Preparation method of polyester porous yarn

A technology of porous yarn and polyester, applied in the direction of filament/thread forming, single-component copolyester artificial filament, fiber type, etc., which can solve the problem of poor oil permeability, decreased silk quality, and increased silk friction coefficient etc. to achieve good lubricity, increase strength, and prevent fiber damage

Active Publication Date: 2018-05-04
JIANGSU HENGLI CHEM FIBER
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the problems in the prior art that the permeability of the oil agent is poor due to the small specific surface area of ​​the fibers, the friction coefficient between the silks increases, and the quality of the silks decreases, and to provide a fiber with a soft and fine appearance. Preparation method of polyester porous yarn with good texture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polyester porous yarn
  • Preparation method of polyester porous yarn
  • Preparation method of polyester porous yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A kind of preparation method of polyester porous yarn, concrete steps are as follows:

[0054] (1) Oil preparation for oiling: 2-hydroxymethyl-12-crown-4, potassium dodecyl phosphate, trimethylolpropane laurate and sodium dodecylsulfonate are mixed at room temperature After mixing evenly, add it to 9# mineral oil and stir evenly at 40°C for 1 hour to obtain an oil agent; in parts by weight, the addition amount of each component is as follows: 2 parts of 9# mineral oil; trimethylolpropane lauric acid 10 parts of ester; 90 parts of 2-hydroxymethyl-12-crown-4; 8 parts of potassium dodecyl phosphate; 3 parts of sodium dodecyl sulfonate. The content of the crown ether in the prepared oil is 79.6wt%. The high temperature resistance of the oil is excellent. After heat treatment at 200°C for 2 hours, the thermal weight loss is 14.5wt%. The viscosity of the oil is low, at (50 ± 0.01) At ℃, the kinematic viscosity is 29.6mm 2 / s, the kinematic viscosity after the concentration ...

Embodiment 2

[0061] A kind of preparation method of polyester porous yarn, concrete steps are as follows:

[0062] (1) Preparation of oil agent for oiling: 15-crown ether-5 and isomeric tridecyl alcohol polyoxyethylene ether phosphate potassium salt, trimethylolpropane laurate and sodium pentadecyl sulfonate at room temperature After mixing evenly under low pressure, add it to 10# mineral oil and stir evenly at 43°C for 1.5h to obtain an oil agent; the addition amount of each component is as follows in parts by weight: 2 parts of 10# mineral oil; trimethylolpropane lauryl 15 parts of acid ester; 70 parts of 15-crown ether-5; 10 parts of isomeric tridecyl polyoxyethylene ether phosphate potassium salt; 7 parts of sodium pentadecylsulfonate. The content of crown ether in the prepared oil is 67.30wt%. The oil has excellent high temperature resistance. After heat treatment at 200°C for 2 hours, the thermal weight loss is 13wt%. The viscosity of the oil is low. When the kinematic viscosity is ...

Embodiment 3

[0069] A kind of preparation method of polyester porous yarn, concrete steps are as follows:

[0070] (1) Preparation of oil for oiling: 2-hydroxymethyl-15-crown-5, potassium salt of tetradecyl phosphate, trimethylolpropane laurate and sodium pentadecylsulfonate in After mixing evenly at room temperature, add it to 11# mineral oil and stir evenly at 48°C for 3 hours to obtain an oil agent; in parts by weight, the addition amount of each component is as follows: 8 parts of 11# mineral oil; trimethylolpropane lauryl 10 parts of acid ester;

[0071] 2-Hydroxymethyl-15-crown-585 parts; Tetradecyl phosphate potassium salt 11 parts; Sodium pentadecylsulfonate 5 parts. The content of crown ether in the prepared oil is 70.83wt%. The oil has excellent high temperature resistance. After heat treatment at 200°C for 2 hours, the thermal weight loss is 11wt%. The viscosity of the oil is low. When the kinematic viscosity is 30.1mm 2 / s, the kinematic viscosity after the concentration is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
surface tensionaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a polyester porous yarn. A polyester fusant is subjected to metering, porous spinning plate extrusion, cooling, oiling, stretching, heat setting and winding to prepare the polyester porous yarn, wherein the pore number of a porous spinning plate is 144 to 288; an oil agent for oiling contains crown ether; the content of crown ether is 67.30 to 85.58weight percent; after the oil agent is subjected to heating treatment for 2h at 200 DEG C, the heat weight loss is smaller than 15 weight percent; when the oil agent is 50+ / -0.01 DEG C, the movementviscosity is 27.5 to 30.1 mm<2> / s; after the oil agent is prepared into an emulsion with the concentration being 10 weight percent, the movement viscosity is 0.93 to 0.95 mm<2> / s; the oil film intensity of the oil agent is 121 to 127N. The preparation method is simple and reasonable; the prepared product has the advantages of softness, fine and smooth effect, good appearance and good texture.

Description

technical field [0001] The invention belongs to the field of fiber preparation and relates to a preparation method of polyester porous yarn. Background technique [0002] Since the appearance of polyethylene terephthalate (PET) fiber, it has developed rapidly because of its excellent performance, and its output has become the crown of synthetic fiber in the world. Polyester fiber has a series of excellent properties such as high breaking strength, high elastic modulus, moderate resilience, excellent heat setting performance, good heat resistance and light resistance, acid resistance, alkali resistance and corrosion resistance, and the fabric prepared from it has wrinkle resistance. And crispness and other advantages, so polyester fiber is widely used in clothing and home textiles and other fields. [0003] Due to the small dielectric constant, low moisture regain and high friction coefficient of most PET fibers, spinning oil must be used in the spinning process. The main c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/84D01D5/247D06M13/11D06M13/224D06M15/53D06M13/02D06M13/292D06M13/256D06M101/32
CPCD01D5/247D01F6/84D06M13/02D06M13/11D06M13/224D06M13/256D06M13/292D06M15/53D06M2101/32
Inventor 王山水丁竹君王雪卓怀智魏德新
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap