Preparation method of wear-resisting ceramic tile capable of releasing negative ion

A technology of ceramic bricks and negative ions, which is applied in the field of preparation of wear-resistant ceramic bricks, can solve problems such as inability to purify air, not conform to the development direction, and poor heat insulation effect, so as to improve human immunity, reduce red blood cell aggregation, eliminate The effect of odor

Active Publication Date: 2018-11-13
广西亚欧瓷业有限公司
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current interior wall brick products still have many shortcomings such as poor heat insulation effect, high water absorption, low strength, easy cracking, etc., and have no environmental protection characteristics, have adverse effects on the human body, and cannot achieve air purification. Completely inconsistent with the development direction of modern wall materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of wear-resisting ceramic tile capable of releasing negative ion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The preparation method of the wear-resistant ceramic tile capable of releasing negative ions of the present invention comprises the following steps:

[0033] Take 600kg of potassium feldspar, 1000kg of albite feldspar, 1000kg of kaolin, 1000kg of washed mud, 200kg of barium carbonate, 300kg of burnt talc, 300kg of nano-zinc oxide, 10kg of methyl cellulose, 5kg of sodium tripolyphosphate, 5kg of sodium sorbate, and negative ion powder 150kg, glaze 2000kg;

[0034]Mix the above-mentioned powders except negative ion powder and glaze, add a methylcellulose solution with a mass fraction of 0.2%, add water to make the water content of the mixed material 18%, grind for 3 hours with a ball mill, and control the speed of the ball mill 15rpm to obtain a slurry; the slurry is deironed, passed through a 200-mesh sieve, and stale for 5 hours to obtain a specific gravity of 1.60g / cm 3 , mud with a water content of 30%; the mud is sent to a spray dryer to dry and pressed to obtain a ...

Embodiment 2

[0041] The preparation method of the wear-resistant ceramic tile capable of releasing negative ions of the present invention comprises the following steps:

[0042] Take 1600kg of potassium feldspar, 2000kg of albite feldspar, 300kg of nepheline, 1700kg of kaolin, 1800kg of washed mud, 700kg of barium carbonate, 650kg of burnt talc, 700kg of nano-zinc oxide, 30kg of methylcellulose, 15kg of sodium tripolyphosphate, and 20kg of sodium benzoate , negative ion powder 250kg, glaze 2750kg;

[0043] With above-mentioned powder except negative ion powder and glaze, after mixing, add the methyl cellulose solution that mass fraction is 0.28%, add water again to make the water content of mixed material be 19%, use ball mill to grind 3.8h, ball mill speed is 17rpm, get the slurry, remove the iron from the slurry, pass through a 220 mesh sieve, stale for 6h, and get a specific gravity of 1.63g / cm 3 , a slurry with a water content of 31%; the slurry is sent to a spray dryer to dry and pre...

Embodiment 3

[0050] The preparation method of the wear-resistant ceramic tile capable of releasing negative ions of the present invention comprises the following steps:

[0051] Take 950kg of potassium feldspar, 1350kg of albite feldspar, 50kg of nepheline, 1500kg of kaolin, 1600kg of washed mud, 400kg of barium carbonate, 450kg of burnt talc, 500kg of nano-zinc oxide, 20kg of methylcellulose, 11kg of sodium tripolyphosphate, fumaric acid Dimethyl ester 12kg, negative ion powder 190kg, glaze 2250kg;

[0052] With above-mentioned powder material except negative ion powder and glaze, after mixing, add the methyl cellulose solution that mass fraction is 0.36%, add water again to make the water content of mixed material be 20%, use ball mill to grind 4.6h, and ball mill speed is 18rpm, get the slurry, remove the iron from the slurry, pass through a 240 mesh sieve, stale for 7h, and get a specific gravity of 1.64g / cm 3 , a slurry with a water content of 32%; the slurry is sent to a spray dryer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
quality scoreaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a wear-resisting ceramic tile capable of releasing a negative ion. A finished product of the ceramic tile is obtained by ball-milling a powder material,pulping, spraying a powder, forming, biscuiting, glazing, glaze-firing and edging; a used glaze comprises a negative ion powder; the powder material comprises potassium feldspar, albite, nepheline, kaolin, washing mud, barium carbonate, calcined talcum, nano-zinc oxide, methylcellulose, sodium tripolyphosphate, a preservative. The preparation method adopts the low-temperature biscuiting and high-temperature glaze-firing process; the ceramic tile produces a large quantity of negative ions, the glaze is flat and smooth, the resistance to thermal shock and the stain resistance are good, and thepreparation method has excellent performances of wear resistance and acid corrosion resistance, and has excellent economic and social benefits.

Description

technical field [0001] The invention relates to the technical field of ceramic production, in particular to a preparation method of a wear-resistant ceramic brick capable of releasing negative ions. Background technique [0002] Negative air ions can promote the synthesis and storage of vitamins in the human body, strengthen and activate the physiological activities of the human body, so it is called "air vitamin". Like the vitamins in food, it has a very important impact on the life activities of the human body and other organisms. For example, after a thunderstorm, the negative ions in the air increase, and people feel comfortable. In the air-conditioned room, because the negative ions in the air almost disappear after a series of air-conditioning purification treatments and long ventilation ducts, people will feel chest tightness, dizziness, fatigue, and decline in work efficiency and health when they stay in it for a long time. syndrome". In the medical field, negative...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/04C03C8/00C04B33/34
CPCC03C8/00C04B33/04C04B33/13C04B33/34C04B2235/3206C04B2235/3215C04B2235/3232C04B2235/3284C04B2235/3445C04B2235/3472C04B2235/447C04B2235/96
Inventor 黄珠祥
Owner 广西亚欧瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap