Biomass based composite material with high degradability for non-woven fabric and processing technology of biomass based composite material

A composite material and processing technology, applied in textiles and papermaking, conjugated synthetic polymer rayon, conjugated rayon, etc., can solve the problem of poor heat resistance, high production cost of polylactic acid, and inability to popularize polylactic acid, etc. problems, to achieve the effect of improving flexibility, improving generalizability, heat resistance and flexibility

Active Publication Date: 2019-08-16
山东莱芬无纺布有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, due to the high production cost of polylactic acid in traditional polylactic acid products, polylactic acid cannot be popularized, and polylactic acid products have poor heat resistance a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A biomass-based composite material with high degradability for non-woven fabrics, mainly comprising the following raw materials in parts by weight: 8 parts of polylactic acid, 6 parts of epoxy soybean oil, 2 parts of zinc chloride, 16 parts of oxidized starch, 3 parts of polyallylamine hydrochloride and 8 parts of modified sodium alginate;

[0036] A processing technology of a highly degradable non-woven biomass-based composite material, the processing technology of the highly degradable non-woven biomass-based composite material mainly includes the following steps:

[0037] (1) Mix sodium alginate and water at a mass ratio of 1:55, and add orthoethyl silicate 4 times the mass of sodium alginate and anhydrous ethyl silicate 10 times the mass of sodium alginate to the mixture of sodium alginate and water For ethanol, stir and mix for 30min at a temperature of 30°C and a speed of 300r / min, then add ammonia water 25 times the mass of sodium alginate to the mixture of sodiu...

Embodiment 2

[0045] A biomass-based composite material with high degradability for non-woven fabrics, mainly comprising the following raw materials in parts by weight: 8 parts of polylactic acid, 6 parts of epoxy soybean oil, 2 parts of zinc chloride, 16 parts oxidized starch and 8 parts modified sodium alginate;

[0046] A processing technology of a highly degradable non-woven biomass-based composite material, the processing technology of the highly degradable non-woven biomass-based composite material mainly includes the following steps:

[0047] (1) Mix sodium alginate and water at a mass ratio of 1:55, and add orthoethyl silicate 4 times the mass of sodium alginate and anhydrous ethyl silicate 10 times the mass of sodium alginate to the mixture of sodium alginate and water For ethanol, stir and mix for 30min at a temperature of 30°C and a speed of 300r / min, then add ammonia water 25 times the mass of sodium alginate to the mixture of sodium alginate and water, and mix at a temperature ...

Embodiment 3

[0055] A biomass-based composite material with high degradability for non-woven fabrics, mainly comprising the following raw materials in parts by weight: 8 parts of polylactic acid, 6 parts of epoxy soybean oil, 2 parts of zinc chloride, 16 parts of oxidized starch, 3 parts of polyallylamine hydrochloride and 8 parts of sodium alginate;

[0056] A processing technology of a highly degradable non-woven biomass-based composite material, the processing technology of the highly degradable non-woven biomass-based composite material mainly includes the following steps:

[0057] (1) Mix sodium alginate and silane coupling agent KH-550 at a mass ratio of 12:1, and add 3 times the mass of silane coupling agent KH-550 to the mixture of sodium alginate and silane coupling agent KH-550 Water and calcium chloride 1 times the mass of silane coupling agent KH-550 were stirred and mixed for 2 hours at a temperature of 40°C and a rotation speed of 250r / min, filtered and dried;

[0058] (2) M...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a biomass based composite material with high degradability for non-woven fabric and a processing technology of the biomass based composite material, and belongs to the technical field of biodegradable polymer composite materials. The processing technology comprises steps as follows: after sodium alginate and nano-silica are mixed, the mixture is processed by a silane coupling agent KH-550, and modified sodium alginate is prepared; then, oxidized starch and polyallylamine hydrochloride are subjected to a mixed reaction, the modified sodium alginate is added, a stirring reaction is performed, and an additive is prepared; polylactic acid and epoxidized soybean oil are mixed, a catalyst and the additive are added, mixed banburying and pelletizing are performed, and thebiomass based composite material with high degradability for the non-woven fabric is obtained. The biomass based composite material with high degradability for the non-woven fabric has better heat resistance, excellent flexibility and higher degradability and is suitable for preparing the non-woven fabric.

Description

technical field [0001] The invention relates to the technical field of composite materials for non-woven fabrics, in particular to a high-degradability biomass-based composite material for non-woven fabrics and its processing technology. Background technique [0002] With the advancement of science and technology and the development of human civilization, polymer material products, such as plastic bags, lunch boxes, medical and a series of plastic products in daily life, are constantly being produced and become waste. [0003] Since the beginning of the 20th century, a large number of applications of synthetic polymer materials have caused serious environmental pollution, and the search and application of new environmentally friendly polymer materials has received extensive attention from all over the world. In this situation, biodegradable polymer materials are developing rapidly. Practice has proved that biodegradable polymer materials are different from general synthetic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F8/14D01F8/18D01F1/10
CPCD01F8/14D01F8/18D01F1/10C08L3/10C08K2003/168C08K2201/011C08L2205/035C08L2201/06C08L2201/08C08L2312/00C08L2203/12C08L67/04C08L91/00C08L39/00C08L5/04C08K3/16C08K9/06C08K3/36
Inventor 卢定华
Owner 山东莱芬无纺布有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap