A method for curing and heat-treating drying of positive electrode wet raw board

A dry, positive electrode technology, applied in the direction of lead-acid battery electrodes, etc., can solve the problems of adding new production processes, prolonging the production cycle of plates, and making it difficult to stably transform the crystal form of positive electrode paste materials.

Active Publication Date: 2021-04-27
CAMEL GRP XIANGYANG BATTERY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the announced heat treatment method adds a new production process, increases the workload of transshipment, and prolongs the production cycle of the plate, which brings some inconvenience to the production
[0003] On the other hand, at present, the curing and drying temperature of the positive plate of the lead-acid battery is basically within 90°C, and the drying time of the wet green plate after the curing stage is as long as 15-30h, especially the loading capacity of the wet green plate in the curing room is large, and the wet green plate When the number of stacked sheets is large, it takes a long time for the wet raw board to dry completely
Chinese patent CN 1330024C discloses a method of increasing pressure and temperature for curing: in the pressure range 170KPa-230KPa, temperature 115°C-125°C; or pressure range 250KPa-360KPa, temperature 126°C-140°C, the curing The time is shortened from tens of hours to 1.5-2 hours, but the drying time is still more than 18 hours
Moreover, the curing time announced in the patent is too short, and the test verification shows that it is difficult to complete the stable transformation of the positive electrode paste material crystal form within 1.5-2 hours

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for curing and heat-treating drying of positive electrode wet raw board
  • A method for curing and heat-treating drying of positive electrode wet raw board
  • A method for curing and heat-treating drying of positive electrode wet raw board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The main process of positive electrode wet raw board curing and heat treatment drying is as follows: figure 1 Shown, the concrete technical parameter of the present embodiment is as shown in table 1:

[0031] Table 1

[0032]

[0033] Step 1 curing stage: the temperature is set to 55°C, the relative humidity is set to 98%, and the time is set to 28h. The pressure relief valve and compressed air are closed, the circulating fan and atomized water humidification are turned on, the indoor pressure is at normal pressure (1atm), and the inlet and outlet dampers are under timing control.

[0034] Compressed air can also be turned on during the curing stage to ensure adequate oxygen in the curing chamber. However, since the atomized water contains compressed air, the atomization humidification process has the function of replenishing air; and when the inlet and outlet dampers are opened regularly, the moisture will be discharged from the outlet damper and the air will ente...

Embodiment 2

[0043] The main process of positive electrode wet raw board curing and heat treatment drying is as follows: figure 1 Shown, the concrete technical parameter of the present embodiment is as shown in table 2:

[0044] Table 2

[0045]

[0046] Step 1 Curing stage: divided into two sub-steps, the first step is to set the temperature to 45°C, the relative humidity to 95%, and the time to 18h; the second step to set the temperature to 65°C, the relative humidity to 80%, and the time to 6h. Close the pressure relief valve and compressed air, turn on the circulating fan and atomized water humidification, the indoor pressure is normal pressure (1atm), and the inlet and outlet dampers are in the timing control state.

[0047] Step 2 heat treatment heating and pressure raising stage: the temperature is set to 150°C, the opening pressure of the relief valve is set to 0.4 Mpa, and the heating time is set to 2h. During this process, the inlet and outlet dampers are closed and the ato...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for solidifying and heat-treating a positive electrode wet raw board, which belongs to the technical field of lead-acid batteries. The method for curing and heat-treating the positive wet raw board is characterized in that: the positive wet green board is cured for 18-40h at a temperature of 40-70°C and a relative humidity of 80%-100%; then the temperature is set to 150-180°C , the opening pressure of the pressure relief valve is set to 0.4‑0.8Mpa, and the temperature rises for 1‑3h; after reaching the set temperature, keep warm for 1.5‑5h; . The invention can realize the heat treatment of the positive grid of the wet raw board during the curing and drying process of the wet raw board, improve the corrosion resistance of the positive grid, and at the same time effectively shorten the total time of curing and heat treatment and drying, and avoid separate treatment of the positive lead belt or The heat treatment of the grid will cause adverse effects such as new production processes, increased transshipment workload, and prolonged production cycle.

Description

technical field [0001] The invention belongs to the technical field of lead-acid storage batteries, and in particular relates to a method for solidifying and heat-treating a positive wet raw plate. Background technique [0002] Appropriate heat treatment of the rolled lead strip and the grid prepared by rolling the lead strip can reduce the internal residual stress and internal energy of the positive electrode grid alloy of the lead-acid battery, and promote the grain boundary reconstruction and regeneration of the grid alloy. Crystallization reduces the chemical instability of the grid alloy and enhances the corrosion resistance of the positive grid of the lead-acid battery. US Patent US 6802917 B and Chinese Patents CN 106435421 B, CN102925834A, and CN1775962A all demonstrate the beneficial improvement of the corrosion resistance of the positive grid after heat treatment. However, the announced heat treatment method adds a new production process, increases the workload of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/20H01M4/21
CPCH01M4/20H01M4/21Y02E60/10
Inventor 刘小锋孟刚张仁银徐建刚邓国强夏诗忠刘长来
Owner CAMEL GRP XIANGYANG BATTERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com