Anion coating additive for removing formaldehyde and purifying air, and preparation method and application of anion coating additive

A negative ion coating and formaldehyde purification technology, applied in the field of coatings, can solve the problems of poor surface performance and adhesion of coatings, unstable chemical properties of coatings, and long drying time, etc., to achieve smooth surface and excellent antifouling performance , Solve the effect of water absorption saturation

Inactive Publication Date: 2019-03-01
广东顺德碧昂负离子新材料有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Based on the function of negative ions to purify the air and promote health and the current situation of people's pursuit of healthy life quality, negative ion coatings are more and more recognized by people. However, although negative ion coatings on the market can effectively release negative ions, a large number of them are used When it comes to organic resins, it not only leads to high cost of use, but also the chemical properties of the coating are unstable, and the effect of wear resistance and heat resistance is poor; when this kind of coating is used, it takes a long time for the coating film to dry, which makes the construction period Too long; in addition, the surface properties and adhesion of the coating are poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] Second aspect, a kind of preparation method of the negative ion coating additive of removing formaldehyde and purifying air as described in the first aspect provided by the present invention, comprises the steps:

[0046] (1) After mixing monazite powder, rare earth-containing compound and water, add the second dispersant and stir at a speed of 200-800r / min for 3-10min, then add the second wetting agent and the second surfactant in sequence, Stir at a speed of 200-800r / min for 15-45min, and grind to obtain the basic material;

[0047] (2) After stirring the basic material obtained in step (1) for 3 to 10 minutes at a speed of 200 to 800 r / min, add the first dispersant, the first wetting agent, the first surfactant, and the aldehyde netting agent at a rate of 500 Stir at a speed of ~1000r / min for 5-20min, then add water and anti-settling agent, stir at a speed of 500-1000r / min for 3-10min, finally add defoamer and preservative, and stir at a speed of 500-1000r / min 10 ~ ...

Embodiment 1

[0061] A kind of preparation method of the negative ion paint additive that removes formaldehyde and purifies air that present embodiment provides, comprises the steps:

[0062] (1) Get the following raw materials by weight percentage: monazite powder 27%, rare earth-containing compound 36%, sodium polyacrylate 0.5%, alkylphenol polyoxyethylene ether 0.3%, polyethylene glycol 4.8%, polyethylene glycol Ethylene glycol phthalate 3.4%, the balance of deionized water; after mixing monazite powder, rare earth-containing compound and deionized water, add sodium polyacrylate and stir at a speed of 200-800r / min for 3-10min, then Add alkylphenol polyoxyethylene ether, polyethylene glycol, and polyethylene phthalate in sequence, stir at a speed of 200-800r / min for 15-45min, and grind to obtain the basic material;

[0063] (2) Get the following raw materials in percent by weight: 53% of the basic material obtained in step (1), 0.4% of sodium polyacrylate, 0.3% of alkylphenol polyoxyethyl...

Embodiment 2

[0065] Adopt the preparation method similar to embodiment 1 to prepare the negative ion coating additive that removes formaldehyde and purify the air, the difference between the present embodiment and embodiment 1 is only: the raw material used in the step (1), by weight percentage, comprises: monazite powder 20 %, rare earth-containing compound 45%, sodium polyacrylate 0.1%, alkylphenol polyoxyethylene ether 0.1%, polyethylene glycol 10%, polyethylene glycol phthalate 5%, deionized water balance; The raw materials used in the step (2), by weight percentage, include: 40% of the basic material obtained in the step (1), 0.1% of sodium polyacrylate, 0.1% of alkylphenol polyoxyethylene ether, 25% of polyethylene glycol, 10% polyethylene glycol phthalate, 0.05% silicon ether copolymer defoamer, 0.1% silicon dioxide, 0.05% Cathone, titanium dioxide doped with silver (the doping amount of silver is 1wt%) 15 %, the balance of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anion coating additive for removing formaldehyde and purifying air, and a preparation method and application of the anion coating additive. The anion coating additive for removing the formaldehyde and purifying the air is prepared from the following components in percentage by weight: 40-60% of base materials, 0.1-1% of a first dispersing agent, 0.1-1% of a first wettingagent, 20-35% of a first surfactant, 0.05-0.5% of a first defoaming agent, 0.1-1% of an anti-settling agent, 0.05-0.5% of a first preservative, 5-15% of a formaldehyde removing agent, and the balanceof water, wherein the base materials are prepared from the following components in percentage by weight: 20-35% of monazite powder, 30-45% of a compound containing rare earth, 0.1-1% of a second dispersing agent, 0.1-1% of a second wetting agent, 5-15% of a second surfactant, and the balance of water. The anion coating additive is scientific and reasonable in formula, zero VOC and zero formaldehyde are achieved, and heavy metal such as lead, cadmium, chromium and mercury is not contained; the removal rate of finished coating containing the coating additive to the formaldehyde in surrounding air can reach 95% or above, the finished coating has a long-acting removing effect on the formaldehyde, negative oxygen ions with high concentration, high vitality and small particle size can be released continuously, and the releasing number of anions is up to 9000 / cm<3>.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an anion coating additive for removing formaldehyde and purifying air, a preparation method and application thereof. Background technique [0002] With the improvement of people's living standards, the environmental protection requirements for the environment and daily necessities are getting higher and higher. The development of the coatings industry also tends to be environmentally friendly. People are paying more and more attention to the quality of indoor air. The first indicator to evaluate indoor air quality is the content of negative ions; negative oxygen ions are known as "air vitamins", which can be positively charged with dust, smoke, PM2.5, etc. in the air After the particles are combined, they settle to the ground, and can react with formaldehyde, benzene, TVOC and other decoration pollutants in the air, and decompose them into carbon dioxide and water, thereby puri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/14C09D5/16C09D7/61
CPCC09D5/14C09D5/1687
Inventor 刘洪军莫福德
Owner 广东顺德碧昂负离子新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com