Solid polymer electrolyte and application of solid polymer electrolyte in lithium metal battery

A solid-state polymer and electrolyte technology, applied in secondary batteries, secondary battery manufacturing, secondary battery repair/maintenance, etc. , Improve the cycle performance and safety performance, the effect of high ionic conductivity

Active Publication Date: 2019-06-14
SUZHOU UNIV
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the ionic conductivity of solid-state electrolytes is relatively low, making it difficult to reach practical application levels.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid polymer electrolyte and application of solid polymer electrolyte in lithium metal battery
  • Solid polymer electrolyte and application of solid polymer electrolyte in lithium metal battery
  • Solid polymer electrolyte and application of solid polymer electrolyte in lithium metal battery

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025] This example provides a solid polymer electrolyte and its application, as follows: Dissolve tris(4-aminophenyl)amine, tris(4-formylphenyl)amine and glacial acetic acid in dioxane, put In a sealed quartz glass tube, degas under the condition of liquid nitrogen bath, seal under Ar condition, and react at 120°C. After the reaction produces a solid, purify, disperse in DMF, add 2-chloro-1,1,3-trimethoxypropane, ionize, purify and dry, the resulting solid is dispersed in an aqueous solution, add 1mol / L bistrifluoromethyl Lithium sulfonyl imide solution, anion exchange, get anion as TFSI - COF-IL material, and then immerse it in 1mol / L lithium hexafluorophosphate solution at room temperature for 12 hours, then filter, separate the solid, dry, and then use a ball mill to grind it evenly, and press it into a tablet to obtain a sheet-shaped solid electrolyte. Assembled button cell; the ratio of the amount of substances of the three (4-aminophenyl) amine, three (4-formylphenyl) ...

example 2

[0029] This example provides a solid polymer electrolyte and its application, specifically as follows: Dissolve tris(4-aminophenyl)amine, tris(4-formylphenyl)amine, and strong protonic acid fluorosulfonic acid in mesitylene , placed in a sealed quartz glass tube, degassed under liquid nitrogen bath conditions, sealed under Ar conditions, and reacted at 120°C. After the reaction generates a solid, purify, disperse in DMF, add chloroacetaldehyde dimethyl acetal, ionize, purify and dry, and the obtained solid is dispersed in an aqueous solution, add 1 mol / L lithium bistrifluoromethanesulfonimide (LiTFSI) solution, anion exchanged to obtain anion as TFSI - COF-IL material, and then immerse it in 1mol / L lithium bistrifluoromethanesulfonimide solution at room temperature for 12 hours, then filter, separate the solid, dry, and then use a ball mill to grind evenly, and press into tablets. A sheet-shaped solid electrolyte is obtained, and the battery is assembled to obtain a button ba...

example 3

[0032] This example provides a solid polymer electrolyte and its application, specifically as follows: Dissolve tris(4-aminophenyl)amine, tris(4-formylphenyl)amine and noble metal salt in N,N-dimethylformaldehyde In the amide, put it into a sealed quartz glass tube, degas it under the condition of liquid nitrogen bath, seal it under the condition of Ar, and react at 120°C. After the reaction produces a solid, purify it, disperse it in DMF, add epoxybromobutane, ionize it, purify and dry it, and disperse the obtained solid in an aqueous solution, add a 1mol / L difluorooxalate lithium borate solution, and perform anion exchange to obtain an anion as TFSI - COF-IL material, and then immerse it in 1mol / L lithium trifluoromethanesulfonate solution at room temperature for 12 hours, then filter, separate the solid, dry, and then use a ball mill to grind evenly, and press into tablets to obtain flakes The solid electrolyte is used to assemble the battery to obtain a button battery; the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a solid polymer electrolyte and application of the solid polymer electrolyte in a lithium metal battery. The solid polymer electrolyte comprises polymer matrix and lithium ionconductors formed in the polymer matrix. The polymer matrix is an ionized ether inorganic / organic hybrid frame. According to the solid polymer electrolyte and the application, through utilization ofa bottom-up self-assembly synthesis method, ionic liquid (IL) electrolyte is fixed in a COF frame. The ionic liquid can dissolve lithium salt. Transmission channels of lithium ions are provided through segment movement. Through utilization of the stable COF frame, the polymer electrolyte has relatively high mechanical performance and heat stability. The COF-IL solid polymer electrolyte disclosed by the invention has good lithium ion conductivity, heat stability and mechanical stability. Safety problems such as battery burning or even explosion resulting from liquid leakage of a conventional lithium ion battery can be avoided.

Description

technical field [0001] The invention belongs to the technical field of lithium battery materials, and relates to a lithium metal battery element, in particular to a solid polymer electrolyte for a lithium metal battery. Background technique [0002] Lithium-ion batteries have become the first choice for portable electronic products, power tools and hybrid / full electric vehicles because of their advantages such as high energy density, long cycle life, low self-discharge rate, no memory effect, stable discharge voltage, fast charge and discharge, and environmental protection. Power battery material. However, when Li-ion batteries are subjected to abuse conditions such as ultra-fast charging, discharging, or overcharging, the high specific energy density of the battery usually causes an energy response that generates enormous heat. The safety risk of Li-ion batteries remains an important challenge and unsolved hurdle, especially in systems with large size and high energy densi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/0565H01M10/42H01M10/04H01M10/0525
CPCY02E60/10Y02P70/50
Inventor 严锋朱海李奇
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com