A kind of core-shell structure heparin-like microsphere based on graphene oxide grafted urease and its preparation method and application

A technology of ene-grafted urease and core-shell structure, applied in the field of heparin-like microspheres with core-shell structure and its preparation, can solve problems such as poor blood compatibility, achieve inhibition of complement activation and contact activation, and good blood compatibility , the effect of prolonging the coagulation time

Active Publication Date: 2021-08-31
SICHUAN UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, graphene oxide has poor blood compatibility, which will cause negative effects when it comes into direct contact with blood, and free two-dimensional nanosheets cannot be easily separated from blood.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of core-shell structure heparin-like microsphere based on graphene oxide grafted urease and its preparation method and application
  • A kind of core-shell structure heparin-like microsphere based on graphene oxide grafted urease and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A preferred embodiment of the present invention provides a method for preparing heparin-like microspheres with a core-shell structure based on graphene oxide grafted with urease. The specific steps are as follows:

[0036] S1. Core layer preparation: disperse graphene oxide in PBS buffered saline solution with a pH of 7.4-7.6 to obtain a solution concentration of 1mg / mL; add 0.01g NHS and 0.015g EDC and mix well, then add 0.2g urease, React at 4°C for 12 hours to obtain a urease-immobilized graphene oxide solution, which should be stored at 4°C before use;

[0037] S2. Shell layer preparation: Dissolve 8g PES in 88.8g DMAC to obtain a uniform solution, then add 0.96g AA, 0.72g AMPS, 0.04g AIBN and 0.06g MBA, react under nitrogen atmosphere at 75°C for 12h, cool to room temperature to obtain a heparan-like polymer solution;

[0038] S3. Preparation of microspheres: drop the urease-immobilized graphene oxide solution prepared in step S1 into the heparan-like polymer solu...

Embodiment 2

[0040] A preferred embodiment of the present invention provides a method for preparing heparin-like microspheres with a core-shell structure based on graphene oxide grafted with urease. The specific steps are as follows:

[0041] S1. Core layer preparation: disperse graphene oxide in PBS buffered saline solution with pH 7.4-7.6 to obtain a solution concentration of 1 mg / mL; add 0.01g NHS and 0.015g EDC and mix well, then add 0.18g urease, React at 4°C for 12 hours to obtain a urease-immobilized graphene oxide solution, which should be stored at 4°C before use;

[0042] S2. Shell layer preparation: Dissolve 8g PES in 89g DMAC to obtain a uniform solution, then add 0.97g AA, 0.73g AMPS, 0.04g AIBN and 0.06g MBA, react at 75°C for 12h under nitrogen atmosphere, and cool to room temperature , to obtain a heparan-like polymer solution;

[0043] S3. Preparation of microspheres: drop the urease-immobilized graphene oxide solution prepared in step S1 into the heparan-like polymer solut...

Embodiment 3

[0045] A preferred embodiment of the present invention provides a method for preparing heparin-like microspheres with a core-shell structure based on graphene oxide grafted with urease. The specific steps are as follows:

[0046] S1. Core layer preparation: disperse graphene oxide in PBS buffered saline solution with pH of 7.4-7.6 to obtain a solution concentration of 1 mg / mL; add 0.01g NHS and 0.017g EDC and mix well, then add 0.2g urease, React at 4°C for 12 hours to obtain a urease-immobilized graphene oxide solution, which should be stored at 4°C before use;

[0047] S2. Shell layer preparation: Dissolve 8g PES in 90g DMAC to obtain a uniform solution, then add 0.97g AA, 0.75g AMPS, 0.04g AIBN and 0.07g MBA, react at 75°C for 12h under nitrogen atmosphere, and cool to room temperature , to obtain a heparan-like polymer solution;

[0048] S3. Preparation of microspheres: drop the urease-immobilized graphene oxide solution prepared in step S1 into the heparan-like polymer s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a heparin-like microsphere with a core-shell structure based on graphene oxide grafted with urease and its preparation method and application. The urease is immobilized on the surface to obtain a core solution; the heparan-like polymer solution is prepared by an in-situ cross-linking polymerization method to obtain a shell solution; the core-shell microspheres are obtained by a reverse-forward phase inversion method. The invention can efficiently remove urea in hemoperfusion, relieve pain of patients, and can also be used for regeneration of dialysate in hemodialysis, providing technical support for wearable artificial kidney.

Description

technical field [0001] The invention belongs to the field of blood purification, and in particular relates to a heparin-like microsphere with a core-shell structure based on graphene oxide grafted with urease and a preparation method and application thereof. Background technique [0002] Chronic kidney disease (CKD) is a worldwide health problem that not only causes kidney failure but also complications such as cardiovascular disease (CVD). For CKD patients, excess uremic toxins accumulate in the body and cannot be effectively excreted. Hemoperfusion is one of the common methods to remove uremic toxins. Although activated carbon, zeolite and other adsorbents have been developed to adsorb urea, due to the high solubility and stability of urea in aqueous solution, no effective physical adsorption materials have been found to remove urea. [0003] Urease is an aminohydrolase whose active site contains two nickel(II) ions, which can catalyze the decomposition of urea into ammo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/24B01J20/28B01J20/30B01D15/08
CPCB01D15/08B01J20/24B01J20/28021
Inventor 何超张珏周密赵长生李明远罗一晏冰清郝媛媛刘尚宇
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap