Method for preparing composite modified p-xylene

A para-xylene and compound modification technology, applied in the direction of one-component copolyester rayon, can solve the problem of single xylene product, achieve good antibacterial effect, improve overall function and quality effect, and improve dispersibility and compatibility effects

Inactive Publication Date: 2018-08-03
ZHEJIANG MODERN TEXTILE IND RES INST
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the product of p-xylene has always been single and almost unchanged
In addition, there is currently no report on how to develop p-xylene with anti-aging function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A preparation method for composite modified p-xylene, comprising the steps of:

[0044] (1) In parts by mass, 1.5 parts of aluminum hexafluorosilicate, 1.5 parts of chromium chlorate phosphate, 30 parts of mass fraction are 5% trifluoroacetic acid aqueous solution, 0.9 parts of nickel oxide, 0.55 parts of calcium phosphate Whiskers were mixed with 9 parts of 2% hexafluorophosphoric acid aqueous solution, ground at 45°C for 2.5h with a high-energy ball mill, and then moved to a reactor lined with polytetrafluoroethylene, heated at 150°C and 0.35MPa The reaction was continuously stirred under pressure for 4 hours, then naturally cooled to normal temperature under stirring, filtered, calcined at 500°C for 3 hours, fully washed with deionized water, dried in vacuum at 75°C, pulverized in a ball mill, and passed through 250-mesh sieve to obtain a special antibacterial modifier.

[0045] (2) In parts by mass, under continuous stirring, 17 parts of p-xylene, 1.5 parts of o-xy...

Embodiment 2

[0049] A preparation method for composite modified p-xylene, comprising the steps of:

[0050] (1) In parts by mass, 1 part of aluminum hexafluorosilicate, 1 part of chromium chlorate phosphate, 50 parts of mass fraction are 5% trifluoroacetic acid aqueous solution, 0.8 part of nickel oxide, 0.5 part of calcium phosphate The whiskers were mixed with 8 parts of 2% hexafluorophosphoric acid aqueous solution, ground at 50°C for 2 hours with a high-energy ball mill, and then moved to a reactor lined with polytetrafluoroethylene, at a temperature of 140°C and a pressure of 0.4MPa The reaction was continuously stirred for 5 hours, then naturally cooled to normal temperature under stirring, filtered, calcined at 480°C for 4 hours, fully washed with deionized water, dried in vacuum at 70°C, pulverized in a ball mill, and subjected to 200 Mesh sieve to prepare a special antibacterial modifier.

[0051] (2) According to the number of parts by mass, under continuous stirring, 15 parts o...

Embodiment 3

[0055] A preparation method for composite modified p-xylene, comprising the steps of:

[0056] (1) In parts by mass, 2 parts of aluminum hexafluorosilicate, 2 parts of chromium chlorate phosphate, 50 parts of mass fraction are 5% trifluoroacetic acid aqueous solution, 1 part of nickel oxide, 0.6 part of calcium phosphate The whiskers were mixed with 10 parts of 2% hexafluorophosphoric acid aqueous solution, ground for 3 hours at 40°C with a high-energy ball mill, and then moved to a reactor lined with polytetrafluoroethylene, heated at a temperature of 160°C and a pressure of 0.3MPa. The reaction was continuously stirred for 3 hours, then naturally cooled to normal temperature under stirring, filtered, calcined at 520°C for 2 hours, fully washed with deionized water, dried in vacuum at 80°C, pulverized in a ball mill, and subjected to 300°C Mesh sieve to prepare a special antibacterial modifier.

[0057] (2) According to the number of parts by mass, under continuous stirring,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing composite modified p-xylene. The method comprises the following steps: 1) mixing aluminium hexafluorosilicate, phosphorus chlorate chromium, nickel oxide, a calcium phosphate whisker and trifluoroacetic acid aqueous solution, and a phosphofluoric acid aqueous solution, grinding a mixture and performing a hydro-thermal reaction, and performing steps of filtering, calcining, washing and drying to prepare a special-purpose antibacterial modifier; 2) mixing p-xylene, o-xylene, an acetamide cosolvent and the special-purpose antibacterial modifier obtained in the step 1), chromium aluminum phosphate, and white carbon black, dispersing the mixture, and filtering the mixture to prepare the composite modified p-xylene mother liquor; and 3) adding thecomposite modified p-xylene mother liquor obtained in the step 2) in p-xylene in a spray form to prepare the composite modified p-xylene. The composite modified p-xylene has excellent antibiosis function.

Description

technical field [0001] The invention belongs to the technical field of xylene variety development, and in particular relates to a preparation method of compound modified p-xylene. Background technique [0002] Dimethylbenzene is a colorless transparent liquid; it is a product in which two hydrogens on the benzene ring are replaced by methyl groups, and there are three isomers of ortho, meta and para. Of the three xylene isomers, para-xylene has the largest commercial market. Para-xylene (para-xylene), which can be abbreviated as "PX", is a derivative of benzene, an important chemical raw material, a colorless liquid, and becomes a flaky or columnar crystal at low temperature, insoluble in water, soluble in ethanol, ether, Benzene, acetone, flammable. [0003] In the prior art, as a chemical raw material, p-xylene is generally prepared mainly by improving processes such as chain transfer, disproportionation reaction, isomerization, and adsorption separation, such as the pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/183C08G63/78C08K7/08C08K3/22C08K3/36C08K3/32D01F1/10D01F6/84
Inventor 李琪凌荣根庞学松范艳苹胡克勤
Owner ZHEJIANG MODERN TEXTILE IND RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com