Wear-resistant self-priming pump liner prepared based on fluorine plastics

A technology of self-priming pumps and fluoroplastics, which is applied in the field of pump valve preparation, can solve problems affecting work efficiency, pump valve damage, hazards, etc., and achieve the effect of increasing material texture, reasonable raw material ratio, and simple process flow

Inactive Publication Date: 2019-05-14
慈溪市得鑫五金配件有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no need to install a bottom valve in the pipeline. Just ensure that there is a quantitative suction liquid stored in the pump body before work. Different liquids can use self-priming pumps of different materials. With the continuous improvement of technology, self-priming pumps are also used in various fields. Diverse, in some chemical companies, because a large amount of acid and alkali and highly corrosive liquids need to be transported, the traditional self-priming pump will have corrosion and aging problems when used, and the concentration of these problems will lead to self-priming The pump is aging and damaged
[0003] Fluorine-lined self-priming pumps have solved the corrosion problem of the above-mentioned self-priming pumps in the field of pump valves at the present stage. The process is made of metal casing tightly lined with fluoroplastics. The main flow-passing parts, impeller and pump cover, are made of metal inserts and outsourced with fluoroplastics at high temperature. The application of this method fully solves the aging problem of self-priming pumps. , but there will still be some disadvantages in actual use
[0004] Fluoroplastics are generally plastic materials. In practical applications, due to different application fields, the fluoroplastics in the self-priming pump will transport different materials during normal use. In the industrial or chemical field, some mixed with a large amount of When the mixed liquid of particulate matter is pumped, due to the strong hardness of the particulate matter, the inner lining will be worn, scratched, even cracked and deformed during long-term transportation. In the lightest cases, the actual pump valve will be damaged, resulting in increased maintenance costs and affecting work efficiency. , the severe one will cause the liquid in the pump to overflow, and the harm caused is immeasurable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Weighing: PTFE 80kg, polyperfluoroethylene propylene 60kg, silicon nitride 8kg, boron carbide 6kg, gypsum powder 8kg, milk thistle extract 6kg, ethyl acetate 3kg, zinc stearate 5kg, antimony oxide 6kg, modified paraffin wax 2kg, chromium trioxide 3kg, zirconia mullite 6kg, white corundum powder 2kg, lignocellulose 3kg, high-strength adhesive 25kg.

Embodiment 2

[0024] Weighing: PTFE 81kg, polyperfluoroethylene propylene 61kg, silicon nitride 9kg, boron carbide 7kg, gypsum powder 9kg, milk thistle extract 7kg, ethyl acetate 4kg, zinc stearate 6kg, antimony oxide 7kg, modified paraffin wax 3kg, chromium trioxide 4kg, zirconia mullite 7kg, white corundum powder 3kg, lignocellulose 4kg, high-strength adhesive 30kg.

[0025] The method for preparing above-mentioned embodiment 1-2 is:

[0026] a. Put polytetrafluoroethylene and polyperfluoroethylene propylene into the internal mixer, raise the temperature to 120°C within 20 minutes, stir while heating, until the materials are completely melted, and then stand at constant temperature for later use;

[0027] b. Add the modified paraffin wax to the raw material treated in the above step a, heat up to 150° C., let stand at a constant temperature, and set aside;

[0028] c. Take a ball mill and grind silicon nitride, boron carbide, gypsum powder, milk thistle extract, ethyl acetate, zinc stear...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant self-priming pump liner prepared based on fluorine plastics, and relates to the technical field of pump valve preparation. The wear-resistant self-priming pumpliner is prepared from, by weight, 80-82 parts of polytetrafluoroethylene, 60-62 parts of polyperfluoro-ethylene propylene, 15-25 parts of phenolic resin, 6-8 parts of molybdenum disulfide, 3-5 partsof carbon black, 8-10 parts of titanium dioxide, 2-4 parts of Mohr's salt, 3-5 parts of barium sulfate, 5-7 parts of magnesium hexasilicate, 3-5 parts of brown aluminum oxide, 3-5 parts of nano-silicon carbide, 6-8 parts of nano-zinc oxide, 2-4 parts of boron oxide, 6-8 parts of glass fibers and 40-50 parts of high-strength mixed adhesives. The wear-resistant self-priming pump liner has the advantages that the technological process is simple, raw material ratio is reasonable, raw materials are inexpensive and easy to obtain, the liner has better wear-resistant effects while the anticorrosionperformance of a traditional fluorine plastic is ensured, and the liner is low in price and simple to process.

Description

technical field [0001] The invention relates to the technical field of pump valve preparation, in particular to a wear-resistant self-priming pump lining material prepared based on fluoroplastics. Background technique [0002] The working principle of the self-priming pump is to fill the pump casing with water before starting the pump. After starting, the impeller rotates at high speed to make the water in the impeller channel flow to the volute. The air in the tube enters the pump and travels through the impeller channel to the outer edge. The self-priming pump is a self-priming centrifugal pump, which has the advantages of compact structure, convenient operation, stable operation, easy maintenance, high efficiency, long life, and strong self-priming ability. There is no need to install a bottom valve in the pipeline. Just ensure that there is a quantitative suction liquid stored in the pump body before work. Different liquids can use self-priming pumps of different materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/18C08L27/12C08L61/06C08L97/00C08L1/28C08L29/04C08L91/06C08K13/04C08K7/14C08K3/30C08K3/04C08K3/22C08K3/34C08K5/098
Inventor 徐玲玲
Owner 慈溪市得鑫五金配件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products