Modified nylon composition and preparation method thereof

A technology of modified nylon and composition, applied in the field of modified nylon composition and its preparation, can solve the problems of nylon smell, poor wear resistance, etc., and achieve the effects of TVOC reduction, good wear resistance, and smooth melting and mixing

Inactive Publication Date: 2018-12-04
HEFEI GENIUS NEW MATERIALS
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art, the present invention provides a modified nylon composition and its preparation method, which solves the technical problems of high nylon odor and poor abrasion resistance in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified nylon composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] Preparation of odor adsorption masterbatch: 100 parts of nylon, 5 parts of hydrophobic diatomaceous earth, 10 parts of hydrophobic activated carbon, 5 parts of acicular zeolite molecular sieve, 10 parts of zinc ricinoleate, 5 parts of nano-silica, 1 part of stearin Calcium acid, 5 parts of melamine, mixed evenly, and then extruded and granulated in a twin-screw extruder to obtain odor absorption masterbatch.

[0028] The number average molecular weight of polytetrafluoroethylene is 1.2 million, and the crystallinity is 90%.

[0029] Nylon 6 melt index is 5-8g / 10min;

[0030] The melt index of nylon 66 is 8-10g / 10min.

Embodiment 1

[0032] The modified nylon composition of this embodiment is made of the following raw materials in parts by weight: 70 parts of nylon 6, 1 part of nylon 66, 1 part of POE grafted maleic anhydride, 25 parts of polytetrafluoroethylene modified glass fiber, 3 parts of odor Adsorption masterbatch, 0.2 parts of silicon carbide, 1 part of silicone powder, 0.2 parts of antioxidant 1098, 0.2 parts of antioxidant 168;

[0033] The preparation method of the present embodiment modified nylon composition comprises the following steps:

[0034] S1. Wash and dry the glass fiber and then immerse it in the polytetrafluoroethylene dispersion, take it out and dry it, bake and sinter at 300°C to obtain the polytetrafluoroethylene modified glass fiber;

[0035] S2. Weigh each raw material in parts by weight, pour nylon 6, nylon 66, POE grafted maleic anhydride, odor absorption masterbatch, silicon carbide, lubricant and antioxidant into the mixer, stir evenly and place in the twin-screw In the e...

Embodiment 2

[0038] The modified nylon composition of this embodiment is made of the following raw materials in parts by weight: 54 parts of nylon 6, 5 parts of nylon 66, 5 parts of POE grafted maleic anhydride, 30 parts of polytetrafluoroethylene modified glass fiber, 1 part of odor Adsorption masterbatch, 0.2 part of silicon carbide, 0.2 part of silicone powder, 0.1 part of antioxidant 1098, 0.1 part of antioxidant 168;

[0039] The preparation method of the present embodiment modified nylon composition comprises the following steps:

[0040] S1. Wash and dry the glass fiber and then immerse it in the polytetrafluoroethylene dispersion, take it out and dry it, bake and sinter at 300°C to obtain the polytetrafluoroethylene modified glass fiber;

[0041] S2. Weigh each raw material in parts by weight, pour nylon 6, nylon 66, POE grafted maleic anhydride, odor absorption masterbatch, silicon carbide, lubricant and antioxidant into the mixer, stir evenly and place in the twin-screw In the e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a modified nylon composition and a preparation method thereof, and relates to the technical field of macromolecular materials. The modified nylon composition is prepared from the following raw materials: nylon 6, nylon 66, POE grafted maleic anhydride, polytetrafluoroethylene modified glass fibers, an odor adsorption masterbatch, silicon carbide, a lubricant and an antioxidant. The modified nylon composition has the characteristics of low odor and good wear resistance. The nylon composition prepared by coordinating action of the raw materials has remarkable improvement in wear resistance and keeps excellent mechanical properties, and the forming and processing properties of the material are not affected.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a modified nylon composition and a preparation method thereof. Background technique [0002] Nylon was developed by an outstanding scientist in the United States, Carothers, and a research team under his leadership. It is the first synthetic fiber to appear in the world. Nylon is a term for polyamide fiber (nylon), which is generally divided into nylon 6 and nylon 66. The appearance of nylon 6 is milky white to light yellow, with toughness, shock resistance, high mechanical strength and heat resistance, good impact strength, high melting point, good molding and processing performance, high water absorption, and saturated water absorption at 11 %, it is easily soluble in sulfuric acid phenols or formic acid, and the low-temperature embrittlement temperature is minus 20 degrees -30 degrees. [0003] Although nylon has many excellent properties, its application will be g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L77/06C08L51/06C08L83/04C08K13/06C08K9/04C08K7/14C08K3/34C08K3/04C08J3/22B29C47/92B29C48/92
CPCC08J3/226C08J2377/02C08J2477/02C08K2201/011C08K2201/014C08L77/02C08L2205/02C08L2205/025C08L2205/035C08L77/06C08L51/06C08L83/04C08K13/06C08K9/08C08K7/14C08K3/34C08K3/04
Inventor 杨桂生吴安琪范继贤
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com