High-density fireproof silicone adhesive and preparation process thereof

A silicone rubber, high-density technology, applied in the rubber field, can solve problems such as inconvenience, high price, and unenvironmental protection, and achieve the effects of broad application prospects, low production cost, and good radiation resistance.

Pending Publication Date: 2019-03-19
深圳市东信硅材料有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the existing fire-resistant silicone rubber can meet the fire-proof requirements through flame-retardant powder, it has disadvantages such as not being environmentally friendly, having poor temperature resistance, poor acid and alkali resistance, producing toxic gases or solids when decomposed, and being expensive; The powder is easily oxidized into bulky oxides, which affects the performance of silicone rubber, or is highly toxic and expensive, which brings inconvenience to people's use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A one-component condensation type silicone rubber with high density and fire resistance, including the following raw materials in parts by weight: 100 parts of 107 rubber, 5 parts of 201 silicone oil, 150 parts of micaceous iron oxide, 80 parts of quartz powder, and 5 parts of fumed white carbon black , 10 parts of crosslinking agent, 1.5 parts of aminopropyltriethoxysilane and 0.1 part of catalyst. The crosslinking agent includes methyl tributylketoxime silane and vinyl tributylketoxime silane, and the mass ratio of methyl tributylketoxime silane to vinyl tributylketoxime silane is 4:1.

[0021] The viscosity of 107 glue is 8000CS, the weight fraction of hydroxyl group is 0.06%, the viscosity of 201 silicone oil is 500CS, the particle size of mica iron oxide is 10 mesh-1000 mesh, the particle size of quartz powder is 10-10000 mesh, fumed The specific surface area is 150 square meters per gram.

[0022] Disperse 107 glue, 201 silicone oil, micaceous iron oxide and quar...

Embodiment 2

[0024] A one-component condensation type silicone rubber with high density and fire resistance, including the following raw materials in parts by weight: 100 parts of 107 glue, 10 parts of 201 silicone oil, 120 parts of mica iron oxide, 50 parts of quartz powder, 100 parts of nano calcium carbonate, 8 parts of methyltrimethylsilane, 1.5 parts of glycidylmioxypropyltrimethoxysilane and 0.4 parts of catalyst.

[0025] The viscosity of 107 glue is 8000CS, the weight fraction of hydroxyl group is 0.06%, the viscosity of 201 silicone oil is 500CS, the particle size of mica iron oxide is 10 mesh-1000 mesh, the particle size of quartz powder is 10-10000 mesh, and the The particle size is 40-60 microns.

[0026] Disperse 107 glue, 201 silicone oil, micaceous iron oxide, nano-calcium carbonate and quartz powder in a mixer, and then lower the temperature at 150 degrees Celsius for 3 hours at a vacuum of minus 0.05 MPa to obtain the first mixture. After the mixture is cooled to room tem...

Embodiment 3

[0028] A two-component condensation type silicone rubber with high density and fire resistance, including the following raw materials in parts by weight: 100 parts of 107 rubber, 5 parts of 201 silicone oil, 100 parts of mica iron oxide, 80 parts of quartz powder, and 0.5 parts of fumed white carbon black , 30 parts of tetraethoxysilane, 20 parts of coupling agent and 0.1 part of catalyst. The coupling agent comprises glycidylmioxypropyltrimethoxysilane and aminopropyltriethoxysilane, and the mass ratio of glycidylmioxypropyltrimethoxysilane and aminopropyltriethoxysilane is 1:1.

[0029] The viscosity of 107 glue is 750CS, the weight fraction of hydroxyl group is 0.2%, the viscosity of 201 silicone oil is 350CS, the particle size of micaceous iron oxide is 10-1000 mesh, and the particle size of quartz powder is 10-10000 mesh.

[0030] Disperse 107 glue, 201 silicone oil, micaceous iron oxide, fumed silica and quartz powder evenly in a mixer, then lower the vacuum degree to n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-density fireproof silicone adhesive and a preparation process thereof. The silicone adhesive is prepared from the following raw materials in parts by weight: 95-108 partsof base adhesive, 0-30 parts of plasticizer, 50-300 parts of scale-like powder, 0-150 parts of unreinforced powder, 0-100 parts of reinforced filler, 0.01-20 parts of crosslinker, 0-5 parts of couplerand 0.0001-10 parts of catalyst. The high-density fireproof silicone adhesive uses the scale-like powder which has the characteristics of high temperature resistance, acid and alkali resistance and low vapor transmittance and can form a laminated state by different flakes after proper addition amount is achieved, and the aim of retarding flame can be achieved by stopping transmittance of high temperature or flame; under the combined effect of the scale-like powder and other raw materials, the high-density fireproof silicone adhesive has excellent radiation resistance and fireproofing performance without flame-retardant powder or metal powder, and has low production cost and wide application prospect.

Description

technical field [0001] The invention relates to the field of rubber, in particular to a high-density fireproof silicone rubber. Background technique [0002] As people's lives become more and more intelligent, people's demand for electricity is also increasing, and there are more and more power plants, more and more substations, and they are getting closer to people's gathering areas. There are more and more electromagnetic ionizing radiation, and people have higher and higher requirements for fire prevention and radiation protection. [0003] Fireproof silicone rubber is a commonly used anti-radiation material. It uses zinc borate, magnesium hydroxide, aluminum hydroxide, nitrogen, phosphorus, nitrogen-phosphorus composite, halogen-containing flame retardants, antimony-based flame retardants, Rare oxides, etc., alone or combined with several kinds of flame retardant powders, through the decomposition of flame retardants to generate water vapor, carbon dioxide, non-combusti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/04C08L83/07C08K13/04C08K3/22C08K3/36C08K5/544
CPCC08K2003/2272C08K2201/003C08K2201/006C08K2201/014C08L83/04C08L2201/02C08L2201/08C08L2205/025C08K13/04C08K7/00C08K3/22C08K3/36C08K5/544
Inventor 王存富王艳超
Owner 深圳市东信硅材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products