Gravure pearlescent ink compound for tipping paper and preparation method thereof

A technology for varnish and tipping paper, which is applied in the field of ink and varnish, can solve the problems of affecting the pearlescent effect of printed products, easy precipitation, layering and agglomeration, increasing production costs, etc., and achieves easy control and large-scale production. , It is not easy to delaminate and precipitate, and the effect of increasing production costs

Active Publication Date: 2018-07-10
玉溪接装纸制造有限公司
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

One is that the wetting and dispersing performance of the pigment is poor, and it is easy to precipitate, stratify and agglomerate after adding the pearlescent pigment. This will not only cause serious color difference in the printed product during the production process, resulting in the scrap of the printed product, but also make it difficul...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The specific formula of this embodiment is calculated in parts by weight: 15 parts of polyvinyl butyral resin, 6 parts of cellulose acetate butyrate, 3 parts of aldehyde and ketone resin, 3 parts of rosin glyceride, 1 part of polyethylene wax, 35 parts of ethanol Parts, 35 parts of ethyl acetate, 2 parts of n-propyl acetate.

[0033] Follow the steps below for production:

[0034] a. Add ethanol, ethyl acetate, and n-propyl acetate weighed according to the proportion into the container and stir at room temperature for 3 to 5 minutes at a stirring speed of 500-700r / min to obtain a mixed solution A;

[0035] b. Add polyvinyl butyral resin, aldehyde and ketone resin, rosin glyceride, and cellulose acetate butyrate weighed according to the ratio to the mixed solution A in sequence, and stir at room temperature for 2 to 4 hours at a stirring speed of 800-1000r / min until completely dissolved to obtain mixed solution B;

[0036]c. Add polyethylene wax weighed according to t...

Embodiment 2

[0043] The specific formula of this embodiment is calculated in parts by weight: 13 parts of polyvinyl butyral resin, 8 parts of cellulose acetate butyrate, 4 parts of aldehyde and ketone resin, 4 parts of rosin glyceride, 2 parts of polyethylene wax, 33 parts of ethanol Parts, 33 parts of ethyl acetate, 3 parts of n-propyl acetate.

[0044] Follow the steps below for production:

[0045] a. Add ethanol, ethyl acetate, and n-propyl acetate weighed according to the proportion into the container and stir at room temperature for 3 to 5 minutes at a stirring speed of 500-700r / min to obtain a mixed solution A;

[0046] b. Add polyvinyl butyral resin, aldehyde and ketone resin, rosin glyceride, and cellulose acetate butyrate weighed according to the ratio to the mixed solution A in sequence, and stir at room temperature for 2 to 4 hours at a stirring speed of 800-1000r / min until completely dissolved to obtain mixed solution B;

[0047] c. Add polyethylene wax weighed according to...

Embodiment 3

[0054] The specific formula of this embodiment is calculated in parts by weight: 10 parts of polyvinyl butyral resin, 10 parts of cellulose acetate butyrate, 5 parts of aldehyde and ketone resin, 5 parts of rosin glyceride, 3 parts of polyethylene wax, 31.5 parts of ethanol Parts, 31.5 parts of ethyl acetate, 4 parts of n-propyl acetate.

[0055] Follow the steps below for production:

[0056] a. Add ethanol, ethyl acetate, and n-propyl acetate weighed according to the proportion into the container and stir at room temperature for 3 to 5 minutes at a stirring speed of 500-700r / min to obtain a mixed solution A;

[0057] b. Add polyvinyl butyral resin, aldehyde and ketone resin, rosin glyceride, and cellulose acetate butyrate weighed according to the ratio to the mixed solution A in sequence, and stir at room temperature for 2 to 4 hours at a stirring speed of 800-1000r / min until completely dissolved to obtain mixed solution B;

[0058] c. Add polyethylene wax weighed accordi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a gravure pearlescent ink compound for tipping paper and a preparation method thereof. The gravure pearlescent ink compound for tipping paper is prepared from the following rawmaterials by weight: 5-25 parts of polyvinyl butyral resin, 5-20 parts of cellulose acetate butyrate, 1-10 parts of aldehyde ketone resin, 1-10 parts of rosin glycerin ester, 1-10 parts of an antisettling agent, and 50-80 parts of a solvent. The gravure pearlescent ink compound provided by the invention adopts reasonable collocation of a variety of non-toxic and transparent resins in the formula,and is synthesized by a blending process. The ink compound has the characteristics of good gloss, excellent pearlescent pigment wet dispersion and directional arrangement properties, strong adhesion,good printing adaptability, fast drying, precipitation prevention, wide application range and the like.

Description

technical field [0001] The present invention relates to ink and varnish, more specifically to a gravure pearlescent varnish for tipping paper and a preparation method thereof. Background technique [0002] In recent years, with the sustained and steady growth of my country's national economy, a wider market space has been provided for the printing and packaging products industry. Among them, pearlescent printing is a special-effect printing product printed with special ink, and its market prospect is widely optimistic by the industry. Through the organic combination of people's personalized design and printing quality, pearlescent printing can rebuild a new color space and light and color effect on the surface of plain and simple paper and other substrates. Using lithographic printing, gravure printing, flexographic printing, letterpress printing, screen printing and other printing processes, in the outer packaging of high-end cosmetics, various cigarette packaging boxes, h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/106C09D11/14C09D11/103C09D11/03C09D11/033
CPCC09D11/03C09D11/033C09D11/103C09D11/106C09D11/14
Inventor 何宗修龚麟杨正德王长寿
Owner 玉溪接装纸制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap