A transmission electron microscope microgrid based on heavy ion irradiation and its preparation method

A technology of transmission electron microscopy and heavy ions, applied in the manufacture of electrode systems, manufacture of discharge tubes/lamps, circuits, etc., can solve problems such as sample drift, jumping, difficult large-scale preparation, poor thermal conductivity, etc., to avoid measurement errors and improve The effect of testing accuracy and improving accuracy

Active Publication Date: 2022-03-25
LANZHOU UNIVERSITY
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation process is relatively complicated, the repeatability is poor, and it is difficult to prepare on a large scale.
However, in practical applications, because the thickness of the carbon film is relatively thick and it is easily affected by factors such as poor electrical conductivity and thermal conductivity of the "carrier support film", it will cause sample drift, jumping, and even rupture of the support film to a certain extent, which is seriously unsatisfactory. Conducive to the improvement of resolution
In the prior art, the microgrid is generally a circular sheet structure with a diameter of about 3 mm. Due to the small size of the microgrid, advanced technology and high manufacturing cost are required in the manufacture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A transmission electron microscope microgrid based on heavy ion irradiation and its preparation method
  • A transmission electron microscope microgrid based on heavy ion irradiation and its preparation method
  • A transmission electron microscope microgrid based on heavy ion irradiation and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A method for preparing a transmission electron microscope microgrid based on heavy ion irradiation, the specific steps are as follows:

[0040] (1) Irradiation of polyethylene terephthalate PET film:

[0041] The high-energy heavy ions are accelerated on the heavy ion accelerator, and the high-energy heavy ions are used to irradiate the surface of the polyethylene terephthalate PET film vertically. The thickness of the polyethylene terephthalate PET film is 5 μm. Among them, the LET linear energy transfer value of the high-energy heavy ions in the polyethylene terephthalate PET film is greater than 4.5 eV / nm, and the number of high-energy heavy ions irradiated on the polyethylene terephthalate film is 2.0 ×10 10 ions / cm 2 .

[0042] (2) Etching of nanopores of polyethylene terephthalate PET film:

[0043] The irradiated polyethylene terephthalate PET film was immersed in a sodium hydroxide solution for chemical etching, wherein the concentration of the sodium hydro...

Embodiment 2

[0047] A method for preparing a transmission electron microscope microgrid based on heavy ion irradiation, the specific steps are as follows:

[0048] (1) Irradiation of polyethylene terephthalate PET film:

[0049] The high-energy heavy ions are accelerated on the heavy ion accelerator, and the high-energy heavy ions are used to irradiate the surface of the polyethylene terephthalate PET film vertically. The thickness of the polyethylene terephthalate PET film is 30 μm. Among them, the LET linear energy transfer value of the high-energy heavy ions in the polyethylene terephthalate PET film is greater than 4.5 eV / nm, and the number of high-energy heavy ions irradiated on the polyethylene terephthalate film is 1.0 ×10 5 ions / cm 2 ;

[0050] (2) Etching of nanopores of polyethylene terephthalate PET film:

[0051] The irradiated polyethylene terephthalate PET film was immersed in a sodium hydroxide solution for chemical etching, wherein the concentration of the sodium hydro...

Embodiment 3

[0055] A method for preparing a transmission electron microscope microgrid based on heavy ion irradiation, the specific steps are as follows:

[0056] (1) Irradiation of polyethylene terephthalate PET film:

[0057] The high-energy heavy ions are accelerated on the heavy ion accelerator, and the high-energy heavy ions are used to irradiate the surface of the polyethylene terephthalate PET film vertically. The thickness of the polyethylene terephthalate PET film is 20 μm. Among them, the LET linear energy transfer value of the high-energy heavy ions in the polyethylene terephthalate PET film is greater than 4.5 eV / nm, and the number of high-energy heavy ions irradiated on the polyethylene terephthalate film is 3.0 ×10 6 ions / cm 2 ;

[0058] (2) Etching of nanopores of polyethylene terephthalate PET film:

[0059] The irradiated polyethylene terephthalate PET film was immersed in a sodium hydroxide solution for chemical etching, wherein the concentration of the sodium hydro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A transmission electron microscope microgrid based on heavy ion irradiation, the transmission electron microscope microgrid is etched with a solution of sodium hydroxide after high-energy heavy ion irradiation to obtain a microporous polyethylene terephthalate PET film and It consists of a metal film plated on it by magnetron sputtering or thermal evaporation or electron beam evaporation. The thickness of the polyethylene terephthalate PET film is 5-30 μm, and the thickness of the metal film is 5‑30 nm. The present invention is based on the use of polyethylene terephthalate PET film irradiated by heavy ions, and then etched to form micropores with uniform and adjustable aperture, magnetron sputtering, thermal evaporation or electron beam evaporation coating A TEM microgrid with higher porosity and conductivity is obtained. Compared with the existing technology, the prepared TEM microgrid uses the heavy ion track film as a template, and covers a layer of metal film with adjustable thickness and type on the template. . The microgrid for transmission electron microscopy is composed of many microporous structures with uniform pore size and adjustable size. Improve the accuracy of the test.

Description

technical field [0001] The invention relates to the technical field of transmission electron microscope microgrid preparation, in particular to a transmission electron microscope microgrid based on heavy ion irradiation etching technology and a preparation method. Background technique [0002] Transmission electron microscopy can observe submicrostructures or ultrastructures that cannot be observed with optical microscopes. By observing the ultrastructure of samples under the electron microscope and combining in-situ observation technology, researchers can deeply understand the essential characteristics of materials and promote the optimal design of materials. In transmission electron microscopy, microgrids are an important tool for carrying samples and performing high-resolution imaging observations. With the continuous development of research on nanomaterials with smaller sizes, the application of transmission electron microscopy in the field of characterization of nanoma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01J37/02H01J37/26H01J9/00
CPCH01J37/02H01J37/26H01J9/00
Inventor 刘德全李一丁刘建德刘艳杰孙楷焦朝晖谢志超常英凡贺德衍
Owner LANZHOU UNIVERSITY