A kind of synthesis of au-doped wo with scheelite concentrate 3 Methods and applications of nanosheets

A technology of nanosheets and concentrates is applied in the field of scheelite concentrate to synthesize Au-doped WO3 nanosheets, which can solve the problems of high price and achieve the effects of good reversibility, low preparation cost and good application prospects.

Active Publication Date: 2021-03-12
NORTHEASTERN UNIV LIAONING
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Prepare WO in existing 3 In the research of nanomaterials, sodium tungstate, ammonium paratungstate, tungsten hexachloride, tungstic acid and other analytically pure or high-purity elemental tungsten metals are mostly used as tungsten sources. These agents are expensive and have certain pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of synthesis of au-doped wo with scheelite concentrate <sub>3</sub> Methods and applications of nanosheets
  • A kind of synthesis of au-doped wo with scheelite concentrate <sub>3</sub> Methods and applications of nanosheets
  • A kind of synthesis of au-doped wo with scheelite concentrate <sub>3</sub> Methods and applications of nanosheets

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] The invention is a kind of synthetic Au-doped WO with scheelite concentrate 3 The method of nanosheet and its function in NO 2 Application of gas sensor. The X-ray diffraction spectrum and scanning electron microscope photograph of the scheelite concentrate (grade being 62.36%) adopted in the present invention are as follows figure 1 As shown, the results show that the raw material of scheelite concentrate is composed of irregular massive particles, and its main useful mineral is CaWO 4 . A gas-sensitive coating for Au-doped WO 3 The gas sensor of nanosheets, its structure schematic diagram is as follows figure 2 shown, where the heating wire 2 is made from Al 2 o 3 The ceramic tube 1 traverses and is welded on the heating electrode of the hexagonal base, the gold electrode 3 is coated on the outer surface of the ceramic tube 1 and welded on the measuring electrode of the hexagonal base through the platinum wire 4, the gas-sensitive coating 5 is coated covered ...

Embodiment 2

[0068] A gas-sensitive coating for Au-doped WO 3 The gas sensor of nanosheets, its structure schematic diagram is as follows figure 2 shown.

[0069] A kind of synthesis of Au-doped WO from scheelite concentrate 3 Preparation method of nanosheets and NO 2 Gas sensor, follow the steps below:

[0070] ①Under the conditions of NaOH concentration of 17.57mol / L, liquid-solid ratio of 1:1, reaction temperature of 180°C, holding time of 120min, and stirring speed of 400rpm, the scheelite concentrate was leached with NaOH to obtain the leached product, and the leached product was filtered to obtain The filtrate and the leaching slag were washed with deionized water for 3 times to obtain a washing solution, and the filtering solution and the leaching solution were combined to obtain a leaching solution containing sodium tungstate;

[0071] ② Dilute the solution obtained in step ①, and add 70 mL of deionized water to 2 mL of the leaching solution containing sodium tungstate with a ...

Embodiment 3

[0078] A gas-sensitive coating for Au-doped WO 3 The structure diagram of the nanosheet gas sensor is shown in Figure 2.

[0079] A kind of synthesis of Au-doped WO from scheelite concentrate 3 Preparation method of nanosheets and NO 2 Gas sensor, follow the steps below:

[0080] ①Under the conditions of NaOH concentration of 17.57mol / L, liquid-solid ratio of 1:1, holding time of 120min, stirring speed of 400rpm, and reaction temperature of 180°C, the scheelite concentrate was leached with NaOH to obtain the leached product, and the leached product was filtered to obtain The filtrate and the leaching slag were washed with deionized water for 3 times to obtain a washing solution, and the filtering solution and the leaching solution were combined to obtain a leaching solution containing sodium tungstate;

[0081] ② Dilute the solution obtained in step ①, and add 70 mL of deionized water to 10 mL of leaching solution containing sodium tungstate with a W concentration of 0.3 mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

A kind of synthesis of Au-doped WO from scheelite concentrate 3 The method and application of nanosheets relate to the field of semiconductor oxide gas sensors. A kind of synthesis of Au-doped WO from scheelite concentrate 3 The method of nanosheets, the method is as follows: use NaOH leaching process to convert and initially purify scheelite concentrate to obtain a leach solution containing sodium tungstate, dilute the solution into a solution with a concentration of sodium tungstate of 0.019-0.044mol / L as a precursor Body, with HAuCl 4 solution, CaCl 2 The solutions are mixed, and the mixing ratio is that the molar ratio of Au, W and Ca is 0.3%-1%:1:3-14. Au-doped WO prepared based on the method of the present invention 3 Nanosheet NO 2 Gas sensor, can achieve low concentration, even ppb level NO 2 High sensitivity, high selectivity and rapid detection of gases. Using cheap and low-pollution scheelite concentrate as the tungsten source greatly reduces the cost from the raw materials and the preparation process.

Description

technical field [0001] The invention relates to the technical field of gas sensors of semiconductor oxides, in particular to a method for synthesizing Au-doped WO with scheelite concentrate. 3 Methods and applications of nanosheets. Background technique [0002] In the past few decades, with the rapid development of economic construction and the continuous acceleration of industrialization, more and more toxic and harmful gases have been discharged into the air, causing serious air pollution and seriously endangering human physical and mental health. NO 2 It is a corrosive and highly toxic gas, mainly from the emissions of factories and motor vehicles and the high-temperature combustion of some petroleum fuels. It is the main cause of acid rain and photochemical smog, and can also cause the thinning of the ozone layer, acidification of the land and surface A series of environmental problems such as water eutrophication. Most importantly, NO 2 It is extremely harmful to h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01G41/02G01N27/12B82Y40/00
Inventor 沈岩柏李停停钟祥熙李国栋高淑玲崔宝玉魏德洲
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap