Pesticide storing container and preparation method thereof
A technology for storing containers and pesticides, applied in chemical instruments and methods, containers, rigid containers, etc., can solve problems such as poor toughness, high breakage rate, accidental poisoning, etc., and achieve improved elastic modulus, tensile properties, and notched impact strength. The effect of strengthening, increasing toughness and strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0041] Preparation examples of toughening agent 1-3
[0042] In Preparation Examples 1-3, the acrylic emulsion was selected from the td-br type acrylic emulsion sold by Shanxi Zhongyi Tuoda Construction Engineering Materials Co., Ltd., and the bisphenol A type epoxy resin emulsion was selected from the TC sold by Jiangyin Wanqian Chemical Co., Ltd. -K44 type bisphenol A general liquid epoxy resin.
Example Embodiment
[0043] Preparation Example 1: (1) According to the ratio in Table 1, weigh 5kg of deionized water, put it into the reactor, add 1kg of zinc stearate to the reactor, heat to 50°C, add 10kg of pineapple leaf fiber, 1kg of glass fiber and 1kg of coconut fiber are stirred at 400r / min until the three fibers are fully dissolved and cooled to room temperature; the pineapple leaf fiber length is 3mm, diameter is 10μm, glass fiber length is 1.5mm, diameter is 10μm , The length of coconut fiber is 10mm and the diameter is 1.5μm;
[0044] (2) Mix 1 kg of acrylic emulsion and 5 kg of bisphenol A epoxy resin and heat to 40° C., add the resultant of step (1), and stir at a rotation speed of 200 r / min to mix uniformly.
[0045] Table 1 The raw material ratio of the toughening agent in preparation examples 1-3
[0046]
Example Embodiment
[0047] Preparation Example 2: (1) Weigh 8kg of deionized water, put it into the reactor, add 3kg of zinc stearate to the reactor, heat to 60°C, add 13kg of pineapple leaf fiber, 5kg of glass fiber and 3kg of coconut fiber, Stir at a speed of 405r / min until the three fibers are fully dissolved and cool to room temperature; the length of the pineapple leaf fiber is 5mm, the diameter is 13μm, the length of glass fiber is 2.0mm, the diameter is 13μm, and the length of coconut fiber is 15mm. The diameter is 2.5μm;
[0048] (2) Mix 3 kg of acrylate emulsion and 8 kg of bisphenol A type epoxy resin and heat to 45° C., add the resultant of step (1), and stir at 250 r / min to mix uniformly.
PUM
Property | Measurement | Unit |
---|---|---|
Length | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap