosion-resistant technology, applied in the field of coatings, can solve the problems of poor fire resistance, shortened service life, and low corrosion resistance, and achieve the effects of improving gloss, good wear resistance and improving strength
Inactive Publication Date: 2018-04-24
ENG EQUIP CO LTD SUZHOU SAI SIDE
View PDF4 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] At present, most of the coatings used in the furniture field have poor fire resistance, and the corresponding corrosion resistance is not high. In the long-term use process, the service life will be shortened.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] This embodiment provides a corrosion-resistant and fire-resistant coating, which includes the following components in parts by mass: water-based polyurethane resin: 57 parts, acetone: 4 parts, maleic acid resin: 17 parts, nano-zincphosphate: 3 parts, polyurethane polymerization Compound: 10 parts, cellulose acetate: 12 parts, ammonium dodecylbenzenesulfonate: 2 parts, p-methoxyphenol: 2 parts, polyvinyl alcohol: 8 parts, azodimethylvaleronitrile: 2 parts , Organic bentonite: 13 parts, triethanolamine: 5 parts, microgel: 6 parts, aluminum dihydrogen phosphate: 4 parts, empty glass microspheres: 12 parts, polydimethylsiloxane: 3 parts, nano pigments: 7 parts, dipentaerythritol: 3 parts, filler: 13 parts, leveling agent: 4 parts, sealing agent: 3 parts, dispersant: 6 parts, wetting agent: 4 parts, stabilizer: 3 parts, defoamer: 5 parts , solvent: 4 parts;
[0017] Among them, the defoaming agent is trifluoropropyl methyl silicone oil; the filler is one or more mixtures o...
Embodiment 2
[0019] This embodiment provides a corrosion-resistant and fire-resistant coating, which includes the following components in parts by mass: water-based polyurethane resin: 57 parts, acetone: 4 parts, maleic acid resin: 17 parts, nano-zinc phosphate: 3 parts, polyurethane polymerization Compound: 10 parts, cellulose acetate: 12 parts, ammonium dodecylbenzenesulfonate: 2 parts, p-methoxyphenol: 2 parts, polyvinyl alcohol: 8 parts, azodimethylvaleronitrile: 2 parts , Organic bentonite: 13 parts, triethanolamine: 5 parts, microgel: 6 parts, aluminum dihydrogen phosphate: 4 parts, empty glass microspheres: 15 parts, polydimethylsiloxane: 3 parts, nano pigments: 7 parts, dipentaerythritol: 3 parts, filler: 13 parts, leveling agent: 4 parts, sealing agent: 3 parts, dispersant: 6 parts, wetting agent: 4 parts, stabilizer: 3 parts, defoamer: 5 parts , solvent: 4 parts;
[0020] Among them, the defoaming agent is trifluoropropyl methyl silicone oil; the filler is one or more mixtures o...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses corrosion-resistant and fireproof coating. The corrosion-resistant and fireproof coating comprises, by mass, 50-60 parts of water-based polyurethane, 3-5 parts of acetone, 15-20 parts of maleic resin, 2-3 parts of nano zincphosphate, 5-13 parts of polyurethanepolymer, 11-13 parts of cellulose acetate, 1-3 parts of ammoniumdodecylbenzenesulfonate, 1-2 parts of 4-methoxyphenol, 6-10 parts of polyvinyl alcohol, 1-2 parts of azo dimethyl valeronitrile, 10-15 parts of organic bentonite, 3-6 parts of triethanolamine, 2-7 parts of microgel, 2-4 parts of aluminum dihydrogenphosphate, 1-3 parts of polydimethyl siloxane, 4-7 parts of nano pigment, 2-3 parts of dipentaerythritol, 10-13 parts of filler, 2-4 parts of leveling agent, 2-3 parts of sealing agent, 5-7 parts ofdispersing agent, 2-4 parts of wetting agent, 1-3 parts of stabilizer, 3-5 parts of defoaming agent and 2-4 parts of solvent.
Description
technical field [0001] The invention relates to the technical field of coatings, in particular to a corrosion-resistant and refractorycoating. Background technique [0002] At present, most of the coatings used in the furniture field have poor fire resistance, and the corresponding corrosion resistance is not high. In the long-term use process, the service life is shortened. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a corrosion-resistant and refractory coating for the above shortcomings of the prior art. [0004] The technical scheme for solving the above technical problems of the present invention is: a corrosion-resistant fire-resistant coating, comprising the following components in parts by mass: water-based polyurethane resin: 50-60 parts, acetone: 3-5 parts, maleic acid resin: 15 parts -20 parts, nano zincphosphate: 2-3 parts, polyurethane polymer: 5-13 parts, cellulose acetate: 11-13 parts, ammoni...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More