Pickering emulsion with CO2/double-response type surfactant and preparation method of Pickering emulsion
A surfactant and emulsion technology, applied in the field of Pickering emulsion and preparation, can solve the problems of unsuitability for industrial application, complex chemical synthesis process, cumbersome preparation, etc., and achieve simple preparation method, simple response process, and low dosage Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0031] Example 1:
[0032] The first step, the carboxy-modified nano silica particles were prepared
[0033] First, the silica nanoparticles are accurately weighted with a silica nanoparticle 5g, and 9 ml of aminopropyltriethoxysilane and 100 ml of the amount of the amount of the toluene were used to add a 250 ml flask, and a few drops of triethylamine were added. The promoter was placed in a 110 ° C oil bath for magnetic stirring and reflux reaction for 5 h. After the end of the reaction, cooled to room temperature, centrifuge by centrifuge, remove solvent toluene, and rinse with water and water and absolute ethanol, and then dried to give silica nanoparticles of surface aminocya.
[0034]The silica nanoparticles having a surface aminocylated silica nanoparticle were added to the flask containing 100 mL of N, N-dimethylformamide solvent, and the ultrasonic instrument was placed around 10 min, so that the nanoparticles sufficiently dispersed in the solvent, Then, tanotharhyric anh...
Example Embodiment
[0038] Example 2:
[0039] CO 2 / Oxidation is reduced to the double stimulating response surfactant to stabilize the performance of the emulsion, adding different mass ferrocene surfactants to 10 ml of deionized water, dispersion uniform in deionized water with ultrasonic instruments (surface The concentration of the aqueous solution of the active agent was added to a 30 ml glass vial, and 10 ml of paraffin oil was added, and the vortex oscillator was emulsified at 1000 rpm Rotate, and a stable emulsion was not obtained, indicating that the surfactant concentration A stable emulsion is not formed when less than CMC.
Example Embodiment
[0040] Example 3:
[0041] CO 2 / Oxidation is reduced to the surface activation of the carboxylated silica nanoparticles.
[0042] Option One:
[0043] 0.00299 g of ferrocene surfactants were added to 10 ml of deionized water (using a concentration of 1.0 × 10 in the use of aqueous phase) -3 Mol·L -1 At the same time, at the same time, 0.1 g of different sizes of carboxy-modified nano silica particles (the aqueous phase) was 1 wt%, the native particle diameter was 20 nm, 30 nm, 50 nm, 100 nm, 200 nm, respectively, using ultrasound instruments It is uniform in deionized water, and the above solution is added to a 30 ml glass vial containing 10 ml of paraffin oil, and the vortex oscillator is utilized to emulsify 3 min at 1000 rpm to give a stable Pickering emulsion, which is as follows.
[0044] Option II:
[0045] Different concentrations of ferrocene surfactants were added to 10 ml of deionized water (from 0.00299 g, 0.004495 g, 0.00599 g, 0.004485 g, 0.00598 g), and 0.1 g of ca...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap