Process for producing foamed ceramic through layered material preparation and allocation and foamed ceramic material

A technology of foamed ceramics and ceramic raw materials, which is applied in the field of materials, can solve the problems of long cycle times of foamed ceramics, and achieve the effects of shortening the production cycle, accelerating the heating rate, and reducing time

Active Publication Date: 2018-12-21
GUANGDONG KITO CERAMICS GROUP CO LTD +2
View PDF12 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the production cycle of foamed ceramics using a roller kiln is longer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for producing foamed ceramic through layered material preparation and allocation and foamed ceramic material
  • Process for producing foamed ceramic through layered material preparation and allocation and foamed ceramic material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] The present embodiment provides a kind of process for producing foamed ceramics from layered material cloth, which includes:

[0049] S1. Configure ceramic raw materials.

[0050] Wherein, in parts by weight, the ceramic raw materials include:

[0051] 60 parts of polishing slag, 20 parts of press mud, 5 parts of waste glass, 6 parts of potassium feldspar, 4 parts of talc, 5 parts of medium temperature sand, 0.2 part of silicon carbide, and 0.1 part of sodium carboxymethyl cellulose.

[0052] S2. Preparation of pellets

[0053] Take the above-mentioned ceramic raw materials, mix with 0.4 wt% ferric oxide, ball mill, spray granulate, and then roll-granulate to make the first granular material with a particle size of -60~+80 mesh; take the above-mentioned ceramic raw materials, mix with Add 0.3 wt% ferroferric oxide to make the second granular material with a particle size of -40~+60 mesh; take the above-mentioned ceramic raw material, add 0.2 wt% ferric oxide to make a...

Embodiment 2

[0063] The present embodiment provides a kind of process for producing foamed ceramics from layered material cloth, which includes:

[0064] S1. Configure ceramic raw materials.

[0065] Wherein, in parts by weight, the ceramic raw materials include:

[0066] 30 parts of polishing slag, 40 parts of press mud, 5 parts of waste glass, 9 parts of potassium feldspar, 6 parts of talc, 15 parts of medium temperature sand, 0.4 part of silicon carbide, and 0.1 part of sodium carboxymethyl cellulose.

[0067] S2. Preparation of pellets

[0068] Take the above-mentioned ceramic raw materials, mix with 0.4 wt% ferric oxide, ball mill, spray granulate, and then roll-granulate to make the first granular material with a particle size of -60~+80 mesh; take the above-mentioned ceramic raw materials, mix with Add 0.3 wt% ferroferric oxide to make the second granular material with a particle size of -40~+60 mesh; take the above-mentioned ceramic raw material, add 0.2 wt% ferric oxide to make ...

Embodiment 3

[0078] The present embodiment provides a kind of process for producing foamed ceramics from layered material cloth, which includes:

[0079] S1. Configure ceramic raw materials.

[0080] Wherein, in parts by weight, the ceramic raw materials include:

[0081] 35 parts of polishing slag, 20 parts of pressing mud, 15 parts of waste glass, 12 parts of potassium feldspar, 9 parts of talc, 11 parts of medium temperature sand, 0.3 part of silicon carbide, and 0.1 part of sodium carboxymethyl cellulose.

[0082] S2. Preparation of pellets

[0083] Take the above-mentioned ceramic raw materials, mix with 0.4 wt% manganese dioxide, ball mill, spray granulate, and then roll-granulate to make the first granular material with a particle size of -60~+80 mesh; take the above-mentioned ceramic raw materials, mix with 0.3 wt% manganese dioxide to make the second particle size of -40~+60 mesh; take the above-mentioned ceramic raw materials, mix 0.2 wt% manganese dioxide to make the third par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a process for producing foamed ceramic through layered material preparation and allocation and belongs to the field of materials. According to the process, multiple foamed ceramic granule materials of different oxidant contents and granularities are adopted to produce a foamed ceramic material through layered material preparation and allocation. Due to the adoption of oxidants, a foaming agent in a ceramic raw material can be promoted to be oxidized to generate gases; due to the adoption of a setup mode of small lower-layer granule particle sizes, high oxidant contents,large upper-layer granule particle sizes and low oxidant contents, channels are provided for low-temperature gas exhaust, and the low-temperature gas exhaust time can be shortened; moreover, the setup mode is beneficial to heat conduction, uneven foams caused by temperature gradients can be made up, the heating velocity in a foaming combustion period can be increased, the foaming temperature keeping time is shortened, and furthermore the production period of the whole foamed ceramic material can be shortened; the foamed ceramic material is prepared from the foamed ceramic produced through layered material preparation and allocation, and is high in quality, small in defect, short in production period and applicable to on-scale production.

Description

technical field [0001] The invention relates to the field of materials, in particular to a process for producing foamed ceramics from layered material cloth and foamed ceramic materials. Background technique [0002] At present, foamed ceramics usually use solid waste such as tailings, polishing slag, and pressed mud as the main raw materials, add feldspar, waste glass, talc, etc. as auxiliary raw materials, add oxidants, mix in proportion, and then ball mill and spray granulate Prepare spherical pellets with a diameter of 40-60 mesh. Then the granular material is distributed into the grinding tool through the distributor, foamed and fired at high temperature, and the foamed ceramic material is obtained after cooling. [0003] Foamed ceramics are used as lightweight wall materials, and the product thickness requirements are generally 100~300 mm. In order to prepare foamed ceramic wall materials with this thickness, the cloth thickness of 40-60 mesh spherical particles is 5...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B33/132C04B33/13B28B13/02
CPCB28B13/02C04B33/13C04B33/132C04B38/02C04B2235/3262C04B2235/3272C04B2235/3472C04B2235/3826C04B2235/6562C04B2235/6565Y02P40/60
Inventor 赵威戴永刚马梦兰江期鸣
Owner GUANGDONG KITO CERAMICS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap