Preparation method of a wood-based biomimetic bone scaffold material

A scaffold material, bionic bone-based technology, applied in the field of bionic bone scaffolds, to achieve the effects of good cell compatibility, increased porosity, and wide sources

Active Publication Date: 2022-02-08
ZHEJIANG FORESTRY UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the defects of existing bone scaffold materials, the present invention provides a preparation method of a wood-based bionic bone scaffold material, which uses the mechanical properties and biocompatibility of lignocellulose and the osteoconductivity of hydroxyapatite to obtain a wood-based bionic bone scaffold material. Biomimetic Bone Scaffold Materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of a wood-based biomimetic bone scaffold material
  • Preparation method of a wood-based biomimetic bone scaffold material
  • Preparation method of a wood-based biomimetic bone scaffold material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] (1) Soak the wood fiber in the alkali solution prepared with 0.01mol / L sodium hydroxide solution and 0.01mol / L sodium sulfite solution according to the mass ratio of 1:1, and then perform mechanical grinding at a speed of 2800r / min Treat for 2 hours to prepare fiber pulp with a mass fraction of 10%;

[0050](2) In a water bath at 40°C, chitosan is dissolved in pure water to prepare a chitosan polymer solution with a mass fraction of 10%, and the fiber pulp with a mass fraction of 10% obtained in step 1 and 10% mass fraction The chitosan polymer solution was mixed at a mass ratio of 1:1, stirred evenly, and kept magnetically stirred in a water bath at 40°C for 0.5h to obtain a mixed solution;

[0051] (3) Add hydroxyapatite to the mixed solution obtained in step 2, and carry out magnetic stirring at 40°C in a water bath for 0.5h to obtain a scaffold material precursor mixed solution, wherein the amount of hydroxyapatite added is the same as that of chitosan and wood The...

Embodiment 2

[0056] (1) Soak the wood fiber in the alkali solution prepared with 0.01mol / L sodium hydroxide solution and 0.01mol / L sodium sulfite solution according to the mass ratio of 1:2, and then perform mechanical grinding at a speed of 2800r / min Treat for 2 hours to prepare fiber pulp with a mass fraction of 10%;

[0057] (2) In a water bath at 50°C, chitosan is dissolved in pure water to prepare a mass fraction of 10% chitosan macromolecule solution, and the fiber pulp with a mass fraction of 10% obtained in step 1 and 10% of the mass fraction The chitosan polymer solution was mixed and stirred evenly at a mass ratio of 1:2, and kept magnetically stirred in a water bath at 50°C for 0.5h to obtain a mixed solution;

[0058] (3) Add hydroxyapatite to the mixed solution obtained in step 2, and carry out magnetic stirring at 40°C in a water bath for 0.5h to obtain a scaffold material precursor mixed solution, wherein the amount of hydroxyapatite added is the same as that of chitosan and...

Embodiment 3

[0063] (1) Soak the wood fiber in the alkali solution prepared according to the mass ratio of 2:1 0.01mol / L sodium hydroxide solution and 0.01mol / L sodium sulfite solution, and then perform mechanical grinding at a speed of 2800r / min Treat for 2 hours to prepare fiber pulp with a mass fraction of 20%;

[0064] (2) In a water bath at 60°C, chitosan is dissolved in pure water to prepare a chitosan polymer solution with a mass fraction of 20%, and the fiber pulp with a mass fraction of 20% obtained in step 1 and 20% of the mass fraction The chitosan polymer solution was mixed and stirred evenly at a mass ratio of 1:1, and kept magnetically stirred in a water bath at 60°C for 0.5h to obtain a mixed solution;

[0065] (3) Add hydroxyapatite to the mixed solution obtained in step 2, and stir magnetically at 60° C. in a water bath for 0.5 h to obtain a scaffold material precursor mixed solution, wherein the amount of hydroxyapatite added is the same as that of chitosan and wood fiber...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
modulusaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a wood-based bionic bone support material, which belongs to the field of bionic bone support. The method comprises: taking wood fibers, soaking them in alkaline solution, and mechanically grinding to obtain fiber pulp; mixing the fiber pulp with polysaccharide polymer solution and stirring evenly to obtain a mixed solution; adding hydroxyapatite to the mixed solution , magnetically stirred in a water bath to obtain a scaffold material precursor mixture; freeze the scaffold material precursor mixture, and then freeze-dry to obtain an airgel scaffold; cross-link the airgel scaffold with glutaraldehyde solution, and then use ethanol and Rinse with deionized water; freeze the scaffold material after rinsing, and then freeze-dry to obtain the wood-based biomimetic bone scaffold material. The present invention prepares a wood-based biomimetic bone scaffold material with a three-dimensional porous structure through a cycle freeze-drying technique. The scaffold material not only has no cytotoxicity, but also has high compressive strength, and mouse osteoblasts can adhere to the scaffold material. growth, meeting the requirements of bone scaffold materials.

Description

technical field [0001] The invention relates to a preparation method of a wood-based bionic bone support material, belonging to the technical field of bionic bone support. Background technique [0002] Bone tissue is composed of ordered collagen, oriented hydroxyapatite and water. Bone tissue closely combines the organic bone matrix structure and the inorganic bone salt framework structure to form an inorganic / organic composite material, thereby meeting the functional requirements of biology and mechanics. When the bone tissue is removed due to congenital, traumatic and tumor deformities, a large area of ​​bone defect is formed. It cannot heal through its own repair ability, so it is necessary to fill the defect with suitable bone repair materials through bone grafting to facilitate the healing and growth of bone tissue. [0003] Hydroxyapatite is the main component of inorganic bone salt and has good biocompatibility, bioactivity and osteoconductivity. Nano-scale hydroxy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/46A61L27/56A61L31/12A61L31/14
CPCA61L27/56A61L31/146A61L27/46A61L31/127A61L2430/02A61L2400/12C08L1/00
Inventor 孙庆丰党宝康王超陈逸鹏
Owner ZHEJIANG FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com