Method for performing zinc enrichment recovery through rotary kiln

A rotary kiln and enrichment technology, applied in rotary drum furnace, process efficiency improvement, furnace type, etc., can solve the problems of low content of crude zinc oxide in zinc-containing dust, low material metallization rate, and low production capacity of rotary kiln. , to achieve the effect of improving the utilization rate of heat energy, improving the recovery rate and reducing the bonding

Active Publication Date: 2020-10-02
UNIV OF SCI & TECH BEIJING
View PDF14 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantages of this method are: there are problems such as low production capacity of the rotary kiln and easy ring formation, low content of crude zinc oxide in the collected zinc-containing dust, and low dezincification rate.
However, the shortcomings of this method are: there are defects such as low dezincification rate, low metallization rate of the reduced material, and low production capacity of the rotary kiln.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for performing zinc enrichment recovery through rotary kiln
  • Method for performing zinc enrichment recovery through rotary kiln
  • Method for performing zinc enrichment recovery through rotary kiln

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] The raw material is low-grade iron ore, and the method of zinc enrichment and recovery using a rotary kiln:

[0054] S1. Raw material preparation: use anthracite and coke powder with a mass ratio of 1:1 as reduced coal, mix them with iron ore and metallurgical dust to evenly pelletize and dry them, and obtain kiln raw materials with an average particle size distribution of 5-15mm; among them, The ratio of the reduced coal, the iron ore and the metallurgical dust is 25%: 35%: 40%; the ash content in the reduced coal is 8%, and the reflow temperature of the ash is greater than 1300°C .

[0055] S2. Calcination process: preheat the kiln-entry raw material prepared in step S1 to 200°C, and then send it into the kiln tail of the variable-diameter rotary kiln. The filling rate of the variable-diameter rotary kiln is 10%; the input amount of the kiln raw material It is 300t / d; and at the end of the kiln, with a blower pressure of 150KPa, pulverized coal and oxygen-enriched ai...

Embodiment 2-3

[0067] The difference from Example 1 lies in that the concentration of oxygen in the oxygen-enriched air is set differently, and other steps are the same as those in Example 1, which will not be repeated here.

[0068]

[0069] The present invention adopts oxygen-enriched air to carry out combustion-supporting, compared with the conventional air in comparative example 2 (oxygen concentration is 21%), can reduce combustion-supporting gas blowing amount, and then make flue gas emission greatly reduce, soot product (coarse zinc oxide ) grade has been improved. At the same time, due to the increase of oxygen concentration, the combustion rate is also improved, which can enhance the processing capacity of rotary kiln reduction roasting, make the recovery of iron ore sufficient, the recovery grade and recovery rate are improved, and the consumption of fuel is greatly reduced .

Embodiment 4-7

[0071] The difference from Example 1 is that the filling rate of the rotary kiln and the input amount of raw materials into the kiln are set differently, and the other steps are the same as in Example 1, and will not be repeated here.

[0072]

[0073] When the residence time of the material is constant, the increase of the filling rate of the rotary kiln and the input of raw materials into the kiln can increase the output of the rotary kiln, but due to the thickening of the material layer, the movement of the material is restricted, so it is unfavorable for the turning and roasting of the material. If the filling rate and input amount are too small, the production capacity of the equipment will not be effectively utilized, and the production cost will also be increased.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for performing zinc enrichment recovery through a rotary kiln. A preheated input raw material is sent to a kiln tail of a diameter-variable rotary kiln, pulverized coaland oxygen-enriched air are blown into the kiln tail, and roasting reaction is executed for 80-100 minutes; under the action of a kiln head exhaust fan, a flowing direction of smoke generated by theroasting reaction keeps consistent with a moving direction of the input raw material, and the smoke and the raw material both move from the kiln tail to the kiln head; roasted ore is collected, and iron ore concentrate is obtained through ore grinding and magnetic separation; the smoke exhausted by the exhaust fan is collected and purified, a dust collection system is enabled to collect zinc-containing dust, the zinc-containing dust is mixed with the input raw material for pelleting, a mixed input raw material is obtained, the mixed input raw material is sent into the diameter-variable rotarykiln, a roasting working procedure and a zinc-containing dust collection working procedure are executed circularly, and thus, circular enrichment of the zinc is realized; after zinc content in the smoke reaches more than 10%, the zinc-containing dust in the smoke is directly collected, and zinc recovery is executed through an acid leaching technology. The method can effectively improve recovery rate of iron and zinc, prevent ring forming of the rotary kiln and be efficient and energy-saving.

Description

technical field [0001] The invention relates to the technical field of metallurgy and mineral processing, in particular to a method for enriching and recovering zinc by utilizing a rotary kiln. Background technique [0002] Iron ore is an important raw material in the development of the iron and steel industry and plays an important role in the development of my country's national economy. With the rapid development of my country's iron and steel industry, the demand for iron ore continues to grow. In order to improve the grade and comprehensive recycling rate of iron ore, iron ore usually needs to be calcined and processed. At present, the widely used It is a rotary kiln-magnetic separation separation process based on reduced coal-based direct reduction. The process combines roasting, beneficiation and smelting in one process, eliminating the need for high energy consumption and high pollution processes such as beneficiation, sintering, and pelletizing, while shortening the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B7/02C22B1/24C22B1/216C22B19/20C22B5/10C22B1/243
CPCC22B1/216C22B1/2406C22B1/243C22B5/10C22B7/007C22B7/02C22B19/22Y02P10/20
Inventor 张建良徐润生刘征建王广伟
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com