Environment-friendly anti-oxidation cable protective sleeve material

A cable protection and anti-oxidation technology, applied in the direction of rubber insulators, organic insulators, etc., can solve the problems of casualties, precision instruments, damage, etc., achieve good heat resistance, improve cross-linking degree, tensile degree and tear resistance excellent effect

Inactive Publication Date: 2018-11-16
安徽电信器材贸易工业有限责任公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because PVC cable materials contain harmful heavy metals such as lead, tin, and barium, and PVC will produce toxic and corrosive gases such as hydrogen chloride and violent smoke during the combustion process, it is easy to cause a large number of casualties and precision instruments in a fire. damage to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] An environment-friendly anti-oxidation cable protective sheath material. The raw materials of the protective sheath material include by weight: 23 parts of ethylene-propylene rubber, 15 parts of butyl rubber, 12 parts of epoxy resin, 7 parts of silicone resin, and 7 parts of aluminum hydroxide colloid 8 parts of glass fiber, 0.9 part of paraffin oil, 3 parts of talcum powder, 4 parts of diatomaceous earth, 1.2 parts of zinc stearate, 1.3 parts of vulcanizing agent DCP, 4 parts of silane coupling agent, 2 parts of auxiliary crosslinking agent TAIC. 6 parts, 4 parts of ultraviolet absorber UV-O, 10763 parts of polyphenol antioxidant;

[0017] The preparation process of the environment-friendly anti-oxidation cable protective sheath material is as follows: add ethylene-propylene rubber, butyl rubber, epoxy resin, and silicone resin into a screw extruder and melt for 10 minutes at a melting temperature of 125°C, then add the remaining raw materials and melt After 20 minutes...

Embodiment 2

[0019] An environment-friendly anti-oxidation cable protective sheath material. The raw materials of the protective sheath material include by weight: 26 parts of ethylene-propylene rubber, 15 parts of butyl rubber, 12 parts of epoxy resin, 6.7 parts of silicone resin, and 5 parts of aluminum hydroxide colloid 11 parts of glass fiber, 1.2 parts of paraffin oil, 3 parts of talcum powder, 6 parts of diatomaceous earth, 1.2 parts of zinc stearate, 0.9 parts of vulcanizing agent DCP, 4 parts of silane coupling agent, 2 parts of auxiliary crosslinking agent TAIC , 4 parts of ultraviolet absorber UV-O, 10762 parts of polyphenol antioxidant;

[0020] The preparation process of the environmentally friendly anti-oxidation cable protective sheath material is as follows: add ethylene-propylene rubber, butyl rubber, epoxy resin, and silicone resin to a screw extruder and melt for 20 minutes at a melting temperature of 135°C, then add the remaining raw materials and melt After 20 minutes, ...

Embodiment 3

[0022] An environment-friendly anti-oxidation cable protective sheath material. The raw materials of the protective sheath material include by weight: 25 parts of ethylene-propylene rubber, 14 parts of butyl rubber, 13 parts of epoxy resin, 6 parts of silicone resin, and 6 parts of aluminum hydroxide colloid 11 parts of glass fiber, 1 part of paraffin oil, 2.5 parts of talcum powder, 6 parts of diatomaceous earth, 2 parts of zinc stearate, 1 part of vulcanizing agent DCP, 3 parts of silane coupling agent, 3.5 parts of auxiliary crosslinking agent TAIC , 3.5 parts of ultraviolet absorber UV-O, 10762.5 parts of polyphenol antioxidant;

[0023] The preparation process of the environmentally friendly anti-oxidation cable protective sheath material is as follows: add ethylene-propylene rubber, butyl rubber, epoxy resin, and silicone resin to a screw extruder and melt for 15 minutes at a melting temperature of 130 ° C, then add the remaining raw materials and melt After 20 minutes, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly anti-oxidation cable protective sleeve material. The material comprises the following raw materials in parts by weight: 30-40 parts of ethylene-propylene rubber, 10-16 parts of butyl rubber, 10-15 parts of epoxy resin, 4-10 parts of organic silicon resin, 4-8 parts of an aluminum hydroxide colloid, 5-12 parts of glass fibers, 0.7-1.3 parts of paraffin oil and 1-5 parts of talcum powder, 4-9 parts of diatomite, 0.5-3 parts of zinc stearate, 0.6-1.5 parts of a vulcanizing agent DPC, 2-5 parts of a coupling agent, 1-4 parts of an assistant crosslinker TAIC, 1-4 parts of an anti-aging agent and 1.5-4 parts of an antioxidant. The preparation process of the protective sleeve material is as follows: adding the ethylene propylene-rubber, the butyl rubber, the epoxy resin and the organic silicon resin into a screw extruder, carrying out fusion for 10-20 minutes, controlling the melting temperature to be 125-135 DEG C, and then adding the remainingraw materials, carrying out extrusion after the fusion is carried out for 20 minutes, placing the extruded material in a flat vulcanizing machine, and carrying out pressing and crushing to obtain theenvironment-friendly anti-oxidation cable protective sleeve material. The protective sleeve material has excellent oxidation resistance, and the service life is prolonged.

Description

technical field [0001] The invention belongs to the field of cables, and in particular relates to an environment-friendly anti-oxidation cable protective sheath material. Background technique [0002] With the rapid development of my country's communication industry, the demand for communication cables as arteries and blood vessels for signal transmission is also increasing day by day. The heat resistance of cable rubber sheaths on the market is generally poor. Using them at high temperatures can easily lead to problems such as premature aging, cracking and stickiness on the surface, and the surface will fall off for a long time, resulting in loss of function, and the cable will be discarded. Moreover, with the strengthening of people's awareness of environmental protection and the introduction of environmental protection regulations, halogen-free flame-retardant technology will gradually replace halogen-free flame-retardant technology. For a long time, the amount of polyvi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/22C08L63/00C08L83/04C08K13/04C08K7/14C08K3/22C08K5/14C08K3/34H01B3/28
CPCC08K2003/2227C08L23/16C08L2201/02C08L2201/08C08L2203/202C08L2205/035C08L2312/00H01B3/28C08L23/22C08L63/00C08L83/04C08K13/04C08K7/14C08K3/22C08K5/14C08K3/34
Inventor 李涛王军李竞竞
Owner 安徽电信器材贸易工业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap