Teflon fireproof gap filling glue and preparation method thereof

A technology of Teflon and caulking adhesive, which is applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of poor high temperature stability and aging resistance, poor adhesion of asphalt pavement, and waste of manpower and material resources, etc., to achieve the effect of good bonding strength, saving manpower and material resources, and convenient operation

Inactive Publication Date: 2019-08-06
姚建珍
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the continuous improvement of people's living standards, automobiles are also becoming longer and longer, and the damage to the road surface is also increasing. Therefore, the road maintenance department must often repair the cracks and potholes on the road surface in time, but the currently used sealant There are the following problems: (1) the formula is relatively complicated; (2) the high temperature stability and aging resistance are poor, and it is easy to become brittle and crack when the temperature is low in winter, and it is not suitable for cold temperature difference areas. The adhesiveness of the road surface is not good, and it will move outward in summer; (3) when the temperature is below zero, the joint filler needs to be heated before it can be used, which causes troubles for the road maintenance department in the process of maintenance and use, and wastes manpower and material resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A Teflon fireproof caulking glue, comprising the following components (by mass percentage): 18-22% of polytetrafluoroethylene fine particles, 14-17% of phenolic resin, 8% of chlorinated polypropylene resin, polymer rubber powder 6%, talcum powder 3%, fly ash 2%, intumescent flame retardant 3.5%, heat stabilizer 2.4%, catalyst 2.2%, defoamer 1.8%, plasticizer 1.5%, foam stabilizer 1.2%, Water-based emulsion is the balance.

[0022] Further, the chlorine element content in the chlorinated polypropylene resin is 20%, and the polymer rubber powder is a redispersible rubber powder.

[0023] Further, the heat stabilizer is sodium stearyl hydrogen, the catalyst is A-1, the defoamer is a polyether defoamer, the plasticizer is dioctyl phthalate, and the foam stabilizer is a silica gel solution.

[0024] Further, the polytetrafluoroethylene fine particles are broken into polytetrafluoroethylene fine particles by using a crusher to crush the polytetrafluoroethylene solids, and th...

Embodiment 2

[0032] A Teflon fireproof caulking glue, comprising the following components (by mass percentage): 20% of polytetrafluoroethylene fine particles, 15% of phenolic resin, 9% of chlorinated polypropylene resin, 7% of polymer rubber powder, talc Powder 4%, fly ash 3%, intumescent flame retardant 4%, heat stabilizer 2.6%, catalyst 2.3%, defoamer 1.9%, plasticizer 1.6%, foam stabilizer 1.3%, water-based emulsion is the rest quantity.

[0033] Further, the chlorine element content in the chlorinated polypropylene resin is 25%, and the polymer rubber powder is a redispersible rubber powder.

[0034] Further, the heat stabilizer is sodium stearyl hydrogen, the catalyst is A-1, the defoamer is a polyether defoamer, the plasticizer is dioctyl phthalate, and the foam stabilizer is a silica gel solution.

[0035] Further, the polytetrafluoroethylene fine particles are broken into polytetrafluoroethylene fine particles by using a crusher to crush the polytetrafluoroethylene solids, and the...

Embodiment 3

[0043] A Teflon fireproof caulking glue, comprising the following components (by mass percentage): 22% of polytetrafluoroethylene fine particles, 17% of phenolic resin, 11% of chlorinated polypropylene resin, 8% of polymer rubber powder, talc 6% powder, 5% fly ash, 4.5% intumescent flame retardant, 2.8% heat stabilizer, 2.5% catalyst, 2.1% defoamer, 1.8% plasticizer, 1.4% foam stabilizer, water-based emulsion quantity.

[0044] Further, the chlorine element content in the chlorinated polypropylene resin is 30%, and the polymer rubber powder is a redispersible rubber powder.

[0045] Further, the heat stabilizer is sodium stearyl hydrogen, the catalyst is A-1, the defoamer is a polyether defoamer, the plasticizer is dioctyl phthalate, and the foam stabilizer is a silica gel solution.

[0046] Further, the polytetrafluoroethylene fine particles are broken into polytetrafluoroethylene fine particles by using a crusher to crush the polytetrafluoroethylene solids, and then dry the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a Teflon fireproof gap filling glue, which comprises, by mass, 18-22% of polytetrafluoroethylene fine particles, 14-17% of a phenol formaldehyde resin, 8-11% of a chlorinated polypropylene resin, 6-8% of polymer rubber powder, 3-6% of talc powder, 2-5% of fly ash, 3.5-4.5% of an intumescent flame retardant, 2.4-2.8% of a heat stabilizer, 2.2-2.5% of a catalyst, 1.8-2.1% ofa defoamer, 1.5-1.8% of a plasticizer, 1.2-1.4% of a foam stabilizer, and the balance of aqueous emulsion. The invention further discloses a preparation method of the Teflon fireproof gap filling glue, wherein the preparation method comprises: grinding sieving, heating stirring, sputtering film forming, and heating and cooling. According to the present invention, the Teflon fireproof gap filling glue has advantages of reasonable formula, good bonding strength, good elasticity, aging resistance, oxidation resistance, high-temperature resistance, low-temperature resistance, brittleness resistance, cracking resistance and long service life; and the preparation method is simple, and has characteristics of convenient operation, low requirements on equipment, manpower saving, material resource saving and good promotion effect.

Description

technical field [0001] The invention relates to the technical field of Teflon materials, in particular to a Teflon fireproof caulking glue and a preparation method thereof. Background technique [0002] With the continuous improvement of people's living standards, automobiles are also becoming longer and longer, and the damage to the road surface is also increasing. Therefore, the road maintenance department must often repair the cracks and potholes on the road surface in time, but the currently used sealant There are the following problems: (1) the formula is relatively complicated; (2) the high temperature stability and aging resistance are poor, and it is easy to become brittle and crack when the temperature is low in winter, and it is not suitable for cold temperature difference areas. The adhesiveness of the road surface is not good, and it will move outward in summer; (3) when the temperature is below zero, the joint filler needs to be heated before it can be used, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J127/18C09J11/04C09J11/06C09J11/08
CPCC08L2201/02C08L2201/08C08L2205/035C09J11/04C09J11/06C09J11/08C09J127/18C08L61/06C08L23/28C08K13/04C08K7/26C08K3/34C08K5/12
Inventor 姚建珍
Owner 姚建珍
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap