A kind of method that utilizes asbestos tailings to prepare porous silica

A technology of porous silica and asbestos tailings, which is applied in the directions of silica, silica, chemical instruments and methods, etc., can solve the problem of easily corroded containers by acid solutions, easily corroded containers by alkaline solutions, low magnesia leaching rate, etc. problems, to achieve the effect of easy promotion and application, low equipment requirements and low cost

Active Publication Date: 2022-04-05
SHAANXI SCI TECH UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of the above disclosed acid leaching method are: insufficient acid treatment, low leaching rate of magnesium oxide, easy to cause secondary pollution during the treatment process; and acid solution is easy to corrode the container, which requires high equipment and high cost
[0004] The Chinese patent No. 105502426B "Method for preparing water glass by extracting silicon oxide from chrysotile tailings by strong alkali roasting method" discloses a method of leaching with strong alkali as a chemical auxiliary agent; the strong alkali roasting method The disadvantage is that the lye is easy to corrode the container, which is highly corrosive and requires high equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method that utilizes asbestos tailings to prepare porous silica
  • A kind of method that utilizes asbestos tailings to prepare porous silica
  • A kind of method that utilizes asbestos tailings to prepare porous silica

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A method for preparing porous silicon dioxide from asbestos tailings, comprising the steps of:

[0045] (1) Ball milling. Take an asbestos tailings in southern Shaanxi, crush them in a ball mill with a rotating speed of 220r / min, and mill them for 8 hours to obtain tailings powder with a particle size of 4.0um to 534.9um; among them, the asbestos tailings include magnesium oxide 40%~42%, silicon dioxide 43%~45%, iron oxide 3%~5%, nickel oxide 0.45%~0.55%;

[0046] (2) Mixing, filtering the above tailings powder with a 400-mesh sieve, and then mixing it with ammonium bisulfate evenly to prepare a powder mixture with a mass ratio of tailings powder and ammonium bisulfate of 1:2.93;

[0047] (3) Roasting, the above powder mixture is moved into a corundum crucible, and then reacted in a box-type resistance furnace at a temperature of 500 ° C for 2.5 hours to obtain powder clinker;

[0048] (4) Dissolution, dissolve the above powder clinker with deionized water to obtain a ...

Embodiment 2

[0052] A method for preparing porous silicon dioxide from asbestos tailings, comprising the steps of:

[0053] (1) Ball milling, pulverize the asbestos tailings in a ball mill with a rotational speed of 240r / min, and ball mill for 7.5 hours to obtain tailings powder with a particle size of 4.0um to 534.9um;

[0054] (2) Mixing, the above tailings powder is filtered through a stainless steel metal screen with a pore size of 0.0374mm, and then mixed with ammonium bisulfate to obtain a powder mixture with a mass ratio of tailings powder and ammonium bisulfate of 1:3.1;

[0055] (3) Roasting, move the above powder mixture into a corundum crucible, and then react in a box-type resistance furnace at a temperature of 530°C for 2.3 hours to obtain powder clinker;

[0056] (4) Dissolution, dissolving the above powder clinker with deionized water 5.5 times the mass of powder clinker to obtain a clinker turbid liquid; Alkaline clinker turbid liquid;

[0057] (5) Separation, using a Buc...

Embodiment 3

[0060] A method for preparing porous silicon dioxide from asbestos tailings, comprising the steps of:

[0061] (1) Ball milling, pulverize the cotton tailings in a ball mill with a rotating speed of 210r / min, and ball mill for 8.5 hours to obtain tailings powder with a particle size of 4.0um to 534.9um;

[0062] (2) Mixing, filter the above tailings powder with a sieve with a pore size less than 0.0374mm, and then mix it evenly with ammonium bisulfate to prepare a powder mixture with a mass ratio of tailings powder and activator ammonium bisulfate of 1:3.3 ;

[0063] (3) Roasting, move the above powder mixture into a corundum crucible, and then react in a box-type resistance furnace at a temperature of 470°C for 3 hours to obtain powder clinker;

[0064] (4) Dissolution, dissolving the above powder clinker with deionized water with 6 times the mass of powder clinker to obtain a clinker turbid liquid; Alkaline clinker turbid liquid;

[0065] (5) Separation, using a Buchner f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of resource utilization of tailings, in particular to a method for preparing porous silica from asbestos tailings, comprising the following steps: (1) ball milling, crushing and ball milling the asbestos tailings to obtain tailings powder; 2) Mixing, the tailings powder is filtered and mixed with an activator to obtain a powder mixture; (3) Roasting, the powder mixture is put into a box-type resistance furnace to react to obtain a powder clinker; (4) Dissolution , dissolving the powdered clinker with water to obtain a clinker turbid liquid, and then adjusting the clinker turbid liquid to alkaline to obtain an alkaline clinker turbid liquid; (5) separation, filtering the alkaline clinker turbid liquid, Separation; (6) drying, drying the solid product remaining after filtration, namely porous silica. The auxiliary ammonium bisulfate used in the invention has little corrosion to equipment, little pollution and low cost, not only realizes resource utilization of asbestos tailings, but also does not cause secondary pollution, meets green production requirements, and is suitable for industrial production.

Description

technical field [0001] The invention relates to the field of resource utilization of tailings, in particular to a method for preparing porous silicon dioxide from asbestos tailings. Background technique [0002] Asbestos tailings are mineral residues produced in asbestos mining and selection. The main component is serpentine, and it also contains a small amount of talc, dolomite and calcite. The chemical composition of asbestos tailings is mainly SiO 2 , MgO and a small amount of iron, aluminum, calcium and other substances. According to statistics, tens of millions of tons of asbestos tailings are produced in my country every year. These huge asbestos tailings not only occupy a large amount of land resources, but also pollute the environment. [0003] The Chinese patent "Method for Comprehensive Utilization of Asbestos Tailings" with the announcement number 101792184A discloses a direct acid leaching method for resource utilization. The Chinese patent No. 102352435A "A h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B33/12B01J20/10B01J20/28B01J20/30C02F1/28C02F101/30
CPCB01J20/103C01B33/12C02F1/281B01J20/28054C01P2004/03C01P2002/72C02F2101/308
Inventor 罗清威
Owner SHAANXI SCI TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap