A functional membrane and its preparation method

A diaphragm and functional technology, applied in the field of functional diaphragm and its preparation, can solve the problems of large expansion and contraction rate, easy bulging of battery cells, battery deformation, etc.

Active Publication Date: 2020-08-25
SHENZHEN SENIOR TECH MATERIAL
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the energy density of the battery cell is getting higher and higher, and the expansion and contraction rate of the electrode during the charging and discharging process is also relatively large. It will be very easy to bulge, which will eventually cause the battery to deform and cause the battery cell to be scrapped

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A functional membrane and its preparation method
  • A functional membrane and its preparation method
  • A functional membrane and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] This embodiment provides a functional diaphragm, the preparation steps of which are as follows:

[0042] Dissolve 10g polysulfone ether ketone resin and 5g polyvinylidene fluoride-hexafluoropropylene resin in 60g N,N-dimethylformamide, then add 4g 4wt% ethanol and 0.01g photoinitiator TPO, stir at high speed for 30 Minutes, evenly, let it stand for degassing. The resulting slurry is sprayed on the surface of a dry-process polypropylene base film with a thickness of 16 microns and a porosity of 40% through a high-speed rotating spray disc, and then undergoes UV pre-curing (pre-curing time 1s), gel washing with water, and UV light curing. (curing time 5s). Finally dry to obtain coating thickness is 3 microns, and the single island-shaped particle (being single island-shaped coating) size is the function of 200-400 micron (island-shaped particle size is different, so what is given in the embodiment is a range value) function diaphragm. The coverage area of ​​the coating...

Embodiment 2

[0044] This embodiment provides a functional diaphragm, the preparation steps of which are as follows:

[0045] Dissolve 10 g of photocurable polyacrylate resin, 10 g of polyester acrylate and 10 g of gel-type polyacrylate resin with active functional groups in a mixed solution of 40 g of acetone and 40 g of toluene. Add 5 g of deionized water, 5 g of 8 wt % ethylene glycol and 0.1 g of photoinitiator α, α-dimethoxy-α-phenylacetophenone, stir at high speed for 30 minutes, and let it stand for defoaming. The resulting slurry is sprayed on the surface of a dry-laid non-woven fabric base film with a thickness of 12 microns and a porosity of 45% through a high-speed rotating spray disc. After UV pre-curing (pre-curing time 1s), gel washing and pore making, UV light curing (curing time 5s). Finally, dry to obtain a functional separator with a coating thickness of 5 microns and a single island particle size of 100-200 microns. The coverage area of ​​the coating on the base film is...

Embodiment 3

[0047] This embodiment provides a functional diaphragm, the preparation steps of which are as follows:

[0048] 5g photocurable urethane acrylate resin, 6g polyether acrylate, 4g photocurable polybutadiene oligomer resin and 8g PVDF-HFP (copolymer of vinylidene fluoride and hexafluoropropylene) gel resin were dissolved in 20g NMP ( N,N-dimethylpyrrolidone), 10g p-xylene and 40g formamide in a mixture. Then add 1g methanol, 2g ether, 3g dichloromethane and 0.0025g photoinitiator 2,4-dihydroxybenzophenone, 0.0035g photoinitiator α, α-dimethoxy-α-phenylacetophenone , 0.02g photoinitiator TPO, stirred at high speed for 30 minutes, evenly, and let it stand for defoaming. The resulting slurry is sprayed on the surface of the wet-process PE-ceramic base membrane with a thickness of 12 microns and a porosity of 45% through a high-speed rotating spray disc. After UV pre-curing (pre-curing time 1s), hot air baking, UV light curing (curing time 5s). Finally, dry to obtain a functional...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a functional diaphragm and a preparation method thereof, and relates to the technical field of lithium ion battery production. The functional diaphragm includes a base film, and the base film includes one or more of polyolefin film, polyolefin ceramic coating film, non-woven fabric, and polyimide film; coating, the coating is formed on the base film, and coated The layer is distributed in an island shape on the base film, and the coating is made of the following raw materials in parts by weight: 10-20 parts of photocurable resin, 5-10 parts of gel resin with active functional groups, and 60-80 parts of main solvent , 4-10 parts of cosolvent, 0.01-0.1 part of photoinitiator. The preparation method of the functional diaphragm includes: coating the mixture of photocurable resin, gel resin with active functional groups, main solvent, co-solvent and photoinitiator on the base film, ensuring that the formed coating is on the base film during coating Distributed in an island shape. After coating, UV pre-curing, pore forming and UV curing were performed on the functional membrane in sequence. This functional separator can solve the problem of battery bulging.

Description

technical field [0001] The invention relates to the technical field of lithium ion battery production, in particular to a functional diaphragm and a preparation method thereof. Background technique [0002] As the energy density of lithium-ion power batteries continues to increase, safety issues have become the primary issue that needs to be addressed in battery design. Especially when the energy density of a single battery reaches 300Wh / kg, the traditional polyolefin-based film and ceramic coating film are difficult to meet the requirements of battery applications, and the polymer-coated separator has a great contribution to the structural design of the battery. To a certain extent, the safety performance and battery life of the battery have been improved, and it has become the first choice for applications. At present, there are three types of power battery cells: square, soft pack and cylindrical. Among them, square cells using winding technology are more widely used by ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/16H01M2/14H01M10/0525H01M10/058H01M50/403H01M50/414H01M50/449H01M50/489
CPCH01M10/0525H01M10/058H01M50/403H01M50/411H01M50/449Y02E60/10Y02P70/50
Inventor 曹江陈秀峰
Owner SHENZHEN SENIOR TECH MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com