Preparation method of antibacterial anti-wrinkle linen-cotton fabric

A fabric, cotton and linen technology, applied in the field of preparation of antibacterial and anti-wrinkle cotton and linen fabrics, can solve the problems of poor antibacterial and anti-wrinkle effects, achieve good inhibition effect, wide application prospects, and improved anti-wrinkle performance

Inactive Publication Date: 2019-02-01
SUZHOU INST OF TRADE & COMMERCE
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the antibacterial and anti-wrinkle effects of existing cotton and linen fabrics are poor, and most fabrics cannot have both properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of antibacterial anti-wrinkle linen-cotton fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A preparation method of antibacterial wrinkle-resistant cotton and linen fabric, comprising the following steps:

[0020] (1) Add cotton and linen fabrics to 20wt% triethanolamine aqueous solution for ultrasonic treatment, the treatment temperature is 40°C, the treatment time is 3h, the ultrasonic frequency is 65Hz, and then the cotton and linen fabrics are ultrasonically machine washed with deionized water After 23 minutes, shake and dry the fabric for later use;

[0021] (2) Prepare 50nM silver nanoparticles dispersed in 0.01M pH7.4 PBS buffer, add PEG400 modified with thiol and amino groups at both ends, so that the concentration of PEG is 2M, shake and mix at room temperature for 40min, then Centrifuge it at 4000r / min for 8min, remove the supernatant, resuspend the precipitated particles with an equal volume of PBS buffer, and disperse the precipitated particles under ultrasonic conditions to prepare amino-modified silver nanoparticles;

[0022] (3) Dissolve 40 par...

Embodiment 2

[0026] A preparation method of antibacterial wrinkle-resistant cotton and linen fabric, comprising the following steps:

[0027] (1) Add cotton and linen fabrics to a triethanolamine aqueous solution with a mass fraction of 10wt% for ultrasonic treatment. The treatment temperature is 30°C, the treatment time is 2 hours, and the ultrasonic frequency is 50Hz. Then, the cotton and linen fabrics are ultrasonically machine washed with deionized water After 15 minutes, the fabric is shaken and dried for later use;

[0028] (2) Prepare 50nM silver nanoparticles dispersed in 0.01M pH7.4 PBS buffer, add PEG400 modified with thiol and amino groups at both ends, so that the concentration of PEG is 1M, shake and mix at room temperature for 30min, then Centrifuge it at 3000r / min for 5min, remove the supernatant, resuspend the precipitated particles with an equal volume of PBS buffer, and disperse the precipitated particles under ultrasonic conditions to prepare amino-modified silver nanopa...

Embodiment 3

[0033] A preparation method of antibacterial wrinkle-resistant cotton and linen fabric, comprising the following steps:

[0034] (1) Add cotton and linen fabrics to a triethanolamine aqueous solution with a mass fraction of 15wt% for ultrasonic treatment. The treatment temperature is 35°C, the treatment time is 2.5h, and the ultrasonic frequency is 60Hz. Then, the cotton and linen fabrics are treated with a deionized water ultrasonic machine. Wash for 20 minutes, shake and dry the fabric for later use;

[0035] (2) Prepare 50nM silver nanoparticles dispersed in 0.01M pH7.4 PBS buffer, add PEG400 modified with thiol and amino groups at both ends, so that the concentration of PEG is 1.5M, shake and mix at room temperature for 35min, Then it was centrifuged at 3500r / min for 6min, the supernatant was removed, the precipitated particles were resuspended with an equal volume of PBS buffer, and the precipitated particles were dispersed under ultrasonic conditions to obtain amino-modi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of antibacterial anti-wrinkle linen-cotton fabric. The method comprises the following steps: (1) ultrasonically treating the linen-cotton fabric with an aqueous solution of triethanolamine; (2) preparing amino-modified silver nanoparticles; (3) modifying 2,3-epoxypropyltrimethyl ammonium chloride by a carbodiimide solution, then crosslinking with the amino-modified silver nanoparticles, aminated graphene, and chitosan, and drying the materials; and (4) adding a dried product obtained in the step (3), tea polyphenol, malic acid, tartaric acid, tripolymaleic acid, nano TiO2, antimony trioxide, an osmotic agent, and fibroin to an aqueous solution of ethanol to prepare a finishing agent, and performing dip padding on the fabric to obtain the antibacterial anti-wrinkle linen-cotton fabric. The linen-cotton fabric prepared by the invention has good inhibition effect on Escherichia coli, Staphylococcus aureus and Candida albicans, and has good anti-wrinkle performance. Therefore, the fabric made by the invention has broad application prospects as the antibacterial anti-wrinkle fabric.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a preparation method of an antibacterial and anti-wrinkle cotton and linen fabric. Background technique [0002] Cotton and linen fabrics are highly recognized in modern textile and apparel applications due to their good hygroscopicity and comfortable wearing. However, cotton and linen fabrics are very easy to breed bacteria in a humid and warm environment. Under suitable conditions, the sugar in cotton fibers can even be used as nutrients for microorganisms, which will not only cause fabric discoloration and mechanical damage, but also threaten human health. , it can be seen that it is necessary to hinder and inhibit the metabolism and reproduction of microorganisms during fabric storage and use. Using antibacterial agents to finish textiles to inhibit and kill harmful bacteria is an important method to prepare antibacterial fabrics, but the long-term use of tradit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/83D06M13/328D06M15/53D06M15/03D06M11/74D06M13/192D06M13/207D06M11/46D06M11/47D06M15/15D06M101/06
CPCD06M11/46D06M11/47D06M11/74D06M11/83D06M13/192D06M13/207D06M13/328D06M15/03D06M15/15D06M15/53D06M16/00D06M2101/06D06M2200/20
Inventor 张小英
Owner SUZHOU INST OF TRADE & COMMERCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap