High-slump-retaining coagulation-retarding type polycarboxylate water reducing agent and preparation and application thereof

A technology of retarded polycarboxylic acid and water reducing agent, applied in the field of concrete admixtures, can solve problems such as poor slump retention, and achieve the effects of low cost, improved construction workability, and good market promotion value

Active Publication Date: 2019-08-09
深圳市五山新材料股份有限公司
View PDF10 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The technical idea of ​​the present invention is to introduce different functional monomers, synthesize polycarboxylic acid macromolecules with specific structures, and adjust the ratio of each functional monomer so that the prepared polycarboxylic acid water reducer has both long-t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-slump-retaining coagulation-retarding type polycarboxylate water reducing agent and preparation and application thereof
  • High-slump-retaining coagulation-retarding type polycarboxylate water reducing agent and preparation and application thereof
  • High-slump-retaining coagulation-retarding type polycarboxylate water reducing agent and preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Add a certain amount of acrylic acid, methyl acrylate, sodium acrylate, polyethylene glycol diacrylate, methallyl alcohol polyoxyethylene ether (HPEG, number average molecular weight 2400), acrylamide in a 500mL flask equipped with a stirrer. (AM), 2-acrylamide-2-methylpropanesulfonic acid (AMPS), 2-acrylamido-2-phenylethanesulfonic acid (AMSS) and deionized water, heated to 50 ° C, stirred to make all the raw materials Dissolve, heat up to 70°C, add initiator sodium persulfate and chain transfer agent mercaptoacetic acid dropwise, add dropwise for 3 hours, keep warm for 1 hour, cool to room temperature after the reaction, and neutralize with NaOH solution to obtain the product polycarboxylic acid Water reducing agent.

[0031] Wherein the amount of each raw material is 0.5mol acrylic acid, 0.2mol methyl acrylate, 0.1mol sodium acrylate, 0.1mol polyethylene glycol (PEG400) diacrylate, 0.05mol methallyl alcohol polyoxyethylene ether (HPEG), 0.3mol Acrylamide (AM), 0.1mo...

Embodiment 2

[0033] The unsaturated polyether macromonomer was changed to allyl polyoxyethylene ether (APEG, number average molecular weight 1800), and the others were the same as in Example 1.

Embodiment 3

[0035] The unsaturated polyether macromonomer was changed to isopentenol polyoxyethylene ether (TPEG, number average molecular weight 2500), and the others were the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-slump-retaining coagulation-retarding type polycarboxylate water reducing agent and a preparation method and application thereof. The water reducing agent is prepared from, by molar part, 10-30 parts of small-molecule unsaturated carboxylic acid, 3-8 parts of ester of small-molecule unsaturated carboxylic acid, 1-5 parts of salt of small-molecule unsaturated carboxylic acid, 2-6 parts of polyethylene glycol diacrylate, 1-5 parts of an unsaturated polyether macromonomer, 8-20 parts of an acrylamide monomer, an initiator and a chain transferring agent, wherein theacrylamide monomer is a group consisting of three monomers including acrylamide (AM), 2-acrylamide-2-methylpropanesulfonic acid (AMPS) and 2-acryloylamino-2-phenylethanesulfonic acid (AMSS). The molecular structure of the water reducing agent is designed according to the construction demands for workability and slump retaining performance, and the high-slump-retaining coagulation-retarding type polycarboxylate water reducing agent with excellent comprehensive performance is finally obtained. During construction, a high water reducing rate can be achieved by applying a low dosage of the water reducing agent, the construction can be guaranteed, the slump retaining performance is excellent, the slump is basically not changed within 3 hours, and the water reducing agent has wide applicabilityin concrete construction.

Description

technical field [0001] The invention belongs to the field of concrete admixtures, and in particular relates to a polycarboxylate water reducer and its preparation and application. [0002] Background technique: [0003] With the rapid development of my country's economy and the improvement of construction levels, the rapid rise of high-speed railways, highway bridges, traffic tunnels, urban rail transit, and large buildings, concrete structures are becoming large, complex, high-rise, and have diverse construction conditions. Therefore, higher requirements are put forward for the strength, construction performance and durability of concrete, and almost all of them require the use of pumped concrete, which also maintains a better performance of concrete in the long-distance pumping process. Fluidity and slump retention, otherwise it will cause the slump loss of the freshly mixed concrete and make it impossible to construct, which will cause great economic losses to the constructi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F283/06C08F220/06C08F220/14C08F220/56C08F220/58C08F222/14C08F4/30C08F2/38C04B24/26C04B103/30
CPCC04B24/2694C04B2103/302C08F2/38C08F4/30C08F283/065C08F222/102
Inventor 马清浩
Owner 深圳市五山新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap