Surface insulating coating for communication cables and preparation method of surface insulating coating

A technology for telecommunications cables and insulating paints, applied in coatings, fire-retardant coatings, etc., can solve problems such as threats to human life safety, cracking of insulating coatings, easy aging and cracking, etc., achieving good market application prospects, not easy to decompose, and good electrical insulation. and the effect of stability in use

Inactive Publication Date: 2018-08-10
HEFEI FENGTENG ENERGY SAVING TECH CO LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing insulating materials for telecommunication cables have poor mechanical properties and are prone to aging. Within a certain period of use, they are prone to aging, cracking, or even falling off due to external light.
The insulating coating on the surface of the telecommunication cable cracks or falls off, which will cause leakage and short circuit, posing a threat to human life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of surface insulation varnish for telecommunication cables, comprises the following raw materials in parts by weight:

[0031] 30 parts of styrene-butadiene-styrene copolymer, 10 parts of epoxy resin, 10 parts of silicone grease, 5 parts of polyvinyl acetal, 6 parts of silane, 4 parts of phosphoric acid or phosphate, 1 part of surfactant , 1.5 parts of curing agent, 1.6 parts of film-forming agent, 0.4 parts of initiator and 1 part of auxiliary agent;

[0032] The additives include 3 parts of flame retardant, 3 parts of preservative and 4 parts of heat-resistant agent.

[0033] The surfactant is sodium dodecylbenzenesulfonate.

[0034] The curing agent is tetraethylenepentamine.

[0035] The film-forming agent is composed of ethylene glycol, propylene glycol and hexylene glycol in a mass ratio of 1:1:1.

[0036] The initiator is azobisisobutyronitrile.

[0037] The flame retardant is aluminum hydroxide;

[0038] The preservative is 1,2-benzothiazolin-3-one; ...

Embodiment 2

[0046] A kind of surface insulation varnish for telecommunication cables, comprises the following raw materials in parts by weight:

[0047] 40 parts of styrene-butadiene-styrene copolymer, 18 parts of epoxy resin, 15 parts of silicone grease, 12 parts of polyvinyl acetal, 13 parts of silane, 9 parts of phosphoric acid or phosphate, 4 parts of surfactant , 3 parts of curing agent, 2.8 parts of film forming agent, 0.8 parts of initiator and 2 parts of auxiliary agent;

[0048] The additives include 5 parts of flame retardant, 8 parts of preservative and 9 parts of heat-resistant agent.

[0049] The surfactant is fatty alcohol polyoxyethylene ether.

[0050] The curing agent is dihexyltriamine.

[0051] The film forming agent is composed of ethylene glycol butyl ether acetate and dodecyl alcohol ester in a mass ratio of 1:1.

[0052] The initiator is azobisisoheptanonitrile.

[0053] The flame retardant is aluminum hydroxide;

[0054] The preservative is composed of one of ...

Embodiment 3

[0062] A kind of surface insulation varnish for telecommunication cables, comprises the following raw materials in parts by weight:

[0063] 35 parts of styrene-butadiene-styrene copolymer, 15 parts of epoxy resin, 12 parts of silicone grease, 6 parts of polyvinyl acetal, 9 parts of silane, 6 parts of phosphoric acid or phosphate, 3 parts of surfactant , 2.2 parts of curing agent, 2.1 parts of film-forming agent, 0.6 parts of initiator and 1.2 parts of auxiliary agent;

[0064] The additives include 4 parts of flame retardant, 6 parts of preservative and 5 parts of heat-resistant agent.

[0065] The surfactant was fatty acid methyl ester ethoxylate.

[0066] The curing agent is tetraethylenepentamine.

[0067] The film forming agent is composed of diethylene glycol, propylene glycol ethyl ether, ethylene glycol butyl ether and propylene glycol butyl ether in a mass ratio of 1:1:1.

[0068] The initiator is azobisisobutyronitrile.

[0069] The flame retardant is aluminum hy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a surface insulating coating for communication cables, and relates to the technical field of insulating materials. The surface insulating coating comprises the following raw materials of: in parts by weight, 30-40 parts of an acrylonitrile-butadiene-styrene copolymer, 10-18 parts of epoxy resin, 10-15 parts of silicone grease, 5-12 parts of polyvinyl acetal, 6-13 parts of silane, 4-9 parts of phosphoric acid or phosphate, 1-4 parts of a surfactant, 1.5-3 parts of a curing agent, 1.6-2.8 parts of a film forming agent, 0.4-0.8 part of an initiator and 1-2 parts of an assistant. The surface insulating coating for the communication cables has stable chemical properties, strong mechanical resistance, difficult aging and strong cohesive force, and does not fall off easily, and the preparation method is simple and easy to operate, and has a good prospect of market application.

Description

technical field [0001] The invention relates to the technical field of insulating materials, in particular to a surface insulating varnish for telecommunication cables and a preparation method thereof. Background technique [0002] Insulating varnish, also known as insulating coatings, is a coating with excellent electrical insulation. It has good electrochemical properties, thermal properties, mechanical properties and chemical properties. It is mostly varnish and colored paint. Insulating varnish is a kind of special varnish in varnish. Insulating varnish is an important insulating material based on high molecular polymer, which can be cured into an insulating film or an insulating whole under certain conditions. [0003] Telecommunication cables are wire products used to transmit electric energy, information and realize electromagnetic energy conversion. In order to isolate conductor current and protect personal and equipment safety, the outside is usually covered with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D155/02C09D5/25C09D5/18
CPCC09D155/02C08K2003/321C08K2003/329C08L2205/035C09D5/00C09D5/18C08L63/00C08L29/14C08L83/04C08K13/02C08K3/32
Inventor 吴旭
Owner HEFEI FENGTENG ENERGY SAVING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap