Preparation method of magnetic photocatalyst for sewage treatment

A photocatalyst and sewage treatment technology, applied in the direction of adsorption water/sewage treatment, light water/sewage treatment, physical/chemical process catalysts, etc., can solve the problems of easy agglomeration, difficult separation and recycling, and achieve avoidance of agglomeration and high reuse rate, the effect of improving water treatment efficiency

Pending Publication Date: 2019-05-28
刘华
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

First solved nano TiO 2 The problem of easy agglomeration during particle preparation, and secondly solved the problem of nano-TiO 2 Photocatalysts are easy to agglomerate when treating sewage and are difficult to separate and recycle. It has achieved the double effect of flocculation and photocatalytic degradation and decomposition of pollutants in sewage treatment, and the separation and recovery rate of magnetic photocatalyst has reached 99%, which can realize the convenience of catalyst and sewage. Rapid separation, no secondary pollution to the water body, and improved catalyst reuse rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of magnetic photocatalyst for sewage treatment
  • Preparation method of magnetic photocatalyst for sewage treatment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of preparation method of magnetic photocatalyst for sewage treatment, its specific preparation steps are as follows:

[0037] (1) Nano-TiO 2 Sol preparation:

[0038] Disperse 60mL of tetrabutyl titanate in a mixed solution of 420mL of absolute ethanol and 6mL of glacial acetic acid, and stir evenly; mix 12g of γ-glycidyl etheroxypropyltrimethoxysilane with 12g of absolute ethanol, and add the above In the system, continue to stir; then adjust the pH of the system to 6 with hydrochloric acid solution, and stir evenly to obtain nano-TiO 2 Sol A;

[0039] (2) Nano-TiO 2 Preparation of sodium alginate / polyacrylamide composite hydrogel:

[0040] Dissolve 1g of sodium alginate in deionized water to prepare a 1% sodium alginate solution; add nano-TiO to the sodium alginate solution 2 Sol A, stir evenly to obtain composite hydrogel B; add 10g acrylamide, 2g acrylic acid to composite hydrogel B and stir evenly, then feed nitrogen into the reaction system, then add 0...

Embodiment 2

[0047] A kind of preparation method of magnetic photocatalyst for sewage treatment, its specific preparation steps are as follows:

[0048] (1) Nano-TiO 2 Preparation of sol: Disperse 70mL of tetrabutyl titanate in a mixed solution of 490mL of absolute ethanol and 7mL of glacial acetic acid, and stir evenly; after mixing 14g of γ-glycidyl etheroxypropyltrimethoxysilane and 14g of absolute ethanol, Add dropwise to the above system and continue to stir; adjust the pH of the system to 6 with hydrochloric acid solution, and stir evenly to obtain nano-TiO 2 Sol A;

[0049] (2) Nano-TiO 2 Preparation of sodium alginate / polyacrylamide composite hydrogel:

[0050] Dissolve 2g of sodium alginate in deionized water to prepare a 1.5% sodium alginate solution; add nano-TiO to the sodium alginate solution 2 Sol A, stir evenly to obtain composite hydrogel B; add 8.5g acrylamide and 2.5g acrylic acid to composite hydrogel B, stir evenly, then pass nitrogen into the reaction system, and t...

Embodiment 3

[0057] A kind of preparation method of magnetic photocatalyst for sewage treatment, its specific preparation steps are as follows:

[0058] (1) Nano-TiO 2 Sol preparation:

[0059] Disperse 85mL of tetrabutyl titanate in a mixed solution of 600mL of absolute ethanol and 8.5mL of glacial acetic acid, and stir evenly; mix 34g of γ-glycidyl etheroxypropyltrimethoxysilane with 34g of absolute ethanol, and add dropwise In the above system, continue to stir; adjust the pH of the system to 6 with hydrochloric acid solution, and stir evenly to obtain nano-TiO 2 Sol A;

[0060] (2) Nano-TiO 2 Preparation of sodium alginate / polyacrylamide composite hydrogel:

[0061] Dissolve 3g of sodium alginate in deionized water to prepare a 2% sodium alginate solution; add nano-TiO to the sodium alginate solution 2 Sol A, stir evenly to obtain composite hydrogel B; add 7g acrylamide and 3g acrylic acid to composite hydrogel B and stir evenly, then feed nitrogen into the reaction system, then a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a magnetic photocatalyst for sewage treatment. According to the preparation method of the magnetic photocatalyst, the magnetic photocatalyst is preparedin the mode that a magnetic material and nano titanium dioxide are wrapped with polymers in situ, the separation efficiency of the photocatalyst is improved through the mode of combination of wrapping and magnetic separation, and the mode of treating sewage by double effects of flocculation and photocatalysis is achieved. The separation and recovery rate of the catalyst reaches 99% or above, andthe ideal removal effect on both organic matter and odor in the sewage is achieved.

Description

technical field [0001] The invention relates to the field of sewage treatment, in particular to a preparation method of a magnetic photocatalyst for sewage treatment. Background technique [0002] With the acceleration of industrialization and the improvement of human living standards, the discharge of industrial wastewater and domestic sewage is increasing, and the problem of water pollution is becoming more and more serious, which makes people pay a heavy price. Due to the complex sources of industrial wastewater and domestic sewage, such as the different components of factory wastewater, it is necessary to research and develop a technology suitable for the treatment of various pollutants. [0003] The surface effect of nanomaterials makes them have high chemical activity. The smaller the particles, the higher the surface activity, and they are easy to combine with other atoms, making them widely concerned in the field of sewage treatment. [0004] Nano-TiO 2 With the el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J31/38C02F1/30C02F1/52C02F1/56C02F1/28
Inventor 刘华
Owner 刘华
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com