A kind of UV-cured electric leakage interruption protection coating, preparation method and application thereof

A technology for protecting coatings and ultraviolet light, applied in epoxy resin coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of affecting the insulation of battery packs, hollowing out of temperature changes, and weak bonding, etc. Production efficiency and environmental safety, good stability, and the effect of improving safety and reliability

Active Publication Date: 2022-05-24
王书传
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, in view of the above content, the present invention provides a UV-cured leakage protection coating, which solves the problem that the prior art uses a blue film to cover the aluminum shell surface of the lithium battery, which is not firmly bonded and is prone to hollowing when the temperature changes. Problems affecting the insulation of battery packs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of UV-cured electric leakage interruption protection coating, preparation method and application thereof
  • A kind of UV-cured electric leakage interruption protection coating, preparation method and application thereof
  • A kind of UV-cured electric leakage interruption protection coating, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of UV-curable electrical leakage protection coating, comprising the following components by weight: 10 parts of bifunctional fatty acid-modified bisphenol A epoxy acrylate, 5 parts of bifunctional polyHDI isocyanate acrylate, tetrahydrofuran acrylate 8 parts, 12 parts of isobornyl methacrylate, 15 parts of tricyclodecane dimethanol diacrylate, 10 parts of pentaerythritol triacrylate, 5 parts of pigments and fillers, 2-hydroxy-2-methyl-1-phenyl- 1 part of 1-acetone, 2 parts of (2,4,6-trimethylbenzoyl)diphenylphosphine oxide, 1 part of silane coupling agent KH-5501, 0.3 part of dispersant, 0.1 part of defoamer, leveling dose 0.2 servings.

[0035] A preparation method of an ultraviolet light-cured leakage electrical disconnection protective coating, comprising the following steps:

[0036] (1) Pre-mixing: add bifunctional fatty acid-modified bisphenol A epoxy acrylate, tetrahydrofuran acrylate, isobornyl methacrylate, dispersant and defoamer into the batching tank...

Embodiment 2

[0040] A kind of ultraviolet light-curing leakage circuit breaker protection coating, comprising the following components by weight: 15 parts of bifunctional fatty acid-modified bisphenol A epoxy acrylate, bifunctional polyH 12 10 parts of MDI isocyanate acrylate, 15 parts of tetrahydrofuran acrylate, 10 parts of N-hydroxyethylacrylamide, 20 parts of tricyclodecane dimethanol dimethyldiacrylate, tris(2-hydroxyethyl)isocyanurate 15 parts of acrylates, 10 parts of pigments and fillers, 3 parts of 2-hydroxy-2-methyl-1-phenyl-1-propanone, 2 (2,4,6-trimethylbenzoyl)diphenylphosphine oxide parts, silane coupling agent KH-5603 parts, dispersant 0.8 parts, defoamer 0.3 parts, leveling agent 0.5 parts.

[0041] A preparation method of an ultraviolet light-cured leakage electrical disconnection protective coating, comprising the following steps:

[0042] (1) Pre-mixing: add bifunctional fatty acid-modified bisphenol A epoxy acrylate, tetrahydrofuran acrylate, N-hydroxyethyl acrylamide,...

Embodiment 3

[0046] A kind of ultraviolet light-curing electrical leakage protection coating, comprising the following components by weight: 20 parts of bifunctional fatty acid-modified bisphenol A epoxy acrylate, 15 parts of bifunctional polyHDI isocyanate acrylate, methacrylic acid 15 parts of hydroxypropyl ester, 15 parts of tetrahydrofuran acrylate, 10 parts of tricyclodecane dimethanol diacrylate, 15 parts of tricyclodecane dimethanol dimethacrylate, 5 parts of propoxylated glycerol triacrylate, pigments and fillers 15 parts, 5 parts of 2-hydroxy-2-methyl-1-phenyl-1-propanone, 2.5 parts of (2,4,6-trimethylbenzoyl)diphenylphosphine oxide, silane coupling agent KH -5705 parts, 1.2 parts of dispersant, 0.8 part of defoamer, 1 part of leveling agent.

[0047] A preparation method of an ultraviolet light-cured leakage electrical disconnection protective coating, comprising the following steps:

[0048] (1) Pre-mixing: Add bifunctional fatty acid-modified bisphenol A epoxy acrylate, hydrox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical resistanceaaaaaaaaaa
Login to view more

Abstract

The present invention relates to the technical field of UV-curable coatings, in particular to a UV-curable leakage protection coating, a preparation method and its application, comprising the following components in parts by weight: 10-20 parts of epoxy acrylate, polyurethane acrylate 5‑15 parts, 20‑30 parts of monofunctional acrylate, 15‑25 parts of difunctional acrylate, 5‑15 parts of multifunctional acrylate, 5‑15 parts of pigment and filler, 3‑8 parts of photoinitiator, silane coupling 1-5 parts of additive and 0.5-3 parts of auxiliary agent can be applied to the surface of aluminum and other metal surfaces on the battery cell in the battery pack to form an insulating protective coating. The present invention solves the problem that in the prior art, the surface of the aluminum shell of the lithium battery is coated with a blue film, the bonding is not firm, hollowing is easy to occur when the temperature changes, and the insulation of the battery pack is affected.

Description

technical field [0001] The invention relates to the technical field of ultraviolet light-curing coatings, in particular to an ultraviolet light-curing leakage circuit breaker protection coating, a preparation method and applications thereof. Background technique [0002] New energy vehicles have the advantages of energy saving, emission reduction and environmental protection. They are of great significance to ensure national energy security, solve environmental pollution, and achieve sustainable social and economic development. It is an inevitable trend to achieve sustainable development. As the core components of new energy vehicles, power batteries are an important focus for the development of the new energy vehicle industry. The composition of the power battery of different models may be different, but on the whole it is a process from a single cell to a module, and a module to a battery pack. The lightweight of battery packs has become a market trend. Therefore, the use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/10C09D175/14C09D5/25
CPCC09D163/10C09D5/00C08L75/14
Inventor 陈增永王书传张武军
Owner 王书传
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap