Catalyst for synthesis of methyl methacrylate by formaldehyde and methyl propionate and preparation method of catalyst

A technology for methyl methacrylate and methyl propionate, which is applied in the field of catalysts for synthesizing methyl methacrylate, can solve problems such as low reaction activity, and achieve the effects of simple preparation method, improved activity, and improved anti-poisoning.

Active Publication Date: 2013-03-13
SOUTHWEST RES & DESIGN INST OF CHEM IND
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Acidic oxides show high selectivity for the aldol condensation reaction, but low reactivity; while basic oxides are used for the reaction, the catalytic activity is high, if the acid-base bifunctional catalyst is used, the selectivity of the reaction can be improved, and the Can increase MMA yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for synthesis of methyl methacrylate by formaldehyde and methyl propionate and preparation method of catalyst
  • Catalyst for synthesis of methyl methacrylate by formaldehyde and methyl propionate and preparation method of catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The catalyst of this embodiment consists of 20% active component, 5% coagent and 75% carrier. The active component is cesium acetate with a content of 20% of cesium oxide in the catalyst, the active agent is silver nitrate with a content of 5% of silver oxide, and the carrier is composed of 88% silicon dioxide, 10% activated alumina and 2% composition of zirconia. The preparation method is as follows:

[0034] (1) Weigh 36.3g of cesium acetate and dissolve it in deionized water to make an aqueous solution;

[0035] (2) Weigh nano-SiO 2 88g, pseudo-boehmite 14g, ZrO 2 2g, after mixing evenly, add the solution prepared in step (1) for kneading, extruding, drying at 100°C for 4 hours, and calcining at 500°C for 4 hours to obtain a catalyst precursor;

[0036] (3) Weigh 7.7gAgNO 3 , add deionized water to dissolve and make a solution;

[0037] (4) Weigh 100 g of the catalyst precursor prepared in step (2) and immerse in the aqueous solution prepared in step (3), immer...

Embodiment 2

[0039] The catalyst of this embodiment consists of 15% active component, 2% coagent and 83% carrier. The active component is cesium nitrate equivalent to 15% cesium oxide content in the catalyst, the active auxiliary agent is silver nitrate equivalent to 2% silver oxide content, and the carrier is composed of 89% silicon dioxide, 10% activated alumina and 1% composition of zirconia. The preparation method is as follows:

[0040] (1) Weigh 49.98g CsNO 3 Add deionized water to dissolve and make an aqueous solution;

[0041] (2) Weigh nano-SiO 2 178g, pseudoboehmite 28g, ZrO 22g, after mixing evenly, add the solution prepared in step (1) for kneading, extruding, drying at 100°C for 4 hours, and calcining at 500°C for 4 hours to obtain a catalyst precursor;

[0042] (3) Weigh 3.0gAgNO 3 , add deionized water to dissolve and make a solution;

[0043] (4) Weigh 100 g of the catalyst precursor prepared in step (2) and immerse in the aqueous solution prepared in step (3), immer...

Embodiment 3~5

[0045] The catalyzer of embodiment 3~5 is made up of 10% active ingredient, 1% coagent and 89% carrier. The active component is cesium nitrate equivalent to 10% cesium oxide in the catalyst, and the active additives are silver nitrate and SbCl 3 1. Niobium oxalate, calculated as oxide, the mass percentage is 1.0%, and the carrier is composed of 75% silicon dioxide, 20% activated alumina and 5% zirconia. The preparation method is as follows:

[0046] (1) Weigh 46.6gCsNO 3 Add deionized water to dissolve and make an aqueous solution;

[0047] (2) Weigh nano-SiO 2 225g, pseudo-boehmite 86g, ZrO 2 15g, after mixing evenly, add the solution prepared in step (1) for kneading, extruding, drying at 100°C for 6 hours, and calcining at 400°C for 4 hours to obtain a catalyst precursor;

[0048] (3) Weigh 1.2gAgNO respectively 3 , 1.3gSbCl 3 Dissolve 1.5g niobium oxalate in water to make 3 solutions;

[0049] (4) Weigh 80g of the catalyst precursor prepared in step (2), immerse in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a catalyst for synthesis of methyl methacrylate by formaldehyde and methyl propionate and a preparation method of the catalyst. The catalyst mainly comprises a main active component, an activated auxiliary and a carrier, wherein the main active component is Cs, the activated auxiliary is selected from one or more of Sb, Nb and Ag, and the carrier is a nanometer SiO2 / Al2O3-ZrO2 composite carrier; and metered by oxides and according to mass percentage, the main active component Cs accounts for 5%-20%, the activated auxiliary accounts for 1%-5%, and the balance is the carrier. Simultaneously, the invention discloses a preparation method of the catalyst. The catalyst provided by the invention is good in activity, selectivity and stability, simple in manufacture technology, suitable for large-scale industrialized application and environment-friendly.

Description

technical field [0001] The invention relates to a catalyst for synthesizing methyl methacrylate, in particular to a catalyst for directly synthesizing methyl methacrylate from formaldehyde and methyl propionate and a preparation method thereof. Background technique [0002] Methyl methacrylate (MMA) is an important organic chemical raw material, mainly used to produce plexiglass (polymethyl methacrylate, PMMA), and also used to manufacture other resins, plastics, coatings, adhesives, lubricants It is widely used as agent, sizing agent for wood and cork, impregnating agent for motor coils, paper polishing agent, printing and dyeing auxiliaries and insulating potting materials, etc. [0003] At present, there have been many patent literature reports for the catalyst research on the synthesis of methyl methacrylate by formaldehyde and methyl propionate at home and abroad, and the performance of catalysts with Cs, Na, K, Rb, etc. as the main active components has been studied. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/66B01J23/68C07C69/54C07C67/343
Inventor 李洁谭平华赖崇伟熊国焱李军刘旋
Owner SOUTHWEST RES & DESIGN INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap