Biodegradable PLA film and preparation method thereof
A biodegradable and PLA technology, applied in the field of biodegradable PLA film and its preparation, can solve the problems of easy adhesion of PLA film, unfavorable performance control and stability, large difference in fluidity, etc., to solve the serious problem of brittleness, Effects of improving processing stability and improving compatibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0039] Example 1
[0040] Method for preparing biodegradable PLA film:
[0041] (1) Four PLA and PBC were dried at 70 ° C for 5 hours;
[0042] (2) Preparation of bio-based opening agent (nucleating agent):
[0043] The discarded egg shell was rinsed, placed in an oven, dried under a temperature of 110 ° C for 5 hours, after removing cooled to room temperature, using a ball mill to pulverize the particle diameter of 2 μm.
[0044] Phenylphosphonic acid was dried in vacuo at 110 ° C at 110 ° C for 4 h at 110 ° C. After drying, the two substances were brought to a mass fraction than 1: 5 at room temperature, and the two substances were mixed uniform. A thickened powder was then placed in an oven at 180 ° C for 5 minutes to give a phenylphosphonic acid calcium carbonate nucleating agent.
[0045] The phenylphosphonic acid attached egg chrose is placed in a high-speed mixer, and the silane coupling agent KH550 is configured to 20% by weight of the silane coupling agent ethanol solutio...
Example Embodiment
[0050] Example 2
[0051] Method for preparing biodegradable PLA film:
[0052] (1) Four PLA and PBC were dried at 70 ° C for 5 hours;
[0053] (2) The bio-based opening agent (nucleating agent) of Example 1 is employed;
[0054] (3) 75 parts, PBC, 14 parts of PBC, 5 parts of Tung oalic anhydride, 0.5 parts of stearate, 0.5 epoxy acrylic copolymers, 5 parts of bio-based dose in high mixing machines Mix for 10 minutes;
[0055] (4) Mix the homogeneous material to the secondary screw extruder in the twin screw extruder for molten, extrusion, water cooling, dry particles, drying to obtain a modified polylactic acid blown film special resin; extruded granulation Conditions: The set temperature of the twin screw extruder is: one district: 80 ° C, second area: 160 ° C, three districts: 180 ° C, four districts: 180 ° C, five districts: 180 ° C, Six districts: 180 ° C, Seven District: 180 ° C, Eight District: 180 ° C, Nine Area: 180 ° C, Ten District: 180 ° C, 11: 180 ° C, Machine Head: 1...
Example Embodiment
[0058] Example 3
[0059] Method for preparing a fully degraded PLA film:
[0060] (1) Four PLA and PBC were dried at 70 ° C for 5 hours;
[0061] The bioefragrance (nucleating agent) of Example 1 was employed.
[0062] (3) 80 parts, PBC, 5 parts of PBC, 5 parts of Tong oleic anhydride, 0.5 parts of stearate, 0.5 epoxy acrylic copolymers, 5 parts of bio-based opening in high mixing machines Mix for 10 minutes;
[0063] (4) Mix the homogeneous material to the secondary screw extruder in the twin screw extruder for molten, extrusion, water cooling, dry particles, drying to obtain a modified polylactic acid blown film special resin; extruded granulation Conditions: The set temperature of the twin screw extruder is: one district: 80 ° C, second area: 160 ° C, three districts: 180 ° C, four districts: 180 ° C, five districts: 180 ° C, Six districts: 180 ° C, Seven District: 180 ° C, Eight District: 180 ° C, Nine Area: 180 ° C, Ten District: 180 ° C, 11: 180 ° C, Machine Head: 170 ° C, ...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap