Preparation method for hydrophilicity-hydrophobicity controllable fluorescence probe and application thereof

A hydrophobic and hydrophilic technology, used in fluorescence/phosphorescence, chemical instruments and methods, luminescent materials, etc., can solve the problems of no preparation of nanomaterials, adverse effects on organisms, complex preparation process, etc., and achieve good applications Promising effect, low cytotoxicity, simple preparation process

Active Publication Date: 2019-10-11
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] CN105418947A discloses a program-controlled assembled fluorescent polymeric vesicle and its preparation method, using choline diyne and polyethylene glycol diyne as starting materials to construct dynamic micelles, and then using butyrylcholine and choline An enzymatic reaction occurs between the diynes, and the diynoic acid and polyethylene glycol diyne produced by the enzymatic reaction can form dynamic vesicles; the preparation process of this method is relatively complicated and involves many substances, which may cause damage to the organism. Negative Effects
[0006] CN103920433A discloses a kind of inorganic nanocrystalline vesicular microsphere and its photochemical synthesis method, the method is assembled in a solvent by irradiating inorganic nanocrystals modified by mercapto functional groups to obtain vesicular microspheres, but this method requires prepared nanocrystals For the reaction, the microreactor does not play the role of preparing nanomaterials, and the reaction steps are cumbersome and cannot be controlled to achieve the effect of hydrophilic-hydrophobic transformation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for hydrophilicity-hydrophobicity controllable fluorescence probe and application thereof
  • Preparation method for hydrophilicity-hydrophobicity controllable fluorescence probe and application thereof
  • Preparation method for hydrophilicity-hydrophobicity controllable fluorescence probe and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] In this example, the hydrophilicity and hydrophobicity control of fluorescent vesicles and fluorescent micelles are realized by the following methods

[0068] (1) Mix nonanoic acid with water, the stirring speed is 100rpm, and the stirring time is 5min to obtain a nonanoic acid aqueous solution with a concentration of 60mM, and then carry out light pretreatment, the light wavelength is 600nm, the light time is 5h, and the reaction is carried out under stirring. The stirring speed is 500rpm, and the stirring time is 5h. After the reaction is completed, there is no separation, and then the rotary steaming is carried out. The rotary steaming temperature is 50°C, and the rotary steaming time is 2h. The ratio (volume ratio) is 2:1, the oscillation speed is 100rpm, the oscillation time is 6h, and the standing time is 20h, and hydrophilic fluorescent vesicles are obtained in the water intake system;

[0069] (2) The aqueous solution of nonanoic acid was not subjected to light ...

Embodiment 2

[0073] In this example, the hydrophilicity and hydrophobicity control of fluorescent vesicles and fluorescent micelles are realized by the following methods

[0074] (1) Mix linoleic acid with water, the stirring speed is 1000rpm, and the stirring time is 1min to obtain an aqueous solution of linoleic acid with a concentration of 140mM, and then carry out light pretreatment, the light wavelength is 800nm, and the light time is 12h. Reaction, stirring speed is 800rpm, stirring time 11h, after the completion of the reaction without any separation, then carry out vacuum distillation, the temperature is 60 ℃, time 3h, then add water and shake and stand for separation, the ratio of adding water to the product after distillation ( The volume ratio) is 4:1, the oscillation speed is 200rpm, the oscillation time is 6h, and the resting time is 20h, and hydrophilic fluorescent vesicles are obtained in the water intake system;

[0075] (2) The linoleic acid aqueous solution was not subjec...

Embodiment 3

[0078] In this example, the hydrophilicity and hydrophobicity control of fluorescent vesicles and fluorescent micelles are realized by the following methods

[0079] (1) Mix 2-oxooctanoic acid with water, the stirring speed is 100rpm, and the stirring time is 5min to obtain a 2-oxooctanoic acid aqueous solution with a concentration of 120mM, and then perform light pretreatment, the light wavelength is 300nm, and the light time is 5h , the reaction was carried out under stirring, the stirring speed was 500rpm, the stirring time was 5h, after the reaction was completed without any separation, then rotary steaming was carried out, the rotary steaming temperature was 50°C, the rotary steaming time was 2h, then water was added to vibrate and stand for separation, and water was added The ratio (volume ratio) to the product after rotary evaporation is 1:1, the oscillation speed is 100rpm, the oscillation time is 6h, and the standing time is 20h, and the water-taking system part is obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method for a hydrophilicity-hydrophobicity controllable fluorescence probe and an application thereof. The method comprises the following steps: using an amphiphilic molecule as a raw material, and controlling hydrophilicity-hydrophobicity of a fluorescence vesicle and a fluorescence micelle through on / off of illumination. The provided method is capable of realizing change of the hydrophilicity-hydrophobicity of solution through controlling the on / off of the illumination, green and simple in process, easy to operate, and convenient for controlling an overall process, wherein nature and morphology of the fluorescence vesicle and the fluorescence micelle are controllable, and the obtained fluorescence vesicle and fluorescence micelle can enter a cell nucleus for imaging, and have good application prospect in a photoelectric material, bioimaging, a diagnostic sensor, a drug carrying material, a catalytic material or a water treatment adsorption and degradation material.

Description

technical field [0001] The invention belongs to the field of nanomaterials, and relates to a method for preparing a fluorescent probe with controllable hydrophilicity and hydrophobicity and its application, in particular to a method for controlling the hydrophilicity and hydrophobicity of fluorescent vesicles and fluorescent micelles and its application. Background technique [0002] Due to their good biocompatibility, biodegradability, low toxicity and amphiphilicity, the synthesis of fluorescent vesicles and fluorescent micelles as probes has attracted great attention and has been widely used in drug delivery, micro / nano reactions devices, carriers, sensors, and templates for nanomaterial synthesis. [0003] The current methods for synthesizing fluorescent vesicles and micelles include: incorporating fluorescent dyes, AIE molecules into or encapsulating vesicle / micelle skeletons or prefabricated vesicle / micelle voids and fluorescent vesicles induced by FCN. For example, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/02C09K11/65G01N21/64
CPCC09K11/025C09K11/65G01N21/64
Inventor 赵赫代琴曹宏斌
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products