Preparation method of low-cost anti-detonation titanium alloy plate

A titanium alloy plate, low-cost technology, applied in the direction of metal rolling, metal processing equipment, etc., to achieve the effect of improving toughness and plasticity, reducing component cost, and improving anti-detonation performance

Active Publication Date: 2021-10-08
西安赛福斯材料防护有限责任公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the preparation of titanium alloys is mainly aimed at composition design, processing preparation and heat treatment process, and does not involve the impact and explosion of materials in special use environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment includes the following steps:

[0028] Step 1. Composition design: design the composition of the target product titanium alloy plate, and obtain the nominal composition of the titanium alloy plate as Ti-4Al-2.8V-1Fe-0.1Si-0.1O, and the specific mass content composition: aluminum 4 %, vanadium 2.8%, iron 1%, silicon 0.1%, oxygen 0.1%, the total mass content of other impurity elements is less than 0.3% and the mass content of any impurity element is less than 0.1%, and the rest is titanium;

[0029]Step 2, batching: according to the mass content and composition of the titanium alloy plate obtained in step 1, select the raw materials for preparing corresponding elements, and batch according to 100kg ingot, the specific raw materials and quality are as follows: Ti-6Al-4V residual material 20kg, sponge titanium 74kg, aluminum-50 vanadium master alloy 2kg, iron-50 vanadium master alloy 2kg, aluminum-20 silicon master alloy 0.5kg, aluminum beans 1.4kg, titanium...

Embodiment 2

[0037] This embodiment includes the following steps:

[0038] Step 1. Composition design: design the composition of the target product titanium alloy plate, and obtain the nominal composition of the titanium alloy plate as Ti-5Al-3V-1Fe-0.4Si-0.2O, and the specific mass content composition: aluminum 5% , vanadium 3%, iron 1%, silicon 0.4%, oxygen 0.2%, the total mass content of other impurity elements is less than 0.3% and the mass content of any impurity element is less than 0.1%, and the rest is titanium;

[0039] Step 2, batching: according to the mass content and composition of the titanium alloy plate obtained in step 1, select the raw materials for preparing corresponding elements, and batch according to 500kg ingot, the specific raw materials and quality are as follows: Ti-5Al residual material 50kg, sponge titanium 404.5kg , aluminum-50 vanadium medium alloy 20kg, iron-50 vanadium master alloy 10kg, aluminum-20 silicon master alloy 10kg, aluminum beans 4.5kg, titanium ...

Embodiment 3

[0047] This embodiment includes the following steps:

[0048] Step 1. Composition design: design the composition of the target product titanium alloy plate, and obtain the nominal composition of the titanium alloy plate as Ti-3Al-2V-1.5Fe-0.5Si-0.1O, and the specific mass content composition: aluminum 3 %, vanadium 2%, iron 1.5%, silicon 0.5%, oxygen 0.1%, the total mass content of other impurity elements is less than 0.3% and the mass content of any impurity element is less than 0.1%, and the rest is titanium;

[0049] Step 2, batching: according to the mass content and composition of the titanium alloy plate obtained in step 1, select the raw materials for preparing corresponding elements, and batch according to 1000kg ingot, the specific raw materials and quality are as follows: Ti-2Al-2V residue 200kg, sponge titanium 737kg, aluminum-50 vanadium intermediate alloy 2kg, iron-50 vanadium intermediate alloy 30kg, aluminum-20 silicon intermediate alloy 25kg, aluminum beans 5kg...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a low-cost anti-detonation titanium alloy plate. The method comprises the following steps that 1, components of a target product titanium alloy plate are designed; 2, raw materials for preparing corresponding elements are selected; 3, an electrode is prepared, a titanium alloy cast ingot is obtained through two times of vacuum consumable smelting, then cutting is conducted, and cogging forging is conducted to obtain a plate blank; 4, the plate blank is subjected to multi-heating-number rolling to obtain a titanium alloy plate; 5, heat treatment is performed; and 6, the anti-detonation titanium alloy plate is obtained through surface treatment. The anti-detonation titanium alloy plate with few components and low alloy element content is designed according to the alloying principle, the component cost is reduced, the effects of reducing the surface density and strengthening are achieved, the toughness and plasticity of the anti-detonation titanium alloy plate are improved on the premise that the strength of the anti-detonation titanium alloy plate is guaranteed, the anti-detonation titanium alloy plate achieves the effects of generating uniform plastic rheology and absorbing more energy under the attack of shock waves, the shock waves brought by explosion are effectively resisted, and the anti-detonation performance of the anti-detonation titanium alloy plate is improved.

Description

technical field [0001] The invention belongs to the technical field of preparation of titanium alloy profiles, and in particular relates to a preparation method of a low-cost detonation-proof titanium alloy plate. Background technique [0002] Titanium alloy has the characteristics of low density, high specific strength, excellent corrosion resistance and high temperature resistance, and is widely used in aerospace, chemical, medical, weapon and other fields, and is an important structural material. At present, the preparation of titanium alloy is mainly aimed at composition design, processing and preparation and heat treatment process, and does not involve the impact and explosion of materials in special use environments. The use of titanium alloys to manufacture explosion-proof bombardment plates is of great significance for enhancing combat capabilities. With the advancement of science and technology, modern high-performance anti-detonation materials have developed in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C14/00C22F1/18B21B1/02B21J5/00
CPCC22C14/00B21J5/002B21B1/026C22F1/183B21B2001/028
Inventor 呼丹高广睿屈静陶路路王宝云
Owner 西安赛福斯材料防护有限责任公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com