An adhesive and strong technology, applied in the direction of adhesive types, graft polymer adhesives, adhesives, etc., can solve the problems of inability to produce product performance and quality, needs, inability to achieve, and achieve high adhesion. , the effect of increasing the solid content and increasing the initial viscosity

Active Publication Date: 2005-08-17
GUANGZHOU GLORYSTAR CHEM
View PDF0 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some high-performance and high-quality adhesives and additives on the market cannot be produced or the performance and quality of the products cannot meet the needs of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] 1. Chloroprene rubber mixing

[0050] Take 100 parts of chloroprene rubber and put it into an open mixer for mixing. After 10 minutes, add 3 parts of thickener white carbon black and mix evenly.

[0051] 2. Pre-reaction

[0052] Add 600 parts of solvents (mixed solvent of toluene, hexanaphthene and gasoline composition, toluene: hexanaphthene: gasoline ratio is 4: 3: 3), 50 parts of modified phenolic resins (commercially available) in reactor, stir Evenly, add 2 parts of antioxidant MgO to it, and continue to stir for 4 hours, so that the complexation reaction between the tackifying resin and the antioxidant takes place.

[0053] 3. Grafting

[0054]Add the mixed chloroprene rubber into the reactor, add 70 parts of grafted monomer methyl methacrylate (MMA), 0.6 part of dispersant dioctadecyl ammonium chloride, 0.34 part of catalyst benzyl peroxide Acyl, stir, dissolve, heat up to 60 ° C, react for 4 hours, immediately add 2.5 parts of polymerization inhibitor 2,6 di-...

Embodiment 2

[0058] 1. Chloroprene rubber mixing

[0059] Take 100 parts of chloroprene rubber and put it into an open mixer for mixing. After 10 minutes, add 2 parts of thickener white carbon black and mix evenly.

[0060] 2. Pre-reaction

[0061] Add 400 parts of solvent (a mixed solvent composed of toluene, n-hexane and gasoline, the ratio of toluene: n-hexane: gasoline is 4:4:2) and 30 parts of terpene resin into the reactor, stir evenly, and add 3 parts of Antioxidant MgO, continue to stir for 4 hours, so that the complexation reaction takes place between the tackifying resin and the antioxidant.

[0062] 3. Grafting

[0063] Add the mixed chloroprene rubber into the reaction kettle, add 20 parts of grafted monomer methyl methacrylate, 0.6 part of dispersant sodium salt of benzenesulfonic acid formaldehyde condensation polymer, 0.2 part of catalyst benzoyl peroxide, stir , dissolved, heated to 40°C, reacted for 6 hours, immediately added 2.2 parts of polymerization inhibitor 2,6 di...

Embodiment 3

[0067] 1. Chloroprene rubber mixing

[0068] Take 100 parts of chloroprene rubber and put it into an open mixer for mixing, add 5 parts of thickener hydroxymethyl cellulose after 10 minutes, and mix for 18 minutes.

[0069] 2. Pre-reaction

[0070] Add 500 parts of solvent (mixed solvent of toluene, methyl ethyl ketone and gasoline composition, toluene: methyl ethyl ketone: gasoline ratio is 4: 3: 3), 50 parts of terpene phenol resins in the reactor, stir evenly, add 1 Parts of antioxidant MgO, continue to stir for 6 hours, so that complexation reaction takes place between the tackifying resin and the antioxidant.

[0071] 3. Grafting

[0072] The chloroprene rubber through mixing is joined in the reactor, add 43 parts of grafting monomer butyl acrylate (BA), 0.5 part of dispersant paraffin, 0.24 part of catalyst dibenzoyl peroxide, stir, dissolve, be heated up to 60°C, reacted for 5 hours, immediately added 3.3 parts of polymerization inhibitor 2,6-di-tert-butyl-4-methylph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The powerful adhesive includes neoprene, grafting monomer, thickener, dispersant, adhesion promoter, catalyst, antioxidant, solvent, stuffing, etc. The present invention also discloses the preparation process of the adhesive, and the preparation includes introducing grafting monomer to neoprene molecule chain to raise the adhesion strength, selecting proper adhesion promoting resin to increase the initial adhesion force, and adopting mixed solvent to form high adhering performance. The adhesive has high solid content and excellent environment protecting performance, and has also excellent antiageing performance, high resistance to heat, oil, chemical and corrosion, high weather resistance, good mildew-proof performance, antibiotic performance, etc. and may be used for adhering timber, concrete, rubber, metal, gypsum board, brick and other building material.

Description

technical field [0001] The invention relates to an adhesive used in building materials, in particular to a high-strength adhesive and a preparation method thereof. Background technique [0002] In the era of continuous improvement of home decoration, in order to achieve a beautiful and firm effect, more and more people hope that the decoration will no longer use nails and screws, but directly bond them with strong adhesives. Traditional adhesives can no longer meet the harmony and unity of safety and aesthetics of chemical materials required by people. In decoration, they either have great limitations in sticking to different materials; or because of unstable chemical properties, the residual harmful substances after bonding cannot reach the minimum standard of the national interior decoration materials. Some high-performance and high-quality adhesives and auxiliary products on the market cannot be produced or the product performance and quality can...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J151/04
Inventor 莫万全
Owner GUANGZHOU GLORYSTAR CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap