PH response type corrosion inhibition capsule based on metal polyphenol network structure and preparation and application of pH response type corrosion inhibition capsule

A network structure, metal technology, applied in the direction of microcapsule preparation, microsphere preparation, etc., can solve the problems of cumbersome process, leakage of corrosion inhibitor molecules, etc., and achieve the effect of low price, easy surface modification, and large specific surface area.

Pending Publication Date: 2021-12-10
HUAZHONG UNIV OF SCI & TECH +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation process of the above three types of corrosion inhibitor capsules is cumbersome, and the corrosion inhibitor molecules are easy to leak during the preparation process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PH response type corrosion inhibition capsule based on metal polyphenol network structure and preparation and application of pH response type corrosion inhibition capsule
  • PH response type corrosion inhibition capsule based on metal polyphenol network structure and preparation and application of pH response type corrosion inhibition capsule
  • PH response type corrosion inhibition capsule based on metal polyphenol network structure and preparation and application of pH response type corrosion inhibition capsule

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The preferred preparation process is:

[0035] 1) First add a certain amount of cetyltrimethylammonium bromide into water, raise the temperature to 80°C, then add NaOH, and stir vigorously for 10-20 minutes.

[0036] 2) Then tetraethyl orthosilicate was added dropwise, reacted at 80° C. for two hours, and the obtained white solid was obtained by suction filtration after cooling.

[0037] 3) Calcining the collected solid in a muffle furnace for 5 h.

[0038] The preferred amount of cetyltrimethylammonium bromide added is 1 g, and the amount of tetraethylorthosilicate is 5 mL.

[0039] The preferred stirring speed is 8000 rpm.

[0040] The preferred calcination temperature is 550°C, and the heating rate is 1°C / min.

[0041] A preparation method of a HMS-based benzotriazole drug-carrying system of the present invention: dissolve benzotriazole in an ethanol solution, then add the HMS suspension prepared above, pump it to a vacuum state by a vacuum water pump, and After ...

Embodiment 1

[0053] Embodiment 1: the preparation of corrosion inhibitor capsule

[0054] 1) Dissolve 1g of hexadecyltrimethylammonium bromide in water, raise the temperature to 80°C, then add NaOH, stir vigorously for 10-20 minutes, then add 5ml of tetraethyl orthosilicate dropwise, at 80°C The reaction was stirred for two hours, and the obtained white solid was filtered by suction after cooling. The collected solid was heated up to 550° C. at a rate of 1° C. / min in a muffle furnace, and continuously calcined for 5 hours to obtain mesoporous silica.

[0055] 2) Take 1g of calcined mesoporous silica and 1.6g of benzotriazole and mix well in a 40ml three-necked flask, stir and load under vacuum for 24h, take out and centrifuge, wash with deionized water three times, and bake at 60°C Dry and set aside.

[0056] 3) Take the prepared HMS@BTA and configure it into 1mL dispersion system. After vortexing for 30s, add 300uL tannic acid first, and then add 500uL ferric ions after the tannic acid ...

Embodiment 2

[0057] Embodiment 2: the selection of number of repetitions in complexing process

[0058] According to the preparation method described in Example 1, the complexation process was repeated several times to be embodied three times, five times, ten times and fifteen times. After the above steps are completed, the prepared corrosion inhibitor capsules are observed by optical electron microscope in turn, and the results are as follows: figure 1 As shown, (a), (b), (c), and (d) in the figure respectively represent the optical images of the corrosion inhibitor capsules prepared for three, five, ten and fifteen times of complexation. When the number of times of complexation is less than five times, it can be seen under the optical microscope that the prepared corrosion inhibitor capsule presents gray and white colors, and when the number of times of complexation reaches more than ten times, the entire capsule is uniformly black. It shows that if the number of complexation is too sma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a pH response type corrosion inhibition capsule based on a metal polyphenol network structure and preparation and application of the pH response type corrosion inhibition capsule, and belongs to the field of application of novel materials. Mesoporous silicon dioxide with a large specific surface area is used as a carrier for loading corrosion inhibitor molecules, and then the corrosion inhibitor molecules are loaded into the mesoporous silicon dioxide through a vacuum loading method. Finally, through modification of organic acid with a polyphenol structure and metal ions, a metal-phenol network structure is generated outside the silicon dioxide, and the corrosion inhibitor capsule with targeting, pH responsiveness and anti-ultraviolet activity can be formed. The capsule corrosion inhibitor can be quickly released at low pH and slowly released in neutral and alkaline systems, so that release of the corrosion inhibitor is intelligent, the utilization efficiency of the corrosion inhibitor is improved, meanwhile, as the corrosion inhibitor molecules are loaded in the whole capsule, direct irradiation of ultraviolet light can be avoided, and when the capsule corrosion inhibitor is applied to an ultraviolet environment, the utilization rate of the corrosion inhibitor molecules is greatly increased.

Description

technical field [0001] The invention belongs to the application field of new materials, more specifically, a pH-responsive corrosion-inhibiting capsule based on a metal-phenol network structure and its preparation and application, especially relates to a metal-phenol network structure-controlled corrosion inhibitor with pH response and anti-ultraviolet activity. Preparation and characterization of corrosion inhibitor capsules and evaluation of corrosion inhibition effects. The synthetic corrosion inhibitor capsules are used in the field of metal protection, making the release of corrosion inhibitors more intelligent. Background technique [0002] Under the application conditions of high ultraviolet light irradiation, the metal substrate itself will not only be attacked by corrosive media, but ultraviolet light will also accelerate the further corrosion of the metal. At present, we generally use the method of painting the protective layer for metal protection in this environm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23F11/14C23F11/16C23F11/04B01J13/02
CPCC23F11/149C23F11/165C23F11/04B01J13/02
Inventor 陈振宇郭成彬魏莉莎曹娇娇邱于兵
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka