A self-reinforced para-aramid paper using aramid nanofibers and its preparation method

A para-aramid paper and nanofiber technology, which is applied in special paper, fiber dispersant addition, papermaking, etc., can solve the problems of aramid paper comprehensive performance decline, and achieve strong innovation, excellent comprehensive performance and broad application prospects Effect

Active Publication Date: 2020-06-23
SHAANXI UNIV OF SCI & TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a self-reinforced para-aramid paper using aramid nanofibers and its preparation method, so as to overcome the above-mentioned defects in the prior art. The aramid paper avoids the current problem of introducing a third type of thermoplastic bonding fiber or resin impregnation to reduce the comprehensive performance of aramid paper used in the reinforcement of aramid paper. It can be used as a high-end insulation material in the field of electrical insulation or in As a structural weight-reducing material in the aerospace field, it has broad application prospects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A self-reinforced para-aramid paper using aramid nanofibers and its preparation method
  • A self-reinforced para-aramid paper using aramid nanofibers and its preparation method
  • A self-reinforced para-aramid paper using aramid nanofibers and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] A method for preparing a self-reinforced para-aramid paper utilizing aramid nanofibers, comprising the following steps:

[0042] Step 1: Disperse the aramid fiber X, that is, the para-aramid chopped fiber, through a standard fiber deflagging machine for 10,000-30,000 r to obtain a slurry suspension A. During the de-flaking, it is necessary to add a fiber with a molecular weight of 3 to 5 million Polyethylene oxide is used as a dispersant, and the dosage is 0.1-0.5% of the absolute dry mass of the aramid fiber X;

[0043] Step 2: Fibrillating one or both of the aramid fiber Y, that is, the para-aramid fibrid fiber and the para-aramid pulp fiber, and adding it to the slurry suspension obtained in step 1 A, using a standard fiber deflagging machine to decompose and disperse for 10000-20000r to prepare a slurry suspension B. The degree of fibrillation treatment is to detect a beating degree of 45-60°SR, and the aramid fiber in the slurry suspension B is X The mass ratio to...

Embodiment 1

[0048] A self-reinforced para-aramid paper using aramid nanofibers, in parts by weight, the components of the aramid paper include: para-aramid fibers: 99 parts, aramid nanofibers: 1 part, The aramid fiber is a mixed system of aramid fiber X and aramid fiber Y, wherein the weight ratio of aramid fiber X and aramid fiber Y is 3:7, and the aramid fiber X is para-aramid Aramid chopped fiber; the aramid fiber Y is a para-aramid fibril;

[0049] Wherein, the aramid fiber nanofiber is made by the following preparation steps:

[0050] Step (1): 1.0g para-aramid yarn fiber, 1.5g potassium hydroxide (KOH) and 500ml dimethyl sulfoxide (DMSO) are placed in a container, and stirred at a temperature of 30°C under sealed conditions After 8 days, the aramid nanofiber dispersion liquid dispersed in the KOH / DMSO system was obtained;

[0051] Step (2): The aramid nanofiber dispersion liquid dispersed in the KOH / DMSO system obtained in step (1), under the action of stirring at 600rpm, inject d...

Embodiment 2

[0061] A self-reinforced para-aramid paper using aramid nanofibers, in parts by weight, the components of the aramid paper include: para-aramid fibers: 97 parts, aramid nanofibers: 3 parts, The aramid fiber is a mixed system of aramid fiber X and aramid fiber Y, wherein the weight ratio of aramid fiber X and aramid fiber Y is 3.5:6.5, and the aramid fiber X is para-aramid Aramid chopped fiber; the aramid fiber Y is para-aramid pulp fiber;

[0062] Wherein, the aramid fiber nanofiber is made by the following preparation steps:

[0063] Step (1): 1.0g of para-aramid chopped fiber, 1.5g of potassium hydroxide (KOH) and 500ml of dimethyl sulfoxide (DMSO) are placed in a container, and stirred at a temperature of 40°C under sealed conditions After 7 days, the aramid nanofiber dispersion liquid dispersed in the KOH / DMSO system was obtained;

[0064] Step (2): The aramid nanofiber dispersion obtained in step (1) dispersed in the KOH / DMSO system is injected with deionized water at a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PPTA paper using aramid nanofiber for self-reinforcement and a preparation method thereof. The preparation method includes: utilizing para-aramid paper nanofiber with the advantages of special nano-structure, small fiber diameter, large length-diameter ratio, high surface activity, excellent heat resistance and the like as the self-reinforcement material of para-aramid paper, conducting mixing, defibering and dispersion on aramid chopped fiber, pulp or fibrid and aramid nanofiber to make a uniform suspension, carrying out papermaking shaping, squeezing and drying, andfurther performing hot-pressing on a hot press to obtain aramid paper. The introduced aramid nanofiber enables nanoscale aramid fiber and an aramid nanofilm formed thereby to reach the good interfacefilling, coating and enhancement effects, provides more binding sites for the combination of components, at the same time reduces the pores and holes between components, significantly improves the bonding strength between the aramid paper components, and greatly enhances the mechanical and insulation properties.

Description

technical field [0001] The invention belongs to the field of polymer nanomaterials and papermaking, and in particular relates to para-aramid paper self-reinforced by aramid nanofibers and a preparation method thereof. Background technique [0002] Para-aramid fiber (PPTA) is a high-performance synthetic fiber with high strength, high modulus, excellent insulation and high temperature resistance, and is an ideal raw material for protective and reinforcing materials. Para-aramid paper is made of para-aramid chopped fibers and para-aramid pulp fibers or para-aramid fibrids as raw materials through wet papermaking and hot-pressing process. Due to the rigid chain structure formed by the π-π conjugation inside the para-aramid fiber molecular chain, the hydrogen bond between the molecular chains and the van der Waals force, it forms a dense and orderly two-dimensional network structure, although the fiber itself is guaranteed High strength, high modulus, high temperature resistanc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/00D21F11/00D21H21/10D21H21/08
CPCD21F11/00D21H21/08D21H21/10D21H27/00
Inventor 杨斌张美云陆赵情宋顺喜罗晶晶
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com