Resveratrol-based bio-based carbon fiber composite material and preparation method thereof

A fiber composite material and a technology of resveratrol, which are applied in the field of bio-based carbon fiber composite materials based on resveratrol and their preparation, can solve the problems of long curing cycle and high curing temperature of carbon fiber composite materials, and achieve shortening curing time, The effect of lowering curing temperature and increasing speed

Inactive Publication Date: 2020-05-08
CHANGCHUN UNIV OF TECH
View PDF10 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problems of long curing period and high curing temperature of carbon fiber composite materials, and provide a bio-based carbon fiber composite material based on resveratrol and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resveratrol-based bio-based carbon fiber composite material and preparation method thereof
  • Resveratrol-based bio-based carbon fiber composite material and preparation method thereof
  • Resveratrol-based bio-based carbon fiber composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] According to the present invention, the epoxy resin with the structure shown in formula 1 is a resveratrol-based epoxy resin, and its preparation method preferably includes:

[0046] Add resveratrol and ECH to a four-neck round bottom flask equipped with mechanical stirring, constant pressure flow pump, thermometer and reflux device, the molar ratio of resveratrol and ECH is 1:6; and make it stir at 110 °C for 2 hour, the mixture was obtained, then, aqueous sodium hydroxide solution (20% w / w, 50mL) was added dropwise to the above mixture with a constant flow pump, and this process was controlled at 2-3 hours, and then the The mixture was reacted for 4 hours. In order to ensure that all phenolic hydroxyl groups were converted into glycidyl ether, 2 g of ferric chloride was added dropwise to the mixture, and the reaction was stopped when no color change was observed in the polymerization system, and then the reaction system was cooled to room temperature. The suspension w...

Embodiment 1

[0052] The preparation of embodiment 1 resveratrol-based epoxy resin

[0053] Add resveratrol (22.8g, 0.1mol) and ECH (55.5g, 0.6mol) in the 500mL four-neck round-bottom flask of assembly mechanical stirring, constant pressure flow pump, thermometer and reflux device, and make it at 110 ℃ Stir for 2 hours. Then, an aqueous sodium hydroxide solution (20% w / w, 50 mL) was added dropwise into the mixture at 110° C. with a constant flow pump, and the process was controlled for about 2 hours. The mixture was reacted at 110 °C for 4 h with vigorous stirring. In order to ensure that all the phenolic hydroxyl groups were converted into glycidyl ether, 2 g of ferric chloride was added dropwise to the mixture, and the reaction was stopped when no color change was observed in the polymerization system, and then the reaction system was cooled to room temperature. The suspension is diluted with about 50 ml of dichloromethane and the organic phase is extracted. After removing the upper aq...

Embodiment 2

[0055] The preparation of embodiment 2 carbon fiber composite material

[0056] (1) Take 58g of resveratrol-based epoxy resin, add 19g of DEDDM curing agent according to the proportion, stir and mix evenly, and then put it into a vacuum oven to remove the air bubbles in the resin.

[0057] (2) Cut 3k carbon fiber cloth with a strength level of T300 to make 3 carbon fiber boards, lay 12 layers of carbon fiber cloth on each board, cut 36 layers in total, and the size of each layer of carbon fiber cloth is 150×120mm; lay it flat in a vacuum bag;

[0058] (3) With the assistance of a vacuum pump, introduce the resin into 115g of carbon fiber, and keep the seal in a vacuum state.

[0059] (4) Put it in an oven, adjust the temperature to 75°C / 30min+110°C / 30min+160°C / 30min to complete the curing, remove the vacuum bag, take out the cured carbon fiber sample, and cut it into a sample of 120mm×12.5mm×3mm strips for bending tests.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a resveratrol-based bio-based carbon fiber composite material and a preparation method thereof, and belongs to the field of carbon fiber composite materials. The composite material comprises 25-35 parts of bio-based epoxy resin, 55-70 parts of a carbon fiber material and 5-10 parts of a curing agent, wherein the bio-based epoxy resin is resveratrol-based epoxy resin or a mixture of the resveratrol-based epoxy resin and bisphenol A type epoxy resin. The resveratrol-based epoxy resin has high polymerization reaction activity, the reaction conditions for preparing the carbon fiber composite material by taking the carbon fiber as a resin matrix are mild, the curing time is effectively shortened, and the curing temperature is reduced; resveratrol is a polyphenol compoundextracted from vegetable tannin, residual monomers are nontoxic, raw materials are renewable, triphenolic hydroxyl groups in the structure of resveratrol can be condensed with epoxy chloropropane to form a polyfunctional epoxy prepolymer, and many crosslinking active sites are provided for resin curing, so the crosslinking density, mechanical properties and heat resistance of a cured product are improved.

Description

technical field [0001] The invention belongs to the field of carbon fiber composite materials, and in particular relates to a resveratrol-based bio-based carbon fiber composite material and a preparation method thereof. Background technique [0002] Carbon fiber composite material (CFRP) is an advanced composite material with high specific strength and high specific modulus, which is widely used in aerospace, transportation and medical equipment and other fields. For the composite material manufacturing industry, in order to increase production, reduce energy consumption, and thus control costs, an effective method is to shorten the manufacturing cycle from tens of hours or minutes to hours or minutes. In the fast curing system, the photoinitiation is usually faster, but the thermal initiation is easier, which can realize the complete curing of the epoxy system, and is suitable for curing thicker or complex-shaped products. Reductions in product cycle times in general indus...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L63/02C08K7/00C08K7/06C08G59/38
CPCC08K7/00C08K7/06C08L63/00C08G59/38C08L2205/025C08L2201/08
Inventor 尚垒徐子策敖玉辉庄海林王红军赵宏武杜巍峰马岩石飞
Owner CHANGCHUN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap