Method for preparing easy-to-disperse waterborne bismuth oxychloride powder and bismuth oxychloride pearlescent slurry through ultrasonic reaction

A bismuth oxychloride and easy-to-dispersion technology, which is applied in chemical instruments and methods, inorganic chemistry, bismuth compounds, etc., can solve the problems of poor dispersion and easy aggregation, complicated process, and uneven particle size distribution, so as to achieve the goal of not easy to aggregate, and the product Effect of high purity and improved crystal weather resistance

Pending Publication Date: 2019-05-14
东阳市康龙工艺材料有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a water-based bismuth oxychloride that is easily dispersible prepared by ultrasonic reaction, aiming at the problems that the particle size distribution of the bismuth ox

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing easy-to-disperse waterborne bismuth oxychloride powder and bismuth oxychloride pearlescent slurry through ultrasonic reaction
  • Method for preparing easy-to-disperse waterborne bismuth oxychloride powder and bismuth oxychloride pearlescent slurry through ultrasonic reaction

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Example 1

[0031] Take 20L of bismuth nitrate aqueous solution with a mass concentration of 15%, add 1L of dilute hydrochloric acid with a mass concentration of 15% and a sodium chloride solution with a mass concentration of 15% to obtain solution A; add 30L of deionized water to a 50L reactor to Adjust the pH to 4.0 by dilute hydrochloric acid with a mass concentration of 15%, heat it to 60°C, and use 30kHz ultrasonic irradiation; add 30ml of nano-silica dispersion with a mass concentration of 20% to the reactor; then add to the reactor Drop the solution A obtained in step (1) at a feed rate of 0.12L / h and react for 10 minutes; adjust the feed rate of adding the solution A obtained in step (1) to the reactor to 0.56L / h and react for 20 minutes; then adjust the feed The rate is 1.12L / h, the reaction is 40 minutes; the feeding rate is adjusted to 1.6L / h, and the reaction is 60 minutes; the feeding rate is adjusted to 2.8L / h, and the reaction is 90 minutes; the feeding rate...

Example Embodiment

[0032] Example 2

[0033] Take 20L of bismuth nitrate aqueous solution with a mass concentration of 13%, add 1L of dilute hydrochloric acid with a mass concentration of 15% and a sodium chloride solution with a mass concentration of 15% to obtain solution A; add 30L of deionized water to a 50L reactor to Adjust the pH to 4.0 by dilute hydrochloric acid with a mass concentration of 15%, heat it to 60°C, and use 30kHz ultrasonic irradiation; add 30ml of nano-silica dispersion with a mass concentration of 20% to the reactor; then add to the reactor Drop the solution A obtained in step (1) at a feed rate of 0.1L / h, and react for 15 minutes; adjust the feed rate of adding the solution A obtained in step (1) to the reactor to 0.5L / h, and react for 30 minutes; then adjust the feed The rate is 1L / h, the reaction is 40 minutes; the feeding rate is adjusted to 1.5L / h, and the reaction is 65 minutes; the feeding rate is adjusted to 2.5L / h for 95 minutes; the feeding rate is adjusted to 3.8L...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing easy-to-disperse waterborne bismuth oxychloride powder and bismuth oxychloride pearlescent slurry through ultrasonic reaction. The method includes following steps: (1), taking an inorganic salt water solution of bismuth, and adding diluted hydrochloric acid and a sodium chloride solution of 10-20% in mass concentration to obtain a solution A; (2), adding deionized water into a reaction kettle, using diluted hydrochloric acid to adjust pH, heating, and performing ultrasonic irradiation; (3), adding nano silicon dioxide dispersion liquid into the reaction kettle; (4), dropwise adding the solution A obtained in the step (1) into the reaction kettle, and adjusting charging rate and reaction time; (5), adding a cerium nitrated solution, and increasing ultrasonic irradiation power; (6), filtering reaction liquid obtained in the step (5), using deionized water to wash obtained solid, and drying to obtain the easy-to-disperse waterborne bismuth oxychloride powder. The method has the advantages that raw materials are low in cost and easy to get, process operation is simple, and obtained bismuth oxychloride is uniform in grain size distribution,high in dispersity and weatherability and resistant to ultraviolet.

Description

technical field [0001] The invention relates to a method for synthesizing bismuth oxychloride pearlescent pigment, in particular to a method for preparing easily dispersible water-based bismuth oxychloride powder and bismuth oxychloride pearlescent slurry by ultrasonic reaction. Background technique [0002] Bismuth oxychloride (BiOCl) is a new type of environmentally friendly pearlescent material, non-toxic, with unique surface adhesion properties and smoothness. Its position in pearlescent pigments is second only to mica titanium pearlescent pigments, and is widely used in cosmetics production, automotive coatings and the manufacture of pearlescent plastic films. Compared with mica titanium pearlescent pigments, bismuth oxychloride not only has pearl luster, but also has an extremely delicate mercerizing effect that mica titanium pearlescent pigments do not have. [0003] The research on the preparation of pearlescent bismuth oxychloride is only a matter of recent decades...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09C1/00C09C3/06C01G29/00
Inventor 周美秀
Owner 东阳市康龙工艺材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka