Modified automobile engineering plastic and preparation method thereof

An automotive engineering and modification technology, applied in the field of plastic materials, can solve the problems of poor corrosion resistance, poor finish, easy water absorption, etc., and achieve excellent mechanical properties, various varieties, and excellent water resistance.

Inactive Publication Date: 2018-10-16
WUHU CHUANGKE NEW MATERIAL TECH CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nylon is mainly used in automobile engines and engine peripheral parts. However, nylon also has some disadvantages, such as high cost, poor corrosion resistance, poor rigidity, easy water absorption, poor paintability, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The modified automotive engineering plastics in this embodiment are made from the following raw materials in parts by weight: 40 parts of modified nylon, 50 parts of PVC resin, 5 parts of ceramic powder, 10 parts of polytetrafluoroethylene micropowder, 5 parts of carbon black, hexamethylphosphoric acid 1 part of triamine, 2 parts of antioxidant, 1 part of compatibilizer, 1 part of toughening agent, 1 part of lubricant, 1 part of aluminate coupling agent, 1 part of dispersant;

[0028] Among them, the modified nylon is glass fiber modified; the particle size of ceramic powder is 60nm; Homopolymer of lipid monomer and styrene monomer; nylon is nylon 6; antioxidant is hindered phenol compound; lubricant is silicone oil; compatibilizer is styrene grafted maleic anhydride;

[0029] The preparation method of the present embodiment modified automotive engineering plastics comprises the following steps:

[0030] S1. Weighing each raw material according to parts by weight;

[...

Embodiment 2

[0034] The modified automotive engineering plastics in this embodiment are made of the following raw materials in parts by weight: 65 parts of modified nylon, 85 parts of PVC resin, 9 parts of ceramic powder, 15 parts of polytetrafluoroethylene micropowder, 12 parts of carbon black, hexamethylphosphoric acid 4 parts of triamine, 6 parts of antioxidant, 3 parts of compatibilizer, 2 parts of toughening agent, 3 parts of lubricant, 2.5 parts of aluminate coupling agent, 2.5 parts of dispersant;

[0035] Among them, the modified nylon is modified by glass fiber; the particle size of the ceramic powder is 120nm; Homopolymer of lipid monomer and styrene monomer; nylon is nylon 66; antioxidant is phosphite compound; lubricant is stearate; compatibilizer is styrene grafted maleic anhydride;

[0036] The preparation method of the present embodiment modified automotive engineering plastics comprises the following steps:

[0037] S1. Weighing each raw material according to parts by weig...

Embodiment 3

[0041] The modified automotive engineering plastics in this embodiment are made of the following raw materials in parts by weight: 52 parts of modified nylon, 67 parts of PVC resin, 7 parts of ceramic powder, 13 parts of polytetrafluoroethylene micropowder, 9 parts of carbon black, hexamethylphosphoric acid 2.5 parts of triamine, 4 parts of antioxidant, 2 parts of compatibilizer, 1.5 parts of toughening agent, 2 parts of lubricant, 1.7 parts of aluminate coupling agent, 1.7 parts of dispersant;

[0042]Among them, the modified nylon is modified by glass fiber; the particle size of the ceramic powder is 90nm; Homopolymer of lipid monomer and styrene monomer; Nylon is mixed with Nylon 6, Nylon 12, Nylon 66, and Nylon 610 according to the mass ratio of 1:1:1; Antioxidant is hindered phenolic compound, phosphite The compound is mixed according to the mass ratio of 1:1:1; the lubricant is white mineral oil, fatty acid amide, paraffin, and ethylene bisstearamide mixed according to t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides modified automobile engineering plastic and a preparation method thereof, and relates to the technical field of plastic materials. The modified automobile engineering plastic isprepared from the following raw materials: modified nylon, PVC resin, ceramic powder, polytetrafluoroethylene micro powder, carbon black, hexamethylphosphoramide, an antioxidant, a compatilizer, a flexibilizer, a lubricant, an aluminate coupling agent and a dispersant. The modified automobile engineering plastic has high impact property and abrasion resistance, not only has excellent mechanical properties, but also improves the weather fastness and heat resistance of the materials, and has excellent water resistance and steam resistance, a product has high tensile strength and impact strength, and further has the advantage that the product is not shrunk and not embrittled in low temperature environment.

Description

technical field [0001] The invention relates to the technical field of plastic materials, in particular to a modified automotive engineering plastic and a preparation method thereof. Background technique [0002] The automobile industry is one of the important basic industries in the national economy. The development of the automobile industry will drive the development of metallurgy, petrochemicals, light industry, textiles, electronic appliances, machinery, building materials and road construction. The development level of the automobile industry is a measure of a country's One of the important symbols of economic strength. Replacing steel with plastic, energy saving and emission reduction, green environmental protection, and automobile lightweight are the top priorities in the automotive industry. At present, a large number of plastics have been used to replace various non-ferrous metals and alloy steels. [0003] With the rise of automobile lightweight, the use of autom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L77/02C08L77/06C08L27/18C08K13/02C08K3/04C08K3/34
CPCC08L27/06C08L2201/08C08L2205/02C08L2205/035C08L77/02C08L27/18C08K13/02C08K3/04C08K3/34C08L77/06
Inventor 汪淼黄小军魏传刚王俊
Owner WUHU CHUANGKE NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More