A kind of coating for electrode and its preparation method and application

An electrode and coating technology, which is applied in the field of electrode coatings and its preparation, can solve problems such as battery failure, battery internal short circuit, unfavorable use of zinc negative electrodes, etc., and achieve the effects of improving cycle life, reducing direct contact, and improving cycle stability

Active Publication Date: 2021-12-14
HUNAN UNIV OF SCI & TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the zinc negative electrode will generate dendrites during the cycle, causing the internal short circuit of the battery, thus making the battery invalid.
In addition, zinc has serious self-corrosion and hydrogen evolution reactions in the electrolyte, which is not conducive to the practical application of zinc anodes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of coating for electrode and its preparation method and application
  • A kind of coating for electrode and its preparation method and application
  • A kind of coating for electrode and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] Dissolve PVDF in nitrogen nitrogen dimethyl pyrrolidone solution, and then add 100nm BaTiO 3 Nanoparticles are added into the homogeneous solution, ultrasonically dispersed and magnetically stirred to make it a homogeneous slurry, in which the mass ratio PVDF: BaTiO 3 for 5:95. Use the cleaned and polished zinc foil as the base, use a coating machine to evenly coat the slurry on the zinc foil, dry it in vacuum at 60°C for no less than 3 hours, and cut it into 1cm -2 The disc electrode is used as a spare. Such as Figure 8 As shown, coated BaTiO 3 The surface of the coated zinc foil is covered with a layer of uniform nanoparticles, and further zoomed in, it is found that the coating has uniform small pores, such as Figure 9 As shown, it can be used as a channel for ion transmission. are significantly different from bare zinc foil, such as Figure 10 shown. Using XRD to characterize nano-BT found that, as Figure 11 As shown, the nanoparticles are a single BT pha...

Embodiment 2

[0060] Using the BaTiO prepared in Example 1 3 The coated zinc foil was used as the electrode, and the electrolyte, diaphragm and battery case used in Comparative Example 1 were used to assemble the Zn@BT||Zn@BT symmetric battery, and the cycle stability of the battery was tested under different charge and discharge current conditions. 0.5mA cm -2 -0.5mAh cm -2 Under the same charging and discharging conditions, the symmetrical battery can stably cycle for more than 420 hours, which is 22 times that of the Zn||Zn symmetrical battery of the control example, such as figure 2 , and the Zn@BT anode has lower hysteresis voltage and nucleation overpotential, such as image 3 shown. at 0.2 mA cm -2 -1mAh cm -2 Under certain charging and discharging conditions, it can stably cycle for 500h, which is 7 times that of Zn||Zn symmetric batteries, such as figure 1 shown. Similarly, using the MnO in the control example 2 The positive electrode assembly full battery test found that ...

Embodiment 3

[0062] Use the slurry in Example 1 to evenly coat the cleaned copper foil to control the thickness of the coating, then vacuum dry at 60°C for no less than 3 hours, and cut into 1cm 2 The wafer current collector (Cu@BT). Using the electrolyte, separator and battery case in Comparative Example 1, and then using the bare zinc foil as the negative electrode, and Cu@BT to assemble a Zn||Cu@BT half-cell, the test found that the Zn||Cu@BT half-cell was 0.5mA cm -2 -0.5mAh cm -2 Under the charging and discharging conditions, it can stably cycle more than 220 times, which is 9 times that of the Zn||Cu half-cell of the control example, such as Figure 4 shown. At the same time, the study of the deposition voltage of zinc on the current collector for the first time found that the Cu@BT current collector has a lower zinc nucleation overpotential of 26mV, which is much lower than the nucleation overpotential of bare copper foil of 54mV, such as Figure 6 shown. Likewise, at 2mA cm -...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
relative permittivityaaaaaaaaaa
Login to View More

Abstract

A paint for electrode, its preparation method and application. The coating formed by the coating uses cheap nano-dielectric fillers to adjust the uniformity of zinc deposition. On the one hand, the nano-channels formed by nanoparticles can regulate the transmission of zinc ions, and on the other hand, it can increase the nucleation sites of zinc on the electrode. point, achieving dendrite-free zinc deposition. At the same time, the dipole and physical barrier effect produced by the coating containing nano-fillers with high dielectric constant can effectively isolate the water molecules in the electrolyte, so as to inhibit the corrosion and hydrogen evolution reaction on the zinc negative electrode, and can significantly improve the performance of the zinc negative electrode. stability. The coating formed by the coating has a large proportion of dielectric fillers, which can use the dipole-dipole effect generated by the dielectric fillers, and can adjust the distribution of zinc ions relative to the electrode surface through the electrostatic interaction between dipoles and zinc ions, weakening the The tip electric field enhancement effect increases the nucleation sites on the electrode surface, thereby effectively inhibiting the generation of dendrites.

Description

technical field [0001] The invention belongs to the technical field of energy storage materials, and in particular relates to a coating for electrodes and a preparation method and application thereof. Background technique [0002] Energy storage materials are the key to clean energy from generation to storage and efficient use. Lithium-ion batteries and lead-acid batteries, as representatives of high energy density and low cost respectively, occupy a key position in the battery industry. However, the price of lithium-ion batteries, the reserves of lithium resources and the safety of batteries all restrict its development, and the low energy density and environmental pollution of lead-acid batteries are not conducive to its sustainable development. Energy-dense battery energy storage devices are crucial. [0003] Aqueous zinc-ion batteries have the advantages of safety and environmental protection, and the zinc-ion batteries with zinc metal as the negative electrode have th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/62H01M4/66H01M4/04H01M4/02H01M10/36H01M10/42
CPCH01M4/62H01M4/622H01M4/667H01M4/0404H01M4/02H01M10/36H01M10/4235Y02E60/10
Inventor 王芳谢春霖马南山欧云
Owner HUNAN UNIV OF SCI & TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com